Search

As a piece of high-intensity running equipment, the wear of an internal mixer determines the quality of rubber and its life. In general, the wear of an internal mixer is caused by the friction between the rubber and metal during the mixing process, and the most severe wear position is the end face of the equipment. In this paper, a mixture of multi-walled carbon nanotubes (MWCNTs) and carbon fibers (CFs) are added to rubber by mechanical compounding to obtain MWCNT/CF/carbon black (CB) composites. By investigating the synergistic mechanism of MWCNTs and CFs, we analyze the effect of the MWCNT/CF ratio on the frictional wear of metal on the end face of the internal mixer. At the microscopic level, MWCNTs and CFs form a spatial meshwork with CB particles through synergistic interactions. The CB particles can be adsorbed on the spatial meshwork to promote the dispersion of CB particles. In addition, the formation of oil film can be slowed down due to the spatial meshwork, which could hinder the spillage of aromatic oil. Meanwhile, the spatial meshwork serves as a physical isolation layer between the rubber and metal to reduce friction. Therefore, it dramatically impacts the dispersion degree of CB particles, the friction coefficient, the roughness of the surface, and the wear of metal. It shows that the synergistic effect of MWCNT/CF and CB particles is best when the CF content of the rubber matrix is 5 phr, showing the most stable spatial network structure, the best dispersion of CB particles, and minor wear on the end face of the internal mixer. [ABSTRACT FROM AUTHOR]

Studies show that the long-term operation of a rubber mixer results in wear at the end face of the mixer. End face wear increases the gap between the mixing chamber and the end face, resulting in leakage and a reduction in the mixing performance, affecting the final product's quality. Therefore, it is essential to investigate the wear of the metal face during the mixing process. The present study added aramid fibers to a rubber compound using a mechanical blender to obtain a composite material. Then, the influence of the aramid fibers on the metal friction and wear of the end face of the mixer was analyzed. This article introduces the concept of the wear ratio and explores the friction and wear of metals from the perspective of formulation technology for the first time. With the addition of aramid fibers, the proportion of abrasive wear of rubber on metal decreased, and the proportion of corrosive wear increased during the mixing process; however, when the addition of aramid fibers exceeded 3 phr, the balance of abrasive wear of rubber on metal increased and the proportion of corrosive wear decreased. It was found that aramid fibers have the property of friction reduction, which reduces the wear of the rubber blend on the metal. When the amount of aramid fibers added was 3 phr, the amount of abrasion of the rubber compound on the metal was the lowest. [ABSTRACT FROM AUTHOR]

The continuous operation of essential refining equipment, internal mixers, leads to wear on their end faces, resulting in an increased gap between the mixer chamber and the end face. This, in turn, causes material leakage, reducing mixing efficiency and adversely impacting rubber performance. Therefore, investigating metal wear on the mixer's end face during the mixing process is essential. Scholars have introduced dynamic covalent bonds into rubber molecular chains, bestowing self-repairing capabilities upon the materials. This innovation has significant implications for extending rubber lifespan and lowering production costs. It involves adding methacrylic acid (MAA) and excess zinc oxide (ZnO) to construct an ionic crosslinking network, limiting covalent crosslinking of rubber molecules and enabling in-situ polymerization of MAA/ZnO, resulting in self-repairing properties. However, it is crucial to consider corrosive wear induced by MAA's strong acidity on metals. This study combines MAA, ZnO, and multi-walled carbon nanotubes (MWCNTs) through mechanical mixing to create a composite material called zinc methacrylate (ZDMA)/MWCNTs/rubber. The research investigates the in-situ synthesis mechanism of MAA and ZnO and the synergistic mechanism of ZDMA and MWCNTs. The study analyzes the impact of MWCNTs additive amount on the frictional wear of the internal mixer's metal end face. During the mixing process, ZDMA is grafted and polymerized onto rubber's macromolecular chains, forming ionic pairs with strong electrostatic interactions, creating a primarily reversible supramolecular network dominated by ion crosslinking. This ion crosslinking network, along with the three-dimensional mesh structure of MWCNTs, establishes a stable spatial structure within the rubber matrix. The study reveals that increasing the MWCNTs content to 3 phr reduces the aggregation of SiO 2 particles and ZDMA granules within the rubber matrix, resulting in reduced friction coefficients, roughness, and wear rates of the metal. However, exceeding 3 phr of MAA content leads to excessive MWCNT aggregation within the rubber matrix, increasing wear rates, roughness, and friction coefficients due to hindrance of rubber macromolecular chain crosslinking and reduced SiO 2 particle dispersion within the rubber matrix. These findings provide valuable insights into the dynamics of frictional wear in internal mixers. • Continuous mixer use erodes end faces, widens gaps, and hampers rubber performance. • Adding dynamic covalent bonds to rubber enhances self-repair, extending lifespan and cutting production costs. • MAA, ZnO, and MWCNTs create ZDMA/MWCNTs/rubber, studied for frictional wear impact. • Elevated MWCNTs levels (up to 3 phr) lower wear rates, roughness, and friction in rubber. • Excessive MAA (> 3 phr) increases wear, roughness, and friction by blocking crosslinking and reducing dispersion. [ABSTRACT FROM AUTHOR]

Prolonged operations of mixers cause wear of mixer rotors and chamber walls and affect the clearances between the rotors and chamber walls, which reduce the mixing effect, weaken the dispersion of the packing, and affect the quality of rubber products. In this study, the effects of traditional mixing and wet mixing on the friction and wear of the chamber, and the properties of rubber were compared by using 60 phr of a silica natural rubber formulation system. The results show that a silanization reaction occurs between silica and the silane coupling agent during the mixing process and that the reaction rate is fastest when the temperature of the mixing chamber is maintained between 145 and 155°C for 1 min during the mixing process. The products of silanization reaction are ethanol and water; the water vapor that forms at high temperatures corrodes the mixing chamber of the internal mixer and aggravates wear and tear. Due to the high dispersion of silica during wet mixing, the silanization reaction is more complete and water vapor is produced at a high temperature. Hence, the rubber compound obtained by wet mixing has more significant wear on the mixing chamber. [ABSTRACT FROM AUTHOR]

During prolonged operation, the end face of the internal mixer, a crucial component in rubber processing, experiences wear, resulting in an increased gap between the mixing chamber and the end face. This gap can lead to material leakage and reduced mixing efficiency, negatively impacting rubber properties. To address this issue, researchers have introduced dynamic covalent bonds into the molecular rubber chains, giving the material self-healing properties. This advancement is essential for extending rubber lifespan and reducing production costs. One common approach involves adding methacrylic acid (MAA) and excess zinc oxide (ZnO) to create ionic crosslinking networks, limiting covalent crosslinking and enabling in-situ polymerization of MAA/ZnO, resulting in self-healing capabilities. However, the strong acidity and corrosive nature of MAA can cause metal wear. In our study, we mechanically blend MAA with ZnO to produce zinc methacrylate (ZDMA)/rubber composites. We investigate the in-situ synthesis mechanism of MAA and ZnO and assess the impact of MAA on the friction and wear of the internal mixer's end face. Our findings reveal that ZDMA ion pairs form an "ion cross-linked network" within the rubber chain, hindering SiO 2 particle dispersion and increasing aggregation within the rubber matrix. This compromises dispersion and leads to abrasive wear from SiO 2 particles, corrosive wear from high-temperature water vapor, and corrosive wear from MAA. Additionally, excessive ZDMA self-polymerization alters SiO 2 particle agglomerates. The strong acidity of MAA and the "ion cross-linked network" within the rubber matrix significantly affect SiO 2 particle dispersion, friction coefficients, metal surface roughness, and metal wear. Our comprehensive analysis, including SEM, dispersion, RPA, metal surface morphology, and CSM friction wear tests, identifies the optimal cross-linking effect with the addition of 15 phr of MAA, resulting in a well-defined "ion cross-linked network" within the rubber matrix, enhancing rubber performance. However, SiO 2 particle dispersion is compromised, leading to increased agglomeration and heightened metal wear. • Prolonged operation of internal mixers causes wear, increasing the gap, impacting rubber quality. • Self-healing rubber with dynamic covalent bonds extends lifespan and reduces costs. • A method involving MAA and ZnO for self-healing, but MAA's acidity causes metal wear. • Blending MAA and ZnO into ZDMA/rubber composites affects dispersion and wear. • An optimal MAA amount enhances rubber performance but compromises SiO 2 dispersion and increases metal wear. [ABSTRACT FROM AUTHOR]

As the essential mixing equipment, long hours of work can cause wear and tear on the end face of the compactor. The wear of the end faces leads to an increase in the gap between the chamber and the end faces, which leads to leakage, reduces the mixing effect, and ultimately affects the rubber properties. Therefore, it is necessary to study the end face metal wear during the mixing process. Thermally cracked carbon black, as recycled material for scrap rubber, can be used as a substitute for other carbon blacks in some fields, vastly reducing the production cost and promoting the reuse of scrap rubber. In this paper, thermally cracked carbon black (CBp) was mixed with multi-walled carbon nanotubes (MWCNTs) and added rubber by mechanical blending to obtain CBp/MWCNTs composites. The synergistic mechanism of CBp and MWCNTs was investigated to analyze the effect of CBp/MWCNTs ratios on the frictional wear of metal on the end face of the compactor. The results showed that MWCNTs cooperated with CBp particles to form a three-dimensional "grape bunch" network structure. On the one hand, the three-dimensional "grape bunch" network structure can adsorb CBp particles to promote the dispersion of CBp particles. On the other hand, the three-dimensional "grape bunch" network structure can also hinder the overflow of aromatic oil and affect oil film formation. At the same time, the three-dimensional "grape bunch" network structure can also form a physical isolation layer between the rubber and the metal. This significantly influences the degree of CBp particle dispersion, friction coefficient, metal surface roughness, and metal wear. It seems that the synergistic effect between MWCNTs and CBp particles is maximized when the content of MWCNTs in CBp/MWCNTs composites is 4 phr, the area of CBp/MWCNTs three-dimensional mesh is maximized, the dispersion of CBp particles is the best, and the wear of CBp/MWCNTs composites on metal is the lowest. • As the essential mixing equipment, long hours of work can cause wear and tear on the end face of the compactor. • The effect of the synergistic effect of CBp and MWCNTs on the friction and wear of end-face metal was analyzed. • The results showed that MWCNTs cooperated with CBp particles to form a three-dimensional "grape bunch" network structure. [ABSTRACT FROM AUTHOR]