Search

While good ohmic contact formation has been achieved on both p-GaN and n-AlGaN surfaces, the turn-on and operating voltages of AlGaN-based deep-ultraviolet light-emitting diodes (DUV-LEDs) remain very high. We find that this critical problem is mainly caused by the large difference between the annealing temperatures required for ohmic contact formation on the p-GaN and high Al-fraction n-AlGaN surfaces. We studied the effects of the high-temperature annealing treatments required for n-ohmic contact formation on the subsequent p-ohmic contact formation process in DUV-LEDs. The results show that post-annealing treatment at high temperature is necessary to form an ohmic contact on n-Al0.7Ga0.3N, but a treatment temperature of 900°C or more could cause severe degradation of the specific contact resistivity and the bulk resistivity of p-GaN. We conclude that 900°C is the optimum temperature to form an ohmic contact on n-Al0.7Ga0.3N in DUV-LEDs, where p-GaN and n-Al0.7Ga0.3N act as the p- and n-ohmic contact layers, respectively. We also found that the specific contact resistivity of p-GaN can be reduced by an additional low-temperature annealing treatment after the high-temperature annealing step; this effect can be attributed to the enhancement of the hole concentration in the p-GaN surface contact region. Finally, DUV-LEDs that emit at 280 nm were fabricated using four different annealing treatments during processing. A considerable reduction in the series resistance and thereby in the operating voltage was confirmed using the annealing process proposed above, consisting of a high-temperature anneal at 900°C followed by a low-temperature anneal at 500°C for 3 min.

We thoroughly explored the physical origin of the efficiency decrease with increasing injection current and current crowding effect in 280 nm AlGaN-based flip-chip deep-ultraviolet (DUV) light-emitting diodes (LEDs). The current spreading length was experimentally determined to be much smaller in DUV LEDs than that in conventional InGaN-based visible LEDs. The severe self-heating caused by the low power conversion efficiency of DUV LEDs should be mainly responsible for the considerable decrease of efficiency when current crowding is present. The wall-plug efficiency of the DUV LEDs was markedly enhanced by using a well-designed p-electrode pattern to improve the current distribution.

We propose a method to determine the current injection efficiency (CIE) and internal quantum efficiency (IQE) of light-emitting diodes (LEDs) during current injection. The method is based on fourth-order polynomial fitting of a modified rate equation to electroluminescence data. Our method can extract the CIE at low injection current densities, unlike conventional methods that generally assume the CIE to be unity. We apply the method to AlGaN-based deep-ultraviolet LEDs. Results show that the CIE was only approximately 51% at low injection current densities and was almost independent of injection current density up to 100 A/cm2. The peak IQE was 77%.

High-power 265 nm deep-ultraviolet (DUV) AlGaN-based light-emitting diodes (LEDs) with large-area AlN nanophotonic light-extraction structures that were fabricated by a nanoimprint lithography process are presented. Each DUV-LED has a large active area (mesa size of ∼0.35 mm2) and a uniform current spreading design that allows high injection current operation. We have shown that these DUV-LEDs with their large-area nanoimprinted AlN nanophotonic structures exhibit wider near-field emitting areas, stronger far-field extracted light intensities, and an approximately 20-fold increase in output power when compared with a conventional flat-surface DUV-LED. A large-area nanoimprinted single-chip DUV-LED operating in the UV-C wavelength regime has demonstrated a record continuous-wave output power in excess of 150 mW for an injection current of 850 mA at a peak emission wavelength of 265 nm.

The current crowding is an especially severe issue in AlGaN-based deep-ultraviolet (DUV) light-emitting diodes (LEDs) because of the low conductivity of the n-AlGaN cladding layer that has a high Al fraction. We theoretically investigated the improvement in internal quantum efficiency and total resistances in DUV-LEDs with an emission wavelength of 265 nm by a well-designed p-electrode geometry to produce uniform current spreading. As a result, the wall-plug efficiency was enhanced by a factor of 60% at an injection current of 350 mA in the designed uniform-current-spreading p-electrode LED when compared with an LED with a conventional cross-bar p-electrode pattern.

Entrainment by a pacemaker was investigated experimentally and numerically in a chain of chemical oscillators using coupled discrete Belousov-Zhabotinsky reaction oscillators. The spontaneous frequency of each oscillator depended on the concentration of catalyst ions. The coupling strengths among the nearest neighbor oscillators were controlled by changing the spacing distance (d) between beads. When the coupling strength was sufficiently strong, the pacemaker entrained other oscillators in the chain. Subsequently, the trigger waves propagating from a pacemaker were observed. The range of trigger wave propagation area, i.e., the number of entrained oscillators, depended on d. Numerical simulation for the system described the experimental results well. Furthermore, photic noise maximized the strength of entrainment at an optimal noise intensity.