Search

In this study, we compare the effect of various precursor‐based graphene oxide (GO) nanofillers on enhancing the mechanical performance of E‐glass fiber‐reinforced epoxy resin composites (EGFPs). GO derived from bituminous coal (BC‐GO) and graphite (Gr‐GO) were dispersed into an epoxy resin matrix. The resulting mixture was combined with E‐glass fiber mats using vacuum‐assisted resin infusion molding. Notable improvements (38.9% in flexural strength, 22.9% in tensile strength, and 21.6% in impact strength) were observed in BC‐GO‐reinforced EGFPs at 0.25 phr loading of BC‐GO. The improvements for Gr‐GO‐reinforced EGFPs were 28%, 9.3%, and 6.8%, respectively. XRD analysis of BC‐GO showed a diffraction peak at 2θ = 20.9°. Except for this peak, no other crystalline peaks were observed when BC‐GO was incorporated into EGFPs. FTIR spectra of both composite samples, with or without the nanofiller, were similar due to the spectral peaks overlap. TEM demonstrated the exfoliated morphology of BC‐GO in EGFPs. These findings underscore the potential of BC‐GO as a cost‐effective reinforcement for polymer nanocomposites across various industrial applications, including the development of lightweight and strong materials for aerospace and automotive industries, protective coatings, petroleum, and aerospace production systems. Highlights: BC‐GO demonstrates superior mechanical performance compared to Gr‐GO in EGFPs.0.25 phr BC‐GO improves 38.9% flexural, 22.9% tensile, and 21.6% impact strengths.Beyond 0.25 phr, BC‐GO and Gr‐GO showed a decline in mechanical enhancement.Role of particle size, loading & adhesion to matrix analyzed using XRD, FTIR, and DLS.Coal‐GO is an attractive alternative nanofiller for EGFPs. [ABSTRACT FROM AUTHOR]

Fiber-reinforced polymer composites are manufactured using various methods, with vacuum-assisted resin transfer molding (VARTM or VARIM). This study's primary focus lies in assessing how the orientation of sampling impacts the mechanical properties of glass fiber-reinforced pure and nanocomposites. 2 wt.% nano Al2O3- doped and non-doped composites were produced using the VARTM process. Tensile, flexural, and density test specimens were extracted from three distinct zones and two distinc direction those aligned horizontally to the resin flow (HRF) and those oriented vertically to the resin flow (VRF). Remarkably, results showed up to a 3.91% increase in values from samples in the third zone, particularly on the vacuum outlet side. To facilitate precise stress value comparisons across plates, uniform sample orientation and consistent zone selection are essential. [ABSTRACT FROM AUTHOR]

Glass fiber‐reinforced polymer‐matrix (GFRP) composites are used to manufacture devices such as radomes, electrical insulators, and radar‐absorbing structures, many of which are used in applications with strict mechanical and dielectric property requirements. As such, designs and properties of GFRP composite materials should be regularly improved to guarantee their safe operation and meet their constantly evolving application requirements. In this study, glass fiber (GF) particles and epoxy resin 128 (EP‐128) were used to manufacture high‐performance EP/GF‐X composites with GF particle contents ranging from 5% to 40%. An investigation into their mechanical and dielectric properties revealed that EP/GF‐20 composite specimens presented the best mechanical performance with their bending strength and modulus reaching 159.68 MPa and 6521.92 MPa, respectively, and an average dielectric constant of 4.862 within the 10–105 Hz frequency range. A theoretical analysis of the EP/GF‐X composite specimens' dielectric constants using classic dielectric models based on the Lichtenecker, Bruggeman, Jaysundere‐Smith, and Maxwell‐Garnett rule‐of‐mixture equations indicated that the dielectric model based on the Bruggeman rule‐of‐mixture equation provided the dielectric constants closest to the measured values with a maximum deviation of less than −0.321% for EP/GF‐40 composites. This study provides a feasible strategy to control the mechanical and dielectric properties of GFRP composites. Highlights: Glass fiber (GF) particles and epoxy 128 (EP‐128) resin were used to manufacture high‐performance glass fiber‐reinforced epoxy (EP/GF‐X) composites.The composite manufacturing process was carefully controlled to ensure uniform distribution and orientation of GF particles in the EP‐128 resin.The mechanical and dielectric properties of the manufactured EP/GF‐X composites were effectively tailored by controlling the content and distribution of GF particles in the EP‐128 resin matrix.The dielectric constants of the EP/GF‐X composites were measured experimentally and predicted using various theoretical dielectric models.The Bruggeman model provided the dielectric constants of the EP/GF‐X composites closest to the measured values. [ABSTRACT FROM AUTHOR]