Search

This study investigates the effect of strengthening self-compacted concrete (SCC) beams using CFRP sheets on flexural behaviour subjected to repeated loads. During the experiment, six rectangular reinforced SCC beams were evaluated; two were reference beams without strengthening, while the remaining four were strengthened with CFRP sheets. The beam's length, depth, and width are 2100 mm, 300 mm, and 200 mm, respectively. A monotonic load was applied to one of the reference beams, while repeated loads were applied to the remaining (compression cyclic loads). The main parameters studied in this experimental work were the type of loading (monotonic and repeated), the positions of strengthening and the dimensions of CFRP sheets. The flexural behaviour of these beams was investigated through experimental examination by recording the ultimate load and maximum deflection. Meanwhile, the cracks' pattern and failure modes were observed. The findings of the present study demonstrated that the limited cycles of repeated loads have marginal effect on the flexural behaviour of the beams. This results in an ultimate load reduction of no more than 11%. It was also noted that SCC beams strengthened using CFRP sheets subjected to repeated loads significantly affected the flexural behaviour of these beams. Consequently, the ultimate load of the strengthened beams was improved by up to 18%. Besides, the maximum deflection of the strengthened SCC beams was reduced by 45% compared to those without strengthening. Using strengthening throughout the beams' entire width and length that are subjected to repeated loads improved their ultimate load to surpass that of non-strengthened beams under monotonic loads by as much as 7%. [ABSTRACT FROM AUTHOR]

An experimental program was conducted to examine the seismic performance of flexural beam members strengthened with carbon fiber-reinforced polymer (CFRP) sheet and anchored using carbon fiber splay anchors. This research study extends the use of carbon fiber anchors to secure the top and bottom CFRP flexural sheets under cyclic loading. In this study, low strength concrete is examined, with lightly reinforced steel ratio (0.0034) to test full-scale rectangular beams. Five reinforced concrete beams were cast, strengthened, and tested under reversed cycles of four-point bending to failure. The beams were categorized into a control specimen, strengthened specimens with thin sheets with and without fiber anchors, and strengthened specimens with thick sheets with and without fiber anchors. They were tested cyclically under displacement control according to the AC 125 loading protocol. The failure modes ranged from classical ultimate failure for the control beam to rupture and intermediate crack (IC) debonding for the beam with unanchored thin CFRP sheets. On the other hand, debonding took place for the thicker sheets with no anchors, while the thicker sheets with fiber anchors underwent cover delamination failure mode despite the fact that the sheets were extended very close to the simple supports. The hysteresis response loops were compared for the different specimens and the analytical envelop curves were predicted resulting in a close agreement to the experimental finding. • Seismic performance of flexural beams CFRP strengthened with and without carbon fiber anchors is successfully examined. • Thicker CFRP sheets yield lower energy dissipation, ductility, but higher strength and seismic pinching. • Failure modes varied from sheet debonding to CFRP rupture and cover delamination. • The use of anchors at sheet ends was not very effective in extending the hysteretic cycles beyond those without anchors. • The need to apply fiber anchors along the entire shear span to harness improved behavior is clearly evident. [ABSTRACT FROM AUTHOR]