Search

The present work deals with analyzing the effect of silicon dioxide on mechanical and thermal stability of hybrid polymer composite. Compression molding is adopted to develop the hybrid composite with constant 0.5 wt.% of graphene and varying wt.% of silicon dioxide (2, 4 & 6 wt.%). Modified hummers method is used to synthesis graphene by chemical exfoliation of graphene from graphite flakes. Mechanical properties of developed composite is investigated using tensile, flexural, impact and interlaminar shear testing follow by fracture surface analysis of tested samples. Thermal stability is examined by thermogravimetric analysis and functional group confirmation is carried out using Fourier transform infrared spectroscopy (FTIR). Investigation over mechanical properties of fabricated composite reveals that addition of silicon dioxide up to 4 wt.% depicted higher flexural and tensile strength. Increment in silicon dioxide percentage improves the toughness of composite. FTIR results confirms the presence of asymmetric stretching vibrations due the after effect of hybrid fillers. Thermogravimetric analysis results depict that incorporation silicon dioxide increases the activation of energy of matrix from ~ 24.2 to 31.5 kJ/mol. [ABSTRACT FROM AUTHOR]

In recent years, the growing environmental awareness has prompted increased attention towards the substitution of nonrecyclable thermosetting epoxy resin composite materials with recyclable thermoplastic composite materials. The objective of this study is to utilize a laboratory‐made polymethyl methacrylate (PMMA)/methyl methacrylate (MMA) binary liquid resin (PMBLR) to prepare thermoplastic resin/glass fiber (GF) composite materials using the vacuum‐assisted perfusion method. These composites are then compared with GF‐reinforced thermosetting epoxy resin composites. The investigation reveals a significant influence of benzoyl peroxide (BPO) content on the mechanical properties of pure MMA and PMBLR casting resins, which also incorporate N‐methyl‐N‐((1‐methyl‐1H‐indol‐3‐yl) methyl) aniline (DMA) as redox composite initiators. The optimal mechanical properties for both types of casting resins are achieved at a DMA:BPO:MMA ratio of 0.5:1.2:100. Additionally, at a PMMA concentration of 24 wt% in PMBLR under this specific initiator ratio, the composites demonstrate the most desirable properties. Furthermore, a comparative analysis of PMBLR/GF composites and epoxy/GF composites indicates that the former exhibit superior 90° tensile strength, bending strength, and short beam shear strength. The fracture morphology analysis highlights discernible micro‐ductile fracture characteristics in PMBLR/GF composites, distinguishing them from epoxy/GF composites. Dynamic thermomechanical analysis (DMA) results further reveal a higher storage modulus and loss factor in PMBLR/GF composites when compared to epoxy/GF composites. Highlights: Glass fiber‐reinforced composites were fabricated at ambient temperature.A degradable PMMA/MMA binary thermoplastic resin (PMBLR) was developed as a replacement for non‐degradable epoxy.PMBLR composites exhibit enhanced strength compared to epoxy: tensile (+18.8%), bending (+27.4%), and short beam shear (+34.3%). [ABSTRACT FROM AUTHOR]

This paper presents a study regarding the obtaining, characterizing and mechanically testing a new laminar composite material, consisting of epoxy resin reinforced with basalt plain fabric. The composites were obtained by manual lay-up, cross-link stage being developed by pressure molding in a hydraulic press. Rectangular plates were obtained and cut into samples with specific shapes, for the mechanical tests (tensile, three-point bending and compression). After testing, the fracture zone was analyzed using optical microscopy to observe the behavior of the composite following the mechanical stresses applied (fracture mechanism, voids presence and fiber delamination identification). Due to the low costs and non-hazardous nature, basalt fibers can be a serious competitor in the production of laminar composites that could successfully replace ordinary glass fiber composites. The mechanical properties in tensile, three-point bending, and compression of epoxy-resin-impregnated basalt fiber composites are comparable and even exceed those of widely used epoxy-resin-impregnated fiberglass composites. [ABSTRACT FROM AUTHOR]

In this study, we compare the effect of various precursor‐based graphene oxide (GO) nanofillers on enhancing the mechanical performance of E‐glass fiber‐reinforced epoxy resin composites (EGFPs). GO derived from bituminous coal (BC‐GO) and graphite (Gr‐GO) were dispersed into an epoxy resin matrix. The resulting mixture was combined with E‐glass fiber mats using vacuum‐assisted resin infusion molding. Notable improvements (38.9% in flexural strength, 22.9% in tensile strength, and 21.6% in impact strength) were observed in BC‐GO‐reinforced EGFPs at 0.25 phr loading of BC‐GO. The improvements for Gr‐GO‐reinforced EGFPs were 28%, 9.3%, and 6.8%, respectively. XRD analysis of BC‐GO showed a diffraction peak at 2θ = 20.9°. Except for this peak, no other crystalline peaks were observed when BC‐GO was incorporated into EGFPs. FTIR spectra of both composite samples, with or without the nanofiller, were similar due to the spectral peaks overlap. TEM demonstrated the exfoliated morphology of BC‐GO in EGFPs. These findings underscore the potential of BC‐GO as a cost‐effective reinforcement for polymer nanocomposites across various industrial applications, including the development of lightweight and strong materials for aerospace and automotive industries, protective coatings, petroleum, and aerospace production systems. Highlights: BC‐GO demonstrates superior mechanical performance compared to Gr‐GO in EGFPs.0.25 phr BC‐GO improves 38.9% flexural, 22.9% tensile, and 21.6% impact strengths.Beyond 0.25 phr, BC‐GO and Gr‐GO showed a decline in mechanical enhancement.Role of particle size, loading & adhesion to matrix analyzed using XRD, FTIR, and DLS.Coal‐GO is an attractive alternative nanofiller for EGFPs. [ABSTRACT FROM AUTHOR]

Glass fiber‐reinforced polymer‐matrix (GFRP) composites are used to manufacture devices such as radomes, electrical insulators, and radar‐absorbing structures, many of which are used in applications with strict mechanical and dielectric property requirements. As such, designs and properties of GFRP composite materials should be regularly improved to guarantee their safe operation and meet their constantly evolving application requirements. In this study, glass fiber (GF) particles and epoxy resin 128 (EP‐128) were used to manufacture high‐performance EP/GF‐X composites with GF particle contents ranging from 5% to 40%. An investigation into their mechanical and dielectric properties revealed that EP/GF‐20 composite specimens presented the best mechanical performance with their bending strength and modulus reaching 159.68 MPa and 6521.92 MPa, respectively, and an average dielectric constant of 4.862 within the 10–105 Hz frequency range. A theoretical analysis of the EP/GF‐X composite specimens' dielectric constants using classic dielectric models based on the Lichtenecker, Bruggeman, Jaysundere‐Smith, and Maxwell‐Garnett rule‐of‐mixture equations indicated that the dielectric model based on the Bruggeman rule‐of‐mixture equation provided the dielectric constants closest to the measured values with a maximum deviation of less than −0.321% for EP/GF‐40 composites. This study provides a feasible strategy to control the mechanical and dielectric properties of GFRP composites. Highlights: Glass fiber (GF) particles and epoxy 128 (EP‐128) resin were used to manufacture high‐performance glass fiber‐reinforced epoxy (EP/GF‐X) composites.The composite manufacturing process was carefully controlled to ensure uniform distribution and orientation of GF particles in the EP‐128 resin.The mechanical and dielectric properties of the manufactured EP/GF‐X composites were effectively tailored by controlling the content and distribution of GF particles in the EP‐128 resin matrix.The dielectric constants of the EP/GF‐X composites were measured experimentally and predicted using various theoretical dielectric models.The Bruggeman model provided the dielectric constants of the EP/GF‐X composites closest to the measured values. [ABSTRACT FROM AUTHOR]