Search

Oil-in-water (O/W) emulsion is widely applied as a lubricant during hot rolling process. For reducing environmental impact caused by O/W emulsion, a novel nano-TiO 2 additive O/W lubricant with improved stability and reduced coefficient of friction (COF) is developed. Little research, however, has been focused on the growth behaviour of oxide scale formed on the workpiece surface and its effects on the tribological property of nano-TiO 2 additive O/W lubricant. In the current work, oxidation tests of high strength steel were conducted to investigate the growth behaviour of oxide scale and obtain different surface morphologies of the oxide scale. Ball-on-disk tribological tests under a temperature of 80 °C were carried out to investigate the effects of surface morphology of oxide scale on the tribological behaviour under nano-TiO 2 additive O/W lubrication. The performance of the new developed lubricant was evaluated by hot rolling process. The growth mechanism of oxide scale and the modified oxide scale growth model were proposed. Tribological results indicate that oxide scale plays an important role in the tribological behaviour of nano-TiO 2 additive O/W lubricant. A reduction in surface roughness can result in a decrease of COF, while the COF will increase if the surface roughness reduces too much because some of the nano-TiO 2 particles cannot go through the contact area to play a positive role in lubrication. [ABSTRACT FROM AUTHOR]

Electron backscatter diffraction (EBSD) of the microtexture in the tertiary oxide scale after hot rolling were investigated. The surface asperity flattening and grain refinement of Fe 3 O 4 were produced at a thickness reduction of 28% and a cooling rate of 28 °C/s. Microtexture development of Fe 3 O 4 manifests as a strong θ fibre parallel to oxide growth, including the {100}<001> and {001}<110> textured components, whereas the {0001}<10 1 ̅ 0> component dominates in α -Fe 2 O 3 as the favoured basal slip. The tribological effect of α -Fe 2 O 3 at the contact surface of steel and rolls was considered at low and high thickness reductions. The propagation of cracks along the Fe 3 O 4 grain boundaries could create a dish to collect nanoparticles during lubrication and thereby changed the wear rates. [ABSTRACT FROM AUTHOR]

The characters of grain boundaries in oxide layers formed on substrates influence adhesion and friction behaviour, surface fracture and wear during high temperature steel processing. In this work, an electron backscattered diffraction (EBSD) analysis was conducted to investigate the role of surface grain boundary and orientation in magnetite (Fe 3 O 4 )/haematite (α-Fe 2 O 3 ) scale during hot rolling, and further evaluate their effects on tribological properties of water-based nanoparticles lubrication. The results demonstrate that Fe 3 O 4 (100) plane is strongly sensitive to the surface characteristics as the minimisation of surface energy. Coincident site lattice (CSL) boundaries in microstructure is in presence of Σ3 in the Fe 3 O 4 and Σ13b in the Fe 2 O 3 of the substrates subjected to a thickness reduction of 28% and cooling rate of 28 °C/s. This is due in great part to the changes in crystal slip systems. These low-Σ CSL boundaries in oxide scale offer obstacles to the propagation of cracks, where some of nanoparticles collected would be trapped at the interface and thereby may cause high wear rates. A lubrication mechanism is proposed to explain the grain boundary effect on nanoparticles lubrication, and further to determine the dependence of frictional behaviour on surface energy, crystallographic preferred orientation (microtexture) and crystal structure. These results provide an intriguing new insight into the application of water-based lubricant with graphite nanoparticles. [ABSTRACT FROM AUTHOR]