Nanozeolite Y was synthesized without a template and modified with phosphorous (P) and metals. P was introduced via impregnation with different weight loadings (0.5, 1, and 2 wt %), while ion exchange was developed to introduce zirconium (Zr) and cobalt (Co). The physicochemical properties of the catalysts were characterized with X-ray diffraction (XRD), N 2 adsorption-desorption, temperature-programmed desorption of ammonia (NH 3 -TPD), and 27 Al and 31 P solid-state nuclear magnetic resonance (NMR). The parent nanozeolite Y showed an identical XRD pattern to that of a previous study, and the modified nanozeolite Y showed a lower crystallinity. The introduction of P altered tetrahedral Al to an octahedral coordination, which affected the catalyst acidity. Then, the catalyst was evaluated to produce olefins from n -dodecane at 550, 575, and 600 °C. The conversion, gas yield, and olefin yield increased with increasing temperature. The maximum olefin yield (63%) was achieved with the introduction of 1 wt % P with the highest selectivity to ethylene. The Co-modified nanozeolite altered the zeolite structure and exhibited similar activity to the P-modified one. Meanwhile, Zr-modified nanozeolite Y caused excessive metal distribution, blocked the porous structure of the zeolite, and then reduced the catalytic activity., Competing Interests: The authors declare no competing financial interest., (© 2022 The Authors. Published by American Chemical Society.)

This study emphasizes tuning the synthesis conditions of MFI zeolites to achieve better catalytic properties by optimizing the mesoporosity, the balance between Brønsted and Lewis sites, and the zeolite particle sizes. The MFI zeolites were hydrothermally synthesized at various temperatures employing different silica sources. The synthesis temperature was varied between 110 to 180 °C at constant synthesis time (15 h). Different silicon sources led to variations in structure, morphology, and size of the MFI zeolite along with tuned Lewis and Brønsted acid sites in parallel correlation with shape selectivity of the reaction. The catalytic activities of synthesized zeolites were investigated in the catalytic cracking of n -dodecane to produce value-added chemicals. The zeolite synthesized at 180 °C using fumed silica presented the highest catalytic conversion (96.6%), while maximum light olefin gaseous products (73.1%) were obtained for the sample synthesized at 140 °C using tetraethyl orthosilicate as the silica source. The MFI zeolite synthesized at 180 °C employing tetraethyl orthosilicate as a silica source facilitated the formation of both naphthenes and aromatics (71.3%) as major liquid products., Competing Interests: The authors declare no competing financial interest., (© 2022 The Authors. Published by American Chemical Society.)