Search

Woven flax-carbon hybrid polyamide biocomposites offer a blend of carbon fibers' mechanical strength and flax's environmental advantages, potentially developing material applications. This study investigated their thermal behavior, degradation kinetics, and durability to water uptake and relative humidity exposure and compared them with pure flax and carbon composites with the same matrix. The hybrid composite exhibited intermediate water/moisture absorption levels between pure flax and carbon composites, with 7.2% water absorption and 3.5% moisture absorption. It also displayed comparable thermal degradation resistance to the carbon composite, effectively maintaining its weight up to 300 °C. Further analysis revealed that the hybrid composite exhibited a decomposition energy of 268 kJ/mol, slightly lower than the carbon composite's value of 288.5 kJ/mol, indicating similar thermal stability. Isothermal lifetime estimation, employing the activation energy (Ed) and degree of conversion facilitated by the Model Free Kinetics method, indicated a 41% higher service life of the hybrid laminate at room temperature compared to the carbon laminate. These insights are crucial for understanding the industrial applications of these materials without compromising durability. [ABSTRACT FROM AUTHOR]

Fiber hybridization is suggested to enhance the properties of fiber‐reinforced composites. Regarding the matrix, thermoplastic alternatives to conventional thermosets are needed to balance mechanical performance and sustainability. We combined woven flax and carbon fibers with a polyamide 11 matrix into a hybrid biocomposite and studied its manufacturing process as well as its impact, tensile, and damping properties. Mechanical damage was investigated using scanning electron microscopy and X‐ray computed tomography. Hybridization significantly improved the tensile properties: 233% higher modulus and 432% higher strength than pure flax composites and 19% higher failure strain than pure carbon composites. Additionally, the hybrid composites exhibited a positive hybrid effect with respect to the impact resistance, characterized by higher displacement at maximum impact force and occurrence of combined damage mechanisms. Although the damping behavior of the hybrid composites remained inferior to that of pure flax composites, their damping factor was 20% higher than that of pure carbon composites. These results provide valuable insights into the mechanical performance of carbon‐flax hybrid composites. Highlights: Enhanced mechanical performance and impact resistance in woven flax‐carbon/PA11 hybrid biocomposite compared to nonhybrid reference composites.Superior tensile modulus and strength of hybrid biocomposite than pure flax fiber composite, and greater failure strain than pure carbon fiber composite.A positive hybridization effect in impact properties with a greater displacement at maximum force and higher dissipated impact energy, indicating enhanced ductility and fracture toughness.Improved damping behavior in hybrid biocomposite compared to the pure carbon composite. [ABSTRACT FROM AUTHOR]

Metal additive manufacturing (AM) technology has been utilized in many industries including automotive, aerospace, and medical. AM Ti6Al4V (Ti64) alloy is highly noticed for production of medical instruments such as dental implants and the machining process is mostly needed during the production or post-processing of these components. Numerical model, as a powerful tool, can be efficiently used for analyzing the machining process. A customized model was employed using a user-written subroutine in this work to evaluate machinability and microstructural changes in cryogenic machining of AM Ti64 alloy. For this purpose, the microstructural changes were simulated as the new numerical outputs. The numerical results of cutting forces, temperature, nano-hardness, and alpha lamellae thickness (grain size) were successfully verified by corresponding experiments from literature. Then, the impact of tool geometry (including rake and clearance angles, cutting edge radius, and nose radius) on the machinability performance was examined. It was found that, the variation of clearance and rake angles were more effective on depth of the hardened layer compared to the other parameters. Thickness of alpha lamellae phase near the machined surface and depth of the affected layer by nano-hardness changes were changed from 0.9 to 1.58 µm, and from 18 to 40 µm, respectively. Overall, it was concluded that the variation of insert positioning made by tool holder (change in rake and clearance angles) was an effective parameter on the process outputs when machining AM Ti64 alloy. [ABSTRACT FROM AUTHOR]

Cavitation erosion poses a significant challenge in fluid systems like hydraulic turbines and ship propellers due to pulsed pressure from collapsing vapor bubbles. To combat this, various materials and surface engineering methods are employed. In this study, nano and micro scale particles of silicon carbide (SiC) or boron carbide (B4C) were incorporated as reinforcement at 6% and 12% ratios, owing to their exceptional resistance to abrasive wear and high hardness. Microparticles were incorporated to assess the damage incurred during the tests in comparison to nanoparticles. Wear tests were conducted on both bulk samples and coated aluminum sheets with a 1mm of composite. Additionally, cavitation tests were performed on coated aluminum tips until stability of mass loss was achieved. The results indicated a distinct wear behavior between the coatings and the bulk samples. Overall, wear tended to be higher for the coated samples with nanocomposites than bulk, except for the nano-composite material containing 12% SiC and pure resin. With the coatings, higher percentages of nanometric particles correlated with increased wear. The coefficient of friction remained within the range of 0.4 to 0.5 for the coatings. Regarding the accumulated erosion in the cavitation tests for 100 min, it was observed that for all nanocomposite materials, it was lower than in pure resin. Particularly, the composite with 6% B4C was slightly lower than the rest. In addition, the erosion rate was also lower for the composites. [ABSTRACT FROM AUTHOR]

Because of the high demand for carbon fiber reinforced polymer (CFRP) materials across all industries, the reuse and/or recycling of these materials (rCFRP) is necessary in order to meet the principles of the circular economy, including recycling and reuse. The objective of this study is to estimate the lifespan of thermoplastic matrix composite materials reinforced with waste materials (CFRP), which undergo only a mechanical cutting process. This estimation is carried out through the thermal decomposition of polymers, including polymer matrix composite materials, which is a complex process due to the numerous reactions involved. Some authors calculate these kinetic parameters using thermogravimetric analysis (TGA) as it is a quick method, and it allows the identification of gases released during decomposition, provided that the equipment is prepared for it. This study includes a comparison between polyamides 11 and 12, as well as between polyamide composite materials with carbon fiber (CF) and polyamides reinforced with CF/epoxy composite material. The latter is treated with plasma to improve adhesion with polyamides. The behavior of weight as a function of temperature was studied at speeds of 3, 6, 10, 13, 17, and 20 °C/min, finding stability of the polyamides up to a temperature of 400 °C, which was consistent with the analysis by mass spectroscopy, where gas evolution is evident after 400 °C. The estimation of the lifespan was carried out using two different methods including the Toop equation and the free kinetics model (MFK). The energy of the decomposition process was determined using the MFK model, which establishes the energy as a function of the degree of conversion. It is estimated that at 5% decomposition, mechanical properties are lost. [ABSTRACT FROM AUTHOR]

Background: Data on the epidemiology of inflammatory bowel disease (IBD) in the Middle East are scarce. We aimed to describe the clinical phenotype, disease course, and medication usage of IBD cases from Iran in the Middle East. Methods: We conducted a cross-sectional study of registered IBD patients in the Iranian Registry of Crohn's and Colitis (IRCC) from 2017 until 2022. We collected information on demographic characteristics, past medical history, family history, disease extent and location, extra-intestinal manifestations, IBD medications, and activity using the IBD-control-8 questionnaire and the Manitoba IBD index, admissions history, history of colon cancer, and IBD-related surgeries. Results: In total, 9746 patients with ulcerative colitis (UC) (n = 7793), and Crohn's disease (CD) (n = 1953) were reported. The UC to CD ratio was 3.99. The median age at diagnosis was 29.2 (IQR: 22.6,37.6) and 27.6 (IQR: 20.6,37.6) for patients with UC and CD, respectively. The male-to-female ratio was 1.28 in CD patients. A positive family history was observed in 17.9% of UC patients. The majority of UC patients had pancolitis (47%). Ileocolonic involvement was the most common type of involvement in CD patients (43.7%), and the prevalence of structuring behavior was 4.6%. A prevalence of 0.3% was observed for colorectal cancer among patients with UC. Moreover,15.2% of UC patients and 38.4% of CD patients had been treated with anti-tumor necrosis factor (anti-TNF). Conclusion: In this national registry-based study, there are significant differences in some clinical phenotypes such as the prevalence of extra-intestinal manifestations and treatment strategies such as biological use in different geographical locations. [ABSTRACT FROM AUTHOR]