Fe78B15Sn7 and (Fe3Co1)78B15Sn7 amorphous metallic alloys were prepared using the method of planar flow casting. The amorphous nature of ribbons containing 7 at. % Sn was verified by X-ray diffraction. The resulting chemical composition was checked by flame atomic absorption spectroscopy and by mass spectrometry with inductively coupled plasma. The microstructure of the as-quenched metallic glasses was investigated by 57-Fe and 119-Sn Mössbauer spectrometry. The experiments were performed with transmission geometry at 300 K, 100 K, and 4.2 K, and in an external magnetic field of 6 T. The replacement of a quarter of the Fe by Co did not cause significant modifications of the hyperfine interactions in the 57-Fe nuclei. The observed minor variations in the local magnetic microstructure were attributed to alterations in the topological short-range order. However, the in-field 57-Fe Mössbauer spectra indicated a misalignment of the partial magnetic moments. On the other hand, the presence of Co considerably affected the local magnetic microstructure of the 119-Sn nuclei. This was probably due to the higher magnetic moment of Co, which induces transfer fields and polarization effects on the diamagnetic Sn atoms. [ABSTRACT FROM AUTHOR]

Fe78B15Sn7 and (Fe3Co1)78B15Sn7 amorphous metallic alloys were prepared using the method of planar flow casting. The amorphous nature of ribbons containing 7 at. % Sn was verified by X-ray diffraction. The resulting chemical composition was checked by flame atomic absorption spectroscopy and by mass spectrometry with inductively coupled plasma. The microstructure of the as-quenched metallic glasses was investigated by 57-Fe and 119-Sn Mössbauer spectrometry. The experiments were performed with transmission geometry at 300 K, 100 K, and 4.2 K, and in an external magnetic field of 6 T. The replacement of a quarter of the Fe by Co did not cause significant modifications of the hyperfine interactions in the 57-Fe nuclei. The observed minor variations in the local magnetic microstructure were attributed to alterations in the topological short-range order. However, the in-field 57-Fe Mössbauer spectra indicated a misalignment of the partial magnetic moments. On the other hand, the presence of Co considerably affected the local magnetic microstructure of the 119-Sn nuclei. This was probably due to the higher magnetic moment of Co, which induces transfer fields and polarization effects on the diamagnetic Sn atoms.