The mechanical performance and microstructures of a CoCrNi medium-entropy alloy (MEA) and NCoCrNi, alloyed with 0.5at% N, after high pressure torsion (HPT) and subsequent annealing treatments in a temperature range of 150-1000 {\deg}C were investigated. The introduction of N results in a reduction of grain size by 40% and ~10-15% increased hardness and bending strength after HPT. Both materials showed strain hardening and plasticity after HPT even at these strength levels over 1500 MPa which is induced by the saturated nanocrystalline state. Annealing at intermediate temperatures of 300-500 {\deg}C resulted in an additional increase of hardness and strength by ~20-40%, compared to the HPT deformed state. This effect was ~10 % more pronounced in the nitrogen alloyed CoCrNi that also showed better thermal stability. However, the increase in strength after 500 {\deg}C annealing was accompanied by a drastic loss of ductility in both materials., Comment: This work was supported by the project from the European Unions Horizon 2020 Research and Innovation Programme under the Marie Sk{\l}odowska-Curie Grant Agreement No101062549. In review as MSEA-D-24-02972

Hydrogen is a promising energy carrier for replacing fossil fuels, and hydrogen production via hydrogen evolution reaction (HER) is an environmentally friendly option if electrocatalysts with low overpotentials and long-term stability are used. In this work, the electrocatalytic performance of $\mathrm{Pt_{57.5}Cu_{14.7}Ni_{5.3}P_{22.5}}$ bulk metallic glass (BMG) with flat, micro-patterned, and nano-patterned surfaces for HER in 0.5 M H2SO4 is studied. The nano-patterned Pt-BMG demonstrates outstanding long-term stability and self-improving behavior with a final overpotential of 150 mV and a Tafel slope of 42 $\mathrm{mV dec^{-1}}$ after 1000 linear sweep voltammetry (LSV) cycles, which is respectively 42% and 37% lower than in the first LSV cycle. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) indicate the formation of a layer of CuO/Cu2O foam deposited on top of the nano-patterned surface during the stability test of 1000 LSV cycles. A three-step process is proposed to explain the formation of CuxO foam via dynamic hydrogen bubble templating (DHBT) electrodeposition from Cu dissolution of the Pt-BMG without using copper salt. This work provides a method to create CuxO foams that could be used for various applications. Moreover, nano-patterned BMGs with DHBT deposition offer a feasible strategy to synthesize metal or metal-oxide foams., Comment: 28 pages, 9 figures (including supplementary information)