Search

The dual‐function retrofitting system that uses the carbon‐fabric reinforced cementitious matrix (C‐FRCM) as both the anode of impressed current cathodic protection (ICCP) system and the structural strengthening (SS) material, that is, an ICCP‐SS system, is investigated. The experimental program mainly focused on the shear behavior of C‐FRCM strengthened reinforced concrete (RC) continuous beam under the dual‐function retrofitting system. The influence of anode polarization on the shear strengthening of RC continuous beams is analyzed. Shear tests were conducted on a total of 14 corroded RC continuous beams to investigate the influence of key parameters, including anode polarization degree of prefabricated C‐FRCM plate, layer of carbon fiber mesh and side‐wrapping. The failure modes, shear capacities, and load‐deflection curves of the shear‐strengthened RC continuous beams are reported. Based on the test results, the applicability of relevant design codes was evaluated and found to provide rather conservative predictions for the shear capacity of the examined C‐FRCM strengthened RC continuous beams. [ABSTRACT FROM AUTHOR]

This study investigates the effect of strengthening self-compacted concrete (SCC) beams using CFRP sheets on flexural behaviour subjected to repeated loads. During the experiment, six rectangular reinforced SCC beams were evaluated; two were reference beams without strengthening, while the remaining four were strengthened with CFRP sheets. The beam's length, depth, and width are 2100 mm, 300 mm, and 200 mm, respectively. A monotonic load was applied to one of the reference beams, while repeated loads were applied to the remaining (compression cyclic loads). The main parameters studied in this experimental work were the type of loading (monotonic and repeated), the positions of strengthening and the dimensions of CFRP sheets. The flexural behaviour of these beams was investigated through experimental examination by recording the ultimate load and maximum deflection. Meanwhile, the cracks' pattern and failure modes were observed. The findings of the present study demonstrated that the limited cycles of repeated loads have marginal effect on the flexural behaviour of the beams. This results in an ultimate load reduction of no more than 11%. It was also noted that SCC beams strengthened using CFRP sheets subjected to repeated loads significantly affected the flexural behaviour of these beams. Consequently, the ultimate load of the strengthened beams was improved by up to 18%. Besides, the maximum deflection of the strengthened SCC beams was reduced by 45% compared to those without strengthening. Using strengthening throughout the beams' entire width and length that are subjected to repeated loads improved their ultimate load to surpass that of non-strengthened beams under monotonic loads by as much as 7%. [ABSTRACT FROM AUTHOR]

An experimental program was conducted to examine the seismic performance of flexural beam members strengthened with carbon fiber-reinforced polymer (CFRP) sheet and anchored using carbon fiber splay anchors. This research study extends the use of carbon fiber anchors to secure the top and bottom CFRP flexural sheets under cyclic loading. In this study, low strength concrete is examined, with lightly reinforced steel ratio (0.0034) to test full-scale rectangular beams. Five reinforced concrete beams were cast, strengthened, and tested under reversed cycles of four-point bending to failure. The beams were categorized into a control specimen, strengthened specimens with thin sheets with and without fiber anchors, and strengthened specimens with thick sheets with and without fiber anchors. They were tested cyclically under displacement control according to the AC 125 loading protocol. The failure modes ranged from classical ultimate failure for the control beam to rupture and intermediate crack (IC) debonding for the beam with unanchored thin CFRP sheets. On the other hand, debonding took place for the thicker sheets with no anchors, while the thicker sheets with fiber anchors underwent cover delamination failure mode despite the fact that the sheets were extended very close to the simple supports. The hysteresis response loops were compared for the different specimens and the analytical envelop curves were predicted resulting in a close agreement to the experimental finding. • Seismic performance of flexural beams CFRP strengthened with and without carbon fiber anchors is successfully examined. • Thicker CFRP sheets yield lower energy dissipation, ductility, but higher strength and seismic pinching. • Failure modes varied from sheet debonding to CFRP rupture and cover delamination. • The use of anchors at sheet ends was not very effective in extending the hysteretic cycles beyond those without anchors. • The need to apply fiber anchors along the entire shear span to harness improved behavior is clearly evident. [ABSTRACT FROM AUTHOR]

Plate end debonding is a common failure mode for fiber reinforced polymer (FRP) strengthened beams. FRP sheets and shape memory alloy (SMA) composites can effectively slow down plate end debonding and improve beam ductility owing to the anchorage effect of SMA wires on the FRP ends. This work aims to comprehensively study the anchorage performance of FRP/SMA composite strengthened beams through both model analysis and experimental investigation. The plate end debonding strength models of existing FRP strengthened beams were initially summarized and analyzed, and an improved model was proposed to predict the debonding strength of FRP/SMA composite strengthened beams at the plate end. Moreover, the anchorage performance and flexural behavior of beams strengthened with carbon fiber reinforced polymer (CFRP) and SMA composites were studied through experiments. The failure mode of the FRP sheet strengthened beams was plate end debonding failure, while the plate end debonding failure of the CFRP/SMA composite strengthened beams occurred at the strengthening zone end, and the peeling failure was delayed owing to the anchorage effect of SMA wires on the ends of the strengthening CFRP sheets. The recovery effect of SMA wires could successfully introduce prestress into CFRP sheets. Moreover, the CFRP strain corresponding to plate end debonding increased because of the anchorage of SMA wires on the CFRP sheet in the strengthening zone. The strength and ductility of the CFRP/SMA composite strengthened beam significantly improved. The proposed model for predicting the plate end debonding strength of FRP/SMA composite strengthened beams was validated through experiments. • An improved model is proposed to predict the debonding strength of beams strengthened with FRP/SMA composites at the plate ends. • The debonding failure was delayed due to the anchorage effect of SMA wires on CFRP sheets in the strengthening zone. • The strength and ductility of the beam strengthened with CFRP/SMA composites have been significantly improved. • The proposed model for predicting the plate end debonding strength of FRP/SMA composite strengthened beams was validated through experiments. [ABSTRACT FROM AUTHOR]