Liquid fuel production from biomass-derived molecules has received great attention due to the diminished fossil fuel reserves, growing energy demand, and the necessity of CO2 emission reduction. The deoxygenation of oils and fatty acids is a promising process to obtain "green" diesel. Herein, we report the results of the study of the deoxygenation of stearic acid to alkanes as a model reaction. Series of Ni-supported on schungite were obtained by precipitation in subcritical water (hydrothermal deposition) and for comparison via wetness impregnation followed, in both cases, by calcination at 500 °C and a reduction in H2 at 300 °C. The catalyst obtained via hydrothermal synthesis showed a three-fold higher specific surface area with a four-fold higher active phase dispersion compared to the catalysts synthesized via conventional impregnation. The catalysts were tested in stearic acid deoxygenation in supercritical n-hexane as the solvent. Under optimized process conditions (temperature of 280 °C, hydrogen partial pressure of 1.5 MPa, and 13.2 mol of stearic acid per mol of Ni), a close to 100% yield of C10–C18 alkanes, containing over 70 wt.% of targeted n-heptadecane, was obtained after 60 min of reaction. [ABSTRACT FROM AUTHOR]

Here, we developed magnetically recoverable biocatalysts based on magnetite nanoparticles coated with an ultra-thin layer (about 0.9 nm) of chitosan (CS) ionically cross-linked by sodium tripolyphosphate (TPP). Excessive CS amounts were removed by multiple washings combined with magnetic separation. Glucose oxidase (GOx) was attached to the magnetic support via the interaction with N-hydroxysuccinimide (NHS) in the presence of carbodiimide (EDC) leading to a covalent amide bond. These steps result in the formation of the biocatalyst for D-glucose oxidation to D-gluconic acid to be used in the preparation of pharmaceuticals due to the benign character of the biocatalyst components. To choose the catalyst with the best catalytic performance, the amounts of CS, TPP, NHS, EDC, and GOx were varied. The optimal biocatalyst allowed for 100% relative catalytic activity. The immobilization of GOx and the magnetic character of the support prevents GOx and biocatalyst loss and allows for repeated use. [ABSTRACT FROM AUTHOR]