Search

Nanocrystalline diamond (NCD) films are attractive for many applications due to their smooth surfaces while holding the properties of diamond. However, their growth rate is generally low using common Ar/CH4 with or without H2 chemistry and strongly dependent on the overall growth conditions using microwave plasma chemical vapor deposition (MPCVD). In this work, incorporating a small amount of N2 and O2 additives into CH4/H2 chemistry offered a much higher growth rate of NCD films, which is promising for some applications. Several novel series of experiments were designed and conducted to tailor the growth features of NCD films by fine-tuning of the gas-phase compositions with different amounts of nitrogen and oxygen addition into CH4/H2 gas mixtures. The influence of growth parameters, such as the absolute amount and their relative ratios of O2 and N2 additives; substrate temperature, which was adjusted by two ways and inferred by simulation; and microwave power on NCD formation, was investigated. Short and long deposition runs were carried out to study surface structural evolution with time under identical growth conditions. The morphology, crystalline and optical quality, orientation, and texture of the NCD samples were characterized and analyzed. A variety of NCD films of high average growth rates ranging from 2.1 μm/h up to 6.7 μm/h were successfully achieved by slightly adjusting the O2/CH4 amounts from 6.25% to 18.75%, while that of N2 was kept constant. The results clearly show that the beneficial use of fine-tuning of gas-phase compositions offers a simple and effective way to tailor the growth characteristics and physical properties of NCD films for optimizing the growth conditions to envisage some specific applications. [ABSTRACT FROM AUTHOR]

Heart failure (HF) is a clinical entity included in cardiovascular diseases affecting millions of people worldwide, being a leading cause of hospitalization of older adults, and therefore imposing a substantial economic burden on healthcare systems. HF is characterized by dyspnea, fatigue, and edema associated with elevated blood levels of natriuretic peptides, such as N Terminal pro-B-type Natriuretic Peptide (NT-proBNP), for which there is a high demand for point of care testing (POCT) devices. Optical fiber (OF) biosensors offer a promising solution, capable of real-time detection, quantification, and monitoring of NT-proBNP concentrations in serum, saliva, or urine. In this study, immunosensors based on plasmonic uncladded OF tips were developed using OF with different core diameters (200 and 600 µm). The tips were characterized to bulk refractive index (RI), anddetection tests were conducted with NT-proBNP concentrations varying from 0.01 to 100 ng/mL. The 200 µm sensors showed an average total variation of 3.6 ± 2.5 mRIU, an average sensitivity of 50.5 mRIU/ng·mL−1, and a limit of detection (LOD) of 0.15 ng/mL, while the 600 µm sensors had a response of 6.1 ± 4.2 mRIU, a sensitivity of 102.8 mRIU/ng·mL−1, and an LOD of 0.11 ng/mL. Control tests were performed using interferents such as uric acid, glucose, and creatinine. The results show the potential of these sensors for their use in biological fluids. [ABSTRACT FROM AUTHOR]

Cr-doped Al2O3 spheres with strong red emission were produced using a simple laser processing approach with a 50 W continuous CO2 laser. Structural characterization revealed that the produced spheres were monophasic, comprising the α-Al2O3 phase. Photoluminescence (PL) studies indicated that the observed red emission originates from multiple Cr3+ optical centers being dominated by the 2E → 4A2 transition (R-lines), with a further contribution from the parity and spin forbidden 2T1 → 4A2 transition (R′-lines). The identification of additional radiative recombination from chromium ion pairs (N-lines) evidences that the produced samples are heavily doped. As such, energy transfer processes between the different chromium optical centers are seen to take place, as suggested by the lifetime decay analysis. PL excitation revealed that the room temperature luminescence is preferentially populated via the spin-allowed 4A2 → 4T2,4T1 transitions and by the parity and spin-forbidden 4A2 → 2T2 (B-lines), 2T1 (R′-lines), 2E (R-lines). Such results demonstrate that the present synthesis method is able to deliver high-optical-quality Al2O3:Cr crystals in a fast and simple way, with potential interest for optical, sensing, or lasing applications. [ABSTRACT FROM AUTHOR]