Lithium-doped anatase-TiO2 nanoparticles (LixTi1-xO2 NPs, x = 0, 0.05, 0.10, 0.15 and 0.20) could be synthesized by a simple sol–gel process. X-ray diffraction (XRD) results displayed the tetragonal (space group: I41/amd) of polycrystalline TiO2 anatase phase. The spectroscopy results of Raman and FT-IR confirmed the anatase phase of TiO2 through the specific modes of metal oxides vibration in the crystalline TiO2. Surfaces micrographs by scanning electron microscope (SEM) of agglomerated LixTi1-xO2 NPs showed a spongy like morphology. Transmission electron microscope (TEM) illustrated a cuboidal shape of dispersed NPs with particle size distributed in a narrow range 5–10 nm. Bruanauer Emmett-Teller (BET) results showed the increased surface area of LixTi1−xO2 NPs with increasing Li content. LixTi1-xO2 NPs (x = 0.05–0.20) working electrodes illustrated a pseudocapacitive behavior with excellent electrochemical properties through the whole cycles of GCD test. Interestingly, Li0.1Ti0.9O2 NPs electrode illustrated a high performance in terms of maximum specific capacitance 822 F g−1 at 1.5 A g−1 in 0.5 M Li2SO4 electrolyte, with excellent capacitive retention 92.6% after 5000 cycles GCD test. [ABSTRACT FROM AUTHOR]

Bismuth based metal oxides are regarded as potential candidates for fabricating photoelectrodes due to their cost-effectiveness, high stability, and significant light absorbing capability. Hence, our present study focuses on rendering an extensive evaluation of nano-sized bismuth tungstate (Bi2WO6) as photoanodes for photoelectrochemical water splitting activity. Bismuth tungstate nanoparticles have been prepared by a facile solvothermal route, and their structural, morphological, elemental composition, and optical properties have been characterized by employing powder X-ray diffraction analysis (PXRD), high-resolution scanning electron microscope (HRSEM), X-ray photoelectron spectroscopy (XPS), and UV-vis diffuse reflectance spectroscopy (UV-DRS) technique. For Bi2WO6 sample, the onset potential obtained for OER under dark and light conditions are ηdark = 0.83 V and ηlight = 0.71 V vs. Ag/AgCl respectively. The magnitude of photocurrent density at 1.23 V vs. RHE has been measured as 0.17 µA/cm2. From the Mott–Schottky plot, the flat band potential (Efb) for Bi2WO6 photocatalyst has been obtained as − 0.38 V vs. Ag/AgCl. Nanosized Bi2WO6 exhibited low onset potential, good photocatalytic stability, and suitable band edge potentials facilitating them to act as an efficient photoanode under stimulated solar light irradiation. [ABSTRACT FROM AUTHOR]