In the present research, glass and basalt fiber-reinforced polypropylene composites' behaviour in quasi-static and dynamic conditions is studied. Composites were fabricated by vacuum assisted Compression molding method. Composites failure under quasi-static tension and compressive conditions was studied along with its failure behaviour under low-velocity impact and super-sonic shock loading under dynamic conditions. The study results showed that basalt fiber-reinforced polypropylene (Basalt/PP) composite's tensile and compressive strength is higher than glass fiber-reinforced polypropylene (Glass/PP). The Basalt/PP showed no penetration against low velocity impact (LVI) with negligible deformations till 50 J. However, the Glass/PP perforated at 50 J with various failure patterns occurring at back side. The fiber-matrix interface adhesion plays an important role in super-sonic shock loading by absorbing shock wave energy due to ductile nature of polypropylene and the two composites absorbed energy via matrix and fibers failure, no brittle failure of laminates occurred under shock loading. [ABSTRACT FROM AUTHOR]

All bioresorbable polymeric implants are radiolucent, making them undetectable under the X-rays. Therefore, to improve their X-ray visibility, the high effective atomic number (Zeff) material such as Pt, Au, Ta, Ba, or its alloy are attached to the body of the bioresorbable implant. However, during the in vivo degradation, these bio-inert heavy metals can either detach or leach out from the lesion site and accumulate into the vital organ, leading to severe health complications. Thus, as a strategy, the novel biodegradable and radiopaque Mg alloy was produced to impart X-ray visibility in the biopolymer. Here, the Mg was alloyed with the optimized ratio of heavy metals, i.e., Zn and Y. The radiopaque Mg alloy was characterized and powdered to the size of 25–20 µm. Further, it was blended with radiolucent Poly-L-lactic acid (PLLA) and polycaprolactone (PCL) polymer. The Bi-axially expanded (BAE) tubes of PLLA/PCL and PLLA/PCL/Mg alloy (5% wt.) were extruded for fabricating cardiovascular stents. The BAE tube comparison studies were performed for thermal stability, wettability, surface roughness, and mechanical properties. The potential of 5% Mg alloy in the polymeric matrix was evaluated as a nucleating, reinforcing, and radiopaque agent. In vitro accelerated degradation study was performed in the physiological fluid to evaluate the pH variation and decomposition rate. Finally, in vitro biocompatibility was assessed by evaluating the behavior of L929 fibroblast cells, followed by the blood biocompatibility test on the blends. [ABSTRACT FROM AUTHOR]