Search

This study investigates the effects of different lubrication conditions on drawing force and microcup formation during micro deep drawing (MDD). Results show that graphene lubricant, in combination with TiO2 nanolubricants, has the potential to reduce friction during MDD. The peak drawing force was reduced by 15.39% when both lubricants were used together, while the use of TiO2 nanolubricant and 10.0 mg/ml graphene lubricant reduced it by 6.03% and 14.52%, respectively. The study also reveals that lubricants reduce wrinkling during the formation of microcups by minimising energy consumption during the primary formation. However, the combination of TiO2 nanolubricant and graphene lubricant can cause inhomogeneous formation on the upper part of the blank, leading to more apparent wrinkling. Overall, the study highlights the potential of TiO2 nanolubricant and graphene lubricant in reducing friction and improving microcup formation during MDD. [ABSTRACT FROM AUTHOR]

In recent years, the quest for effective lubrication in micro deep drawing (MDD) has seen promising advancements. In this study, the influence of TiO2 nanolubricants and graphene lubricants on the performance of 301 stainless steel foil in MDD is examined. The MDD undergoes an extensive evaluation of various lubrication conditions, including dry, TiO2 nanolubricant, graphene lubricant at concentrations of 2.5 mg/mL, 5.0 mg/mL, and 10.0 mg/mL, as well as combined applications of TiO2 and graphene lubricants. Utilising a 5.0 mg/mL graphene lubricant together with TiO2 nanolubricants led to a significant reduction in drawing force, highlighting the synergistic efficacy of this combined lubricant. A pronounced enhancement in the consistency of the produced microcups was also attained. These results emphasise the promise of TiO2 nanolubricant and graphene lubricants in optimising the MDD process. [ABSTRACT FROM AUTHOR]

At present, Al matrix composites (AMCs) have drawn much attention owing to their light weight, high specific strength, high thermal conductivity, and superior excellent wear resistance, which endows them with great potential in the aerospace, automobile and military industries. In this study, AMCs with different Ti contents (0, 5 and 10 vol.%) were prepared by powder metallurgy. During the sintering, Al3Ti particles were in situ formed in the Al matrix. It was found that the Ti completely reacted with the Al matrix and formed fine in situ Al3Ti particles in Al-10Ti, while some large Ti-Al3Ti core-shell formed in Al-5Ti due to the incomplete reaction between the Ti and the Al matrix. Furthermore, the hardness of the composites was significantly improved by the in situ formed Al3Ti particles, reaching 143.3 HV in Al-5Ti and the highest value at 331.2 HV in Al-10Ti, respectively. The wear resistance of the composites is remarkably enhanced by Al3Ti particles compared to the unreinforced Al. Al-5Ti has the highest wear resistance among the samples. The wear resistance of the Al-10Ti composite becomes slightly deteriorated compared to Al-5Ti due to the brittle nature of Al3Ti, which leads to a three-body abrasive wear. [ABSTRACT FROM AUTHOR]

To improve the quality of products produced from microforming, various nanolubricants have been applied in the field of micromanufacturing in recent years. In this paper, the effects of glycerol-based lubricant containing TiO2 NPs (NPs) on micro deep drawing (MDD) of austenitic stainless steel (ASS) SUS301 were studied, and the lubrication mechanism involved was discussed. The MDD experiments were conducted with the SUS301 foils under dry, 1, 2, and 4 wt% TiO2 NP lubrication conditions. The results show that the use of the TiO2 nanolubricants can significantly improve the quality of the drawn cups in terms of decreased wrinkling and surface roughness. Besides, the concentration of TiO2 NPs influences lubricity by reducing friction during the MDD process. The peak drawing force is the lowest when 2 wt% nanolubricant is applied, which drops to 72.54 N from 77.38 N under dry conditions. The micro cup drawn under 2 wt% TiO2 nanolubricant has the best quality among those obtained under all the lubrication conditions. The lubrication mechanisms are derived from the mending effects of TiO2 NPs and the formation of thin lubricant films associated with the open lubricant pockets (OLPs) and close lubricant pocket (CLPs) theory in the MDD. The CLPs function as reservoirs that retain lubricants to counteract the load pressure, whereas the OLPs lead to lubricant leakage due to the higher flow resistance. It was found that the lubricant film and NPs are insufficient at a low concentration (1 wt%), while the lubrication performance can be enhanced with increased NP concentration. However, there exist apparent agglomerations on the surface of the produced micro cup when using 4 wt% nanolubricant, which greatly deteriorates the lubricant performance in the MDD process. It is concluded that the lubricant containing 2 wt% TiO2 NPs demonstrates the best lubrication performance during the MDD of ASS SUS301. [ABSTRACT FROM AUTHOR]

Micro deep drawing (MDD) is a fundamental process in microforming which has wide applications in micro electromechanical system (MEMS) and biological engineering. Titanium possesses excellent mechanical properties and biocompatibility, which makes it a preferred material in micromanufacturing. In this study, eco-friendly and low-cost water-based TiO2 nanolubricants were developed and applied in the MDD with 40 μm-thick pure titanium foils. The lubricants consisting of TiO2 nanoparticles (NPs), 10 wt% glycerol, 0.1 wt% sodium dodecyl-benzene sulfonate (SDBS) and balanced water were synthesised in a facile process. The MDD with 40 μm-thick pure titanium was carried out using the lubricants with varying concentrations of 0.5, 1.0 and 2.0 wt%. The results show that the formability of micro cups could be significantly improved when the nanolubricants are applied. Especially, the use of 1.0 wt% TiO2 nanolubricant demonstrates the best lubrication performance by significantly reducing the final drawing forces, and surface roughness, and the wrinkles by up to 24.2%, 12.55% and 4.82%, respectively. The lubrication mechanisms including the ball bearing and mending effects of NPs on open lubricant pockets (OLPs) and close lubricant pockets (CLPs) areas were then revealed through microstructure observation. [ABSTRACT FROM AUTHOR]

The microstructure of Cr–Mn–Ni–N stainless steel is regulated by a combination of cold deformation and subsequent martensite reversed annealing. The yield strength and tensile strength of the tested steel are greatly improved to 1220 and 1357 MPa, respectively, by conventional heavy cold rolling (66% thickness reduction) and a subsequent annealing process (750 °C for 5 min) relative to those before cold rolling (austenized state); at the same time, the total elongation keeps an appropriate value. The results show that the grain refinement strengthening acts as the primary factor for the strengthening of the tested steels while the precipitation behavior from the M23C6‐type carbides is not quite effective. Additionally, different yield phenomena and microstructural evolution for tested steels with 66% thickness reduction annealed at 750 °C with different holding times are systematically analyzed and discussed. Lüders‐like deformation features noticeably appear but become weakening with the longer annealing time. The change in initial free mobile dislocation density is the core cause of the preyield plateau phenomenon. [ABSTRACT FROM AUTHOR]