Search

Adsorption of small pellicle proteins statherin or proline-rich protein 1 (PRP1), respectively, and subsequent adsorption of human whole saliva (HWS) or salivary mucin MUC5B, respectively, was studied using ellipsometry and total internal reflectance fluorescence. Differences in elution (using sodium dodecyl sulphate (SDS) solutions) between mixed and single protein films were also investigated. On both hydrophilic and hydrophobized surfaces HWS and MUC5B were found to adsorb to pre-adsorbed layers of statherin and PRP1, respectively. Statherin adsorption on both substrate types showed no or minor exchange by HWS or MUC5B and no change in SDS elution between mixed and single protein films. Small amounts of PRP1 were exchanged by HWS on both surface types and the SDS elutable fractions were similar or larger for mixed films compared to single protein films. PRP1 and MUC5B in sequence showed minor exchange of PRP1 on hydrophilic surfaces, while no exchange could be established on hydrophobized substrates. SDS elutable fractions decreased for PRP1 and MUC5B mixed films compared to single protein films. In conclusion, minor amounts of statherin and PRP1 are exchanged during the time course of the experiments, which indicates that these proteins may to a large extent remain incorporated in the pellicle.

The salivary protein statherin is known to adsorb selectively onto hydroxyapatite (HA), which constitutes the main mineral of the tooth enamel. This adsorption is believed to be crucial for its function as an inhibitor of primary (spontaneous) and secondary (crystal growth) precipitation of calcium phosphate salts present in saliva. A fragment corresponding to the first 21 N-terminus amino acids of statherin (StN21) was previously found to reduce the rate of demineralization of HA. Therefore, the interfacial properties of this peptide and statherin onto silica, hydrophobized silica and HA discs was studied by in situ ellipsometry. Their reversibility induced by dilution and elutability induced by buffer and sodium dodecyl sulfate (SDS) was also determined. The results revealed that statherin adsorbed at a greater extent onto the HA as compared to StN21, suggesting that the hydrogen bonding between the uncharged polar residues at the C-terminal region of statherin and HA contributes to its adsorption. However, on both silica surfaces the peptide adsorption appeared to proceed in a similar way. Onto the hydrophobized silica the adsorption of both peptides was suggested to occur either via multilayer formation or adsorption of aggregates from solution, while onto the hydrophilic silica adsorption of peptide aggregates from solution was the suggested mechanism. Further, both peptides were observed to be strongly adsorbed onto HA, even after SDS treatment, in comparison to the layers adsorbed onto hydrophobized silica. Both peptide layers were found to be weakly adsorbed onto the hydrophilic silica surface as they were totally removed by buffer dilution.

In situ ellipsometry was used to study layer-by-layer film formation on hydrophilic and hydrophobized silica surfaces by alternating sequential adsorption of human mucin MUC5B and cationic proteins lysozyme, lactoferrin, lactoperoxidase or histatin 5, respectively. The stability of the multilayers was investigated by addition of sodium dodecyl sulfate solution (SDS). Atomic force microscopy was employed to investigate morphological structures on the surfaces during the layer-by-layer film build-up. It was clearly shown that, on both hydrophilic and hydrophobized silica, only MUC5B and lactoperoxidase showed the ability for multilayer formation, resulting in an approximately linear increase in adsorbed amount and film thickness with each deposition cycle. The net increase in amounts per cycle was larger on the hydrophilic silica. Further, MUC5B needs to be adsorbed first on the hydrophilic substrates to obtain this fast build-up behavior. Generally, addition of SDS solution showed that a large fraction of the adsorbed film could be desorbed. However, films on the hydrophobized silica were more resistant to surfactant elution. In conclusion, MUC5B-cationic protein multilayers can be formed on hydrophilic and hydrophobized silica, depending on the choice of the cationic protein as well as in which order the build-up is started on hydrophilic silica. Additionally, SDS disrupts the layer-by-layer film formed by MUC5B and lactoperoxidase.

Bovine submaxillary mucin (BSM) and chitosan were used to build layer-by-layer structures on solid substrates. The build-up was monitored using in situ ellipsometry to obtain time resolved values of the thickness and adsorbed amount. Additionally surface morphology during build-up was studied by atomic force microscopy (AFM). It was found that the adsorbed amount of the film increases approximately linearly with each deposition cycle on hydrophobized silica whereas construction on silica was found not to be possible at the experimental conditions used. We conclude that sufficient amount of the first mucin layer is crucial for the subsequent multilayer formation. The complex build-up kinetics on hydrophobized silica is characterized by adsorption and redissolution processes and the overall growth is the sum of both processes. AFM imaging on hydrophobized silica also confirmed the presence of redissolution processes and chitosan addition led to a reduction both in the number of surface aggregates and in the roughness of the surface. The present work also shows that by adjusting the relative concentrations of the polyelectrolytes it is possible to change the growth rate considerably. The final structures after deposition of 8 bilayers were found to have a high content of water and film stability test revealed that a substantial amount dissolves when increasing electrolyte concentration or pH of the ambient solution. Human mucin from saliva (MUC5B) was also used to create multilayers with chitosan on hydrophobized silica and it was revealed that no redissolution appears to be present in this system.