Search

Glass fiber‐reinforced resin matrix composites have good mechanical and impact resistance properties, while with particle co‐reinforcement, a synergistic effect can further improve their performance. In this paper, continuous glass fiber‐reinforced nylon 6 (GF/PA6) and continuous glass fiber (GF) with glass beads (GBs) co‐reinforced nylon 6 (GB–GF/PA6) were prepared to investigate the co‐reinforcement mechanism and the synergistic effect of particle and fiber. A quantitative parameter of the residual impact force divided by the critical force Pr/Pcr, as the damage degree of the low‐velocity impact, is defined to evaluate the impact resistance of the composite. The results indicate that the damage of GB–GF/PA6 was lower than that of GF/PA6, and the synergistic effect reaches the most obvious at the GB addition of 10 wt%. Scanning electron microscope (SEM) and x‐ray computed tomography (XCT) images disclose that GB impedes the type II crack spread in the matrix and fiber/matrix interface. With the type II cracks reducing, the materials' resistance to delamination can be significantly enhanced. For the composite structure, in which 10 wt% GB and 60 wt% GF are introduced, the flexural strength, shear strength, and pendulum impact strength were tested with the maximum values of 379.4 MPa, 53.1 MPa, and 219.0 J/m2, respectively. This composite structure design, presenting a continuous GF and GBs co‐reinforce effect, offers a manufacturing process that is easily scalable to achieve excellent characteristics. [ABSTRACT FROM AUTHOR]

Honeycomb composite with excellent mechanical–physical properties had attracted extensive attention. To achieve outstanding sound insulation while maximizing the high‐performance of honeycomb composite, this article reported a honeycomb composite structure filled with glass fiber (HFG) based on a paper‐making process and the corresponding sandwich structure. Pulping parameters, mechanical property, air permeability and sound insulation of HFG were analyzed. The results showed that the hanging index and settling height of glass fiber slurry were inversely proportional to the beating degree, which was beneficial for reducing the coefficient of variation (CV) of HFG with value of 4%–6%. The maximum improvement in tensile strength and bursting strength of HFG were 70% and 53%, respectively. In addition, sound transmission loss (STL) of HFG was proportional to cell size, density, filling amount and thickness of the honeycomb. Compared to HFG, sandwich structure consisting of HFG and glass fiber/hot melt fiber panels effectively improved STL, especially at low‐mid frequencies. It was also found that designing holes on the surface of sandwich structure could further improve STL in certain frequency bands. The structure offered a lightweight and high‐performance response for construction, transportation and infrastructure. Highlights: This article designs a new type of honeycomb filled glass fiber via paper‐making process, aiming to improve the comprehensive performance of honeycomb.By the design of embedded structure, the maximum improvement in tensile strength and bursting strength of honeycomb were 70% and 53%, respectively.By designing perforated, embedded and laminated structures, sound insulation has been improved, while reducing material quality. [ABSTRACT FROM AUTHOR]

The use of fillers in fiber-reinforced epoxy matrix composites to enhance the wear performance of the composite is a widely employed method nowadays. In this study, the effect of incorporating graphite filler into a glass fiber-reinforced composite structure on the tribological properties of the composite was investigated. Composite materials produced using the hand lay-up method with three different levels of graphite filler were compared to unfilled composites in terms of wear behavior under different loads (7 N, 10 N, 15 N) and sliding distances (200 m, 400 m). The influence of load, filler content, and sliding distance on the friction coefficient and wear rate was discussed. When the results are examined, the significant effects of graphite filler on wear volume and friction coefficient are clearly observed. In the composite containing 12% graphite, the wear volume has decreased by almost 96%; this ratio has been around 93% for the composite with 4% graphite filler. As the reinforcement of graphite and force increase, the friction coefficient decreases, whereas with the increase in sliding distance, the friction coefficient declines. Microstructural analysis revealed that the filled composites exhibited less abrasion compared to the unfilled composites, and the surface porosity and craters were shallower. [ABSTRACT FROM AUTHOR]