Search

In this paper, the microstructure and mechanical properties of Al-6.5Si-5.5Cu-0.2Zr-0.01Sr-0.06Ti-0.2Ce cast aluminum alloys were investigated in multistage solid solution systems. The microstructure of the alloy was characterized using an optical microscope (OM), scanning electron microscope (SEM), energy-dispersive spectrometer (EDS), x-ray diffraction (XRD) and transmission electron microscope (TEM), respectively. The hardness and conductivity of the alloy were measured using a Vickers hardness and eddy current conductivity testers, respectively, and the tensile properties were described by a drawing machine. The results showed that the mechanical properties of the alloy are the worst under the four-stage solid solution system (G1). With the increase in multistage solution temperature and holding time, θ phase (Al2Cu) was gradually dissolved into α-Al matrix to enhance the effect of dislocation strengthening. When the solution temperature reached 510 °C, the mechanical properties of the alloy were the best, and the tensile strength and elongation were increased to 354.90 MPa and 9.02%, respectively. With the increase in temperature, eutectic Si agglomeration and large area of insoluble phase between metals were found, resulting in the decrease in mechanical properties. [ABSTRACT FROM AUTHOR]

This study investigates the new surface development on AA6061 and AA5086 alloys considering the wire-arc additive manufacturing technique as a direct energy deposition (DED) process of wire. Two different quantities of MWCNTs, i.e., 0.01 (low) and 0.02 (high) g, with a constant nickel (Ni) weight (0.2 g) were pre-placed in the created square patterns. ER4043 filler was used as a wire for additive deposition, and an arc was generated through a tungsten inert gas (TIG) welding source. Furthermore, hardness and pin-on-disk wear-testing methods were employed to measure the changes at the surfaces with the abovementioned inducements. This work was designed to illustrate the hardness and the offered wear resistance in terms of mass loss of the AA6061 and AA5086 aluminum alloys with the function of nano-inducements. Two sliding distance values of 500 m and 600 m were selected for the wear analysis of mass loss from tracks. A maximum increase in hardness for AA6061 and AA5086 alloys was observed in the experiments, with average values of 70.76 HRB and 74.86 HRB, respectively, at a high mass content of MWCNTs. Moreover, the tribological performance of the modified surfaces improved with the addition of MWCNTs with Ni particles in a broader sense; the modified surfaces performed exceptionally well for AA5086 compared to AA6061 with 0.02 and 0.01 g additions, respectively. The system reported a maximum of 38.46% improvement in mass loss for the AA5086 alloy with 0.02 g of MWCNTs. Moreover, the morphological analysis of the developed wear tracks and the mechanism involved was carried out using scanning electron microscope (SEM) images. [ABSTRACT FROM AUTHOR]

Aluminum alloys are extensively used to manufacture mechanical components. However, when exposed to alkaline environments, like lubricants, refrigerants, or detergents, they can be corroded, reducing their durability. For this reason, the aim of this study is to investigate the influence of aggressive alkaline solutions (i.e., pH and presence of chlorides) on the corrosion resistance of three aluminum alloys (AA 5083-H111, AA 6082-T6, and AA 7075-T6) with and without anodizing treatments. Open circuit potential (EOCP) and anodic polarization measurements were carried out and typical corrosion parameters such as corrosion current density (icor) and corrosion rate (CR) were determined. Morphology of the corrosion attack and samples microstructure were investigated by scanning electron microscope. Results show that corrosion behavior of the three investigated alloys is influenced by (i) the aggressiveness of the testing environments; (ii) the thickness of the anodizing treatment; (iii) the alloy chemical composition; (iv) the distribution of intermetallic phases in the aluminum matrix. Moreover, three galvanic series have been built also testing other metallic alloys commonly used in mechanical applications, i.e., carbon steel (C40), stainless-steel (AISI 304), and Cu-based alloys (Cu-Ni alloy and CW 617 N, respectively). Results clearly indicate that galvanic series play a fundamental role when it is necessary to select an alloy for a specific environment, highlighting the thermodynamic conditions for corrosion occurrence. On the other hand, kinetic measurements and microstructural studies carried out on the three aluminum alloys stress the importance of the surface treatments and relevant thickness as well as the effect of metal exposure. Future work will involve the study of other surface treatments on aluminum alloys and the evaluation of their corrosion behavior in acidic environments. [ABSTRACT FROM AUTHOR]

This study was conducted with a high level of thoroughness. X-ray diffraction (XRD), Scanning Electron Microscope (SEM), and Transmission Electron Microscope (TEM) were used to analyze the phase composition and microstructure of the AM-2024Al and the RO-2024Al. The hardness and porosity of the AM-2024Al, as well as the bonding strength between AM-2024Al and RO-2024Al, were also investigated. Furthermore, the corrosion and tribocorrosion properties and failure mechanisms of the AM-2024Al and the RO-2024Al were systematically and thoroughly compared and analyzed. The results of this comprehensive study revealed that the AM-2024Al displayed a similar phase structure and higher hardness in comparison to the RO-2024Al, and the AM-2024Al was compact and tightly bound to the RO-2024Al with a bonding strength of over 55.5 MPa. Furthermore, the AM-2024Al exhibited better corrosion resistance under PDP (potentiodynamic polarization) corrosion and similar wet sliding wear resistance under an approximate pure friction process (OCP corrosion, namely open circuit potential corrosion) and tribocorrosion compared with the RO-2024Al. These findings provide a high level of confidence in the potential of cold spraying additive manufacture 2024Al as a reliable way to repair damaged RO-2024Al. [Display omitted] • The tribocorrosion is first reported for the CS additive manufacturing 2024Al alloy. • The AM-2024Al exhibits superior anti-corrosion compared to the RO-2024Al. • The AM-2024Al has a comparable tribocorrosion resistance to the RO-2024Al. • Splats (AM-2024Al) and grains (RO-2024Al) are partly peeled during the tribocorrosion. • A plastic deformation layer was generated in the wear track surfaces of the two 2024Al. [ABSTRACT FROM AUTHOR]

The microstructure, phase composition, precipitates evaluation, casting, and mechanical properties of the novel cast Al-4Cu-2.1Er-1Mg-0.2Zr-0.2Cr-0.15Fe-0.15Si-0.1Ti alloy were analyzed using by optical microscope, scanning and transmission electron microscopes, differential scanning calorimetry, thermodynamic calculations, hot cracking and mechanical properties measurements. The positive effect of Cr as a substitution of Mn on plasticity and precipitation strengthening was demonstrated. The 0.2Zr, 0.2Cr and 0.1 Ti as a grain refiners provide a fine grain size of 25 μm in the as-cast state due to primary Al 75–80 Cu 10–12 Er 3–4 Cr 7 phase particles formation as a nucleation centers of Al. The hot cracking index (HCI) of the AlCuErMgCr alloy was 12–14 mm which is similar with HCI of the cast Al-Si-Cu-Mg alloys. The good casting properties in the AlCuErMgCr alloy achieved due to a fine grain structure and narrow solidification range. The contribution of the Al 3 (Zr,Er) (40 nm), Al 45 Cr 7 (6 nm), and S'(θ') (100/5 nm) precipitates is 38.5 MPa, 140.4 MPa, and 198.9 MPa and the calculated contribution from dislocation and precipitates is 262.3 MPa. The ultimate tensile strength (UTS) and elongation (El.) of the AlCuErMgCr alloy are 372 MPa and 6% which is higher in 16.6% and 150%, respectively, than in the Mn-containing alloy. Novel alloy has an excellent combination of yield strength (YS) and plasticity at 20–250°C. The YS and El. are 301 MPa and 6% and 225–250 MPa and 4.6–11.5% at 20 and 200–250°C, respectively. The rupture strength at 250°C after 100 h (σ 100 250) is 106 MPa. Mechanical and casting properties of the novel alloy are superior to the properties of commercial 201.0 (Al-Cu-Mn-Mg-Ag-Ti) alloy. • Cr, replacing Mn, had a positive impact on both plasticity and precipitation strengthening. • 0.2Zr, 0.2Cr, and 0.1Ti as grain refiners resulted in the formation of primary Al 75–80 Cu 10–12 Er 3–4 Cr 7 phase particles. • The AlCuErMgCr alloy displayed an ultimate tensile strength (UTS) of 372 MPa and an elongation (El.) of 6%. • The rupture strength at 250°C after 100 hours was determined to be 106 MPa. [ABSTRACT FROM AUTHOR]