The structures and functional properties of Na0.5Bi0.5TiO3- xKNbO3 (NBT-xKN) solid solutions, with x in the range from 0.01 to 0.09, were investigated using a combination of high-resolution synchrotron X-ray powder diffraction (SXPD) and ferroelectric property measurements. For low KN contents, an irreversible transformation from cubic to rhombohedral phases was observed after the application of a high electric field, indicating that the polar nanoregions (PNRs) in the unpoled state can be transformed into metastable long-range ordered ferroelectric domains in the poled state. In contrast, the near-cubic phase of the unpoled ceramics was found to be remarkably stable and was retained on cooling to a temperature of −175°C. Upon heating, the field-induced metastable ferroelectric rhombohedral phase transformed back to the nanopolar cubic state at the structural transformation temperature, TST, which was determined as approximately 225°C and 125°C for KN contents of 3% and 5% respectively. For the field-induced rhombohedral phase in the poled specimens, the pseudo-cubic lattice parameter, ap, exhibited an anomalous reduction while the inter-axial angle increased towards a value of 90° on heating, resulting in an overall increase in volume. The observed structural changes were correlated with the results of temperature-dependent dielectric, ferroelectric and depolarization measurements, enabling the construction of a phase diagram to define the stable regions of the different ferroelectric phases as a function of composition and temperature. [ABSTRACT FROM AUTHOR]

(1 − x)Na 0.5 Bi 0.5 TiO 3 -xKNbO 3 (NBT-xKN) ceramics, with x in the range 0.01–0.09, were prepared by solid state reaction and conventional sintering. A progressive transformation from a nano-polar to a long-range ordered ferroelectric phase was observed after the application of a cyclic electric field with an amplitude of 5 kV mm −1 . It is shown by analysis of the crushed ceramic pellets, using high resolution synchrotron x-ray diffraction, that the application the cyclic electric field induced an irreversible transformation from a pseudo-cubic nano-polar phase to a rhombohedral ordered ferroelectric phase having R3c symmetry. Furthermore, a systematic variation, from 89.6° to 90°, was observed in the rhombohedral interaxial angle as the KN content increased from 1 to 9%. By comparing the structural evidence with the ferroelectric polarization-electric field hysteresis loops, it is shown that the electric field-induced transformation is partially reversible for NBT-5KN and completely reversible or nonexistent for NBT-9KN. [ABSTRACT FROM AUTHOR]