Search

The ZnO nanorods/ZnSe nanosheets heterostructure had been successfully fabricated by the spin coating method. The evolution of the structural, optical and photocatalytic properties of the samples with different spin coating times was comprehensively investigated. The X-ray diffraction (XRD) patterns showed that the relative intensities of ZnSe peaks increased gradually with the increase of spin coating times, but the ZnO peaks were relatively suppressed, which had a good agreement with the results of Raman spectra. The scanning electron microscope (SEM) and transmission electron micrograph (TEM) images further confirmed that the ZnSe nanosheets (NSs) had been successfully assembled on the top surfaces of the ZnO nanorods (NRs) and in the upper parts of the gaps between the rods. At room temperature, the ZnO/ZnSe heterostructures exhibited a relatively suppressed UV emission together with a dramatically enhanced deep-level emission. In addition, the heterostructures exhibited remarkable photocatalytic activities. The type-II staggered band alignment and defects formed at the ZnO/ZnSe interfaces should be the key factors for improved photocatalytic performance, and the probable photocatalytic mechanism was discussed in detail. [ABSTRACT FROM AUTHOR]

Zinc oxide (ZnO) nanophotocatalyst is a promising candidate for degrading organic pollutants but has an extremely low photocatalytic activity under nature sunlight. In this work, flower-like MoS 2 quantum dots/ZnO (MQ/ZnO) nanospheres with the size of approximately 1.26 μm are prepared at low temperature. The resultant flower-like MQ/ZnO nanospheres displayed higher photocatalytic activity than pure ZnO nanospheres under natural sunlight and without stirring, with the decomposition rate of the MQ/ZnO composites approximately 3.3 times higher than that of the pure ZnO nanospheres. Furthermore, the introduction of MoS 2 QDs endowed ZnO nanospheres with optical memory ability. The enhanced sunlight-driven photocatalytic activity is dependent on the unique electrical properties of MoS 2 QDs and the synergistic effect between ZnO and MoS 2 QDs. [ABSTRACT FROM AUTHOR]

Abstract: Zn0.97Cu0.01V0.02O nanoparticles have been successfully prepared by the sol–gel method and sintered at 600°C in argon and air atmosphere, respectively. The effects of annealing atmosphere on the structural, optical and magnetic properties of the obtained samples were studied. The X-ray diffraction result showed that the Zn0.97Cu0.01V0.02O was single phase with the wurtzite structure of ZnO. The sample annealed in air had much better crystallization. Photoluminescence shows an increase in green emission when annealing in argon. The two Zn0.97Cu0.01V0.02O samples exhibited ferromagnetism at room temperature. The ferromagnetism in this study was itself property of Cu, V co-doped ZnO and not originated from the secondary phase. [Copyright &y& Elsevier]

Abstract: The Cr-doped zinc oxide (Zn1−x Cr x O, 0≤x≤0.08) diluted magnetic semiconductors have been synthesized successfully by the sol–gel method. Investigations on magnetic, optical and structural properties of the produced samples have been done. Energy dispersive spectroscopy (EDS) shows the existence of Cr ion in the Cr-doped ZnO. The results of X-ray diffraction (XRD), the transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) indicate that the Cr ions are at least partially substitutionally incorporated into the crystal lattice of ZnO. The produced samples show good high-T c (Curie temperature) ferromagnetism (FM) in Cr-doped ZnO nanoparticles with Cr concentration of less than 5at%. The results of photoluminescence (PL) further testify that FM is an intrinsic property of the Cr-doped ZnO nanoparticles. And the occurrence of FM should mainly contribute to the Cr doping. [Copyright &y& Elsevier]