Search

The paper presents and discusses the results of a study of the thermal properties of cement composites with different contents of magnetite aggregate (0%, 20%, 40% and 60% by volume). The effect of grain size on the evaluated thermal properties was also investigated. For this purpose, concrete containing 50% by volume of magnetite aggregate with four different fractions (1–2 mm, 2–4 mm, 4–8 mm and 8–16 mm) was used. Thermal parameters were evaluated on specimens fully saturated with water and dried to a constant mass at 65 °C. The series with varying grain sizes of magnetite achieved thermal conductivity values in the range of 2.76–3.03 W/(m·K) and 2.00–2.21 W/(m·K) at full water saturation and after drying to a constant mass, respectively. In the case of the series with 20% magnetite by volume, the thermal conductivity was 2.65 W/(m·K) and 1.99 W/(m·K) for the material fully saturated with water and dried to a constant mass, respectively. The series with a 60% volume share of magnetite obtained values of this parameter of 3.47 W/(m·K) and 2.66 W/(m·K), respectively, under the same assumptions. [ABSTRACT FROM AUTHOR]

The manufacturing method influences the properties of the produced components. This work investigates the influence of manufacturing methods, such as fused deposition modeling (3D printing) and injection molding, on the water absorption and mechanical and thermal properties of the specimens produced from neat bio-based poly(lactic acid) (PLA) polymer and poly(lactic acid)/wood composites. Acrylonitrile butadiene styrene (ABS) acts as the reference material due to its low water absorption and good functional properties. The printing layer thickness is one of the factors that affects the properties of a 3D-printed specimen. The investigation includes two different layer thicknesses (0.2 mm and 0.3 mm) while maintaining uniform overall thickness of the specimens across two manufacturing methods. 3D-printed specimens absorb significantly higher amounts of water than the injection-molded specimens, and the increase in the layer thickness of the 3D-printed specimens contributes to further increased water absorption. However, the swelling due to water absorption in 3D-printed specimens decreases upon increased layer thickness. The tensile, flexural, and impact properties of all of the specimens decrease after water absorption, while the properties improve upon decreasing the layer thickness. Higher porosity upon increasing the layer thickness is the predominant factor. The results from dynamic mechanical analysis and microscopy validate the outcomes. The results from this experimental study highlight the limitations of additive manufacturing. [ABSTRACT FROM AUTHOR]

2,3-dihydro-5,6,7,8-tetranitro-1,4-benzodioxine (TNBD), molecular formula = C8H4N4O10, is a completely nitrated aromatic ring 1,4-benzodioxane derivative. The convenient method of TNBD synthesis was developed (yield = 81%). The detailed structure of this compound was investigated by X-ray crystallography. The results of the thermal analysis (TG) obtained with twice re-crystallized material revealed the onset at 240 °C (partial sublimation started) and melting at 286 °C. The investigated material degraded completely at 290–329 °C. The experimental density of 1.85 g/cm3 of TNBD was determined by X-ray crystallography. The spectral properties of TNBD (NMR, FT-IR and Raman) were explored. The detonation properties of TNBD calculated by the EXPLO 5 code were slightly superior in comparison to standard high-energy material—tetryl (detonation velocity of TNBD—7727 m/s; detonation pressure—278 kbar; and tetryl—7570 m/s and 226.4 kbar at 1.614 g/cm3, or 260 kbar at higher density at 1.71 g/cm3. The obtained preliminary results might suggest TNBD can be a potential thermostable high-energy and -density material (HEDM). [ABSTRACT FROM AUTHOR]

Advanced electronics technology is moving towards smaller footprints and higher computational power. In order to achieve this, advanced packaging techniques are currently being considered, including organic, glass, and semiconductor-based substrates that allow for 2.5D or 3D integration of chips and devices. Metal-core substrates are a new alternative with similar properties to those of semiconductor-based substrates but with the added benefits of higher flexibility and metal ductility. This work comprehensively compares the thermal properties of a novel metal-based substrate, molybdenum, and silicon and fused silica glass substrates in the context of system-on-foil (SoF) integration. A simple electronic technique is used to simulate the heat generated by a typical CPU and to measure the heat dissipation properties of the substrates. The results indicate that molybdenum and silicon are able to effectively dissipate a continuous power density of 2.3 W/mm2 as the surface temperature only increases by ~15 °C. In contrast, the surface temperature of fused silica glass substrates increases by >140 °C for the same applied power. These simple techniques and measurements were validated with infrared camera measurements as well as through finite element analysis via COMSOL simulation. The results validate the use of molybdenum as an advanced packaging substrate and can be used to characterize new substrates and approaches for advanced packaging. [ABSTRACT FROM AUTHOR]

This article describes the use of microwave irradiation in the synthesis of bis(cyclo carbonate) compounds (BCCs) in bulk (without solvent) from carbon dioxide capture using an epoxidized compound—a commercial epoxy resin—and compares this process to the conventional method. CO2 cycloaddition to epoxides is an ecological and efficient method for the formation of bis(cyclic carbonates). Moreover, the introduction of gas into the reaction mixture was carried out at atmospheric pressure with a controlled flow rate, which is advantageous from an economic point of view. Progressive structural changes and the presence of characteristic chemical groups were monitored using attenuated total reflectance infrared spectroscopy with Fourier transform. The obtained crude products were purified to obtain three fractions, which were subjected to detailed structural analysis using FT-IR and 13CNMR. The formation of the main product with two cyclic carbonates was confirmed. The presence of monomers, dimers and trimers in individual fractions as well as their thermal stability were determined, and the molecular masses in individual fractions were determined using gel permeation chromatography (GPC). [ABSTRACT FROM AUTHOR]

The structural and thermal characterization of milled wood lignin (MWL) prepared from bamboo (Phyllostachys pubescens) grown in Korea was investigated, and the results were compared with bamboo MWLs from other studies. The C9 formula of the bamboo MWL was C9H7.76O3.23N0.02 (OCH3)1.41. The Mw and Mn of MWL were 13,000 and 4400 Da, respectively, which resulted in a polydispersity index (PDI) of 3.0. The PDI of the prepared MWL was higher than other bamboo MWLs (1.3–2.2), suggesting a broader molecular weight distribution. The structural features of MWL were elucidated using FT-IR spectroscopy and NMR techniques (1H, 13C, HSQC, 31P NMR), which indicate that MWL is of the HGS-type lignin. The major lignin linkages (β-O-4, β-β, β-5) were not different from other bamboo MWLs. The syringyl/guaiacyl ratio, determined from 1H NMR, was calculated as 0.89. 31P NMR revealed variations in hydroxyl content, with a higher aliphatic hydroxyl content in MWL compared to other bamboo MWLs. Thermal properties were investigated through TGA, DSC, and pyrolysis-GC/MS spectrometry (Py-GC/MS). The DTGmax of MWL under inert conditions was 287 °C, and the Tg of MWL was 159 °C. Py-GC/MS at 675 °C revealed a syringyl, guaiacyl, p-hydroxyphenyl composition of 17:37:47. [ABSTRACT FROM AUTHOR]