This study investigates the hygrothermal aging effect on the tensile and impact behavior of flax/PLA biocomposites. Specimens underwent up to four weeks of conditioning at 40°C in a climate chamber with water. Analysis covered porosity, moisture diffusibility, and transversal microstructure, enabling assessment of tensile strength, tensile modulus, and impact performance in relation to moisture uptake and fiber orientation. The study of tensile properties revealed that at approximately 12% moisture content, stiffness and yield stress decrease, while strength remains constant. Moisture diffusivity is higher in warp and weft yarn directions than the out‐of‐plane direction. Tensile testing at environmental equilibrium moisture reveals greater stiffness in the weft direction, correlated with lower crimp percentage and yarn angle. The main contribution of the paper is the study of the influence of moisture on the impact behavior, the results show that energy absorption capability of flax/PLA biocomposite increases with moisture content. Highlights: Fully biodegradable composite material by heat‐compression molding subjected to hygrothermal aging conditions for up to four weeks.The moisture diffusivity in both the warp and weft yarn directions registered higher values in comparison to the out‐of‐plane direction.Tensile testing at environmental equilibrium moisture revealed that the stiffness in the weft direction presented higher values.At 12% of moisture uptake, the stiffness and yield stress reached their lowest values, while strength remained constant.However, the low‐velocity impact properties of the composites exhibited improvement with moisture. [ABSTRACT FROM AUTHOR]

The main goal of this study is the comparison of different reinforcement architectures on the low-velocity impact behavior of green composites. The study includes the comparison of unidirectional, basket weave, and twill weave flax/PLA composites, they are subjected to unidirectional tensile tests, drop-weight impact tests, and after-impact compression tests. Results show that the unidirectional composite demonstrates superior tensile strength and initial modulus due to reduced fiber crimp, while basket weave exhibits the highest energy absorption capability and strain capacity attributed to its higher fiber–weight ratio and fiber crimp. Unidirectional composite also shows a larger impacted damage area compared to basket weave and twill weave, attributed to its internal architecture. Residual compressive strength across all composites decreased by 40% compared to the reference sample. However, the reduction in stiffness after impact was different, UD/PLA composite stiffness was reduced by 30% while the reduction in BW/PLA and T/PLA composites was about 20%. [ABSTRACT FROM AUTHOR]