Search

The scintillation characteristics of Lu0.8Gd2.2 (Al5–xGax)O12:Ce,Mg (x = 2.6 and 3) single crystals grown by the micropulling down method are investigated. The light yield of 27600 photons/MeV obtained for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg is higher than that of 25 400 photons/MeV obtained for Lu0.8Gd2.2Al2.4Ga2.6O12:Ce,Mg. The photoluminescence and scintillation decays measured at room temperature (RT) for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg are faster than those for Lu0.8Gd2.2Al2.4Ga2.6O12:Ce,Mg. Temperature dependence of radioluminescence (RL) intensity indicates a lower quenching temperature for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg. Coincidence time resolution of a Lu0.8Gd2.2Al2Ga3O12:Ce,Mg detector in coincidence experiment with a BaF2 detector was measured to be 410 ps. The afterglow and thermally stimulated luminescence (TSL) characteristics below RT are also measured. [ABSTRACT FROM AUTHOR]

The scintillation characteristics of Gd 3 Al 2 Ga 3 O 12 :Ce, Li (GAGG:Ce,Li) and Gd 3 Al 2 Ga 3 O 12 :Ce, Mg (GAGG:Ce,Mg) single crystals were compared. Radioluminescence spectra and photoluminescence decay curves were measured at various temperatures between 77 and 500 K to investigate the thermal luminescence quenching. At 662 keV γ rays, the LY value of 35,400 photons/MeV and energy resolution of 6.9% obtained for GAGG:Ce, Li are superior to those of 24,200 photons/MeV and 9.5% for GAGG:Ce,Mg. Scintillation decays are approximated by a double exponentials with a fast principal decay component of 47 ns (83%) for GAGG:Ce, Mg and 90 ns (86%) for GAGG:Ce,Li. Coincidence time resolution of 282 ps obtained for GAGG:Ce, Mg is better than that of 389 ps for GAGG:Ce,Li. GAGG:Ce, Mg shows a much lower afterglow and thermally stimulated luminescence intensity with respect to GAGG:Ce,Li. • Scintillation properties of Li+ and Mg2+ -codoped Gd 3 Al 2 Ga 3 O 12 :Ce are compared. • Gd 3 Al 2 Ga 3 O 12 :Ce, Mg exhibits better timing performance. • Gd 3 Al 2 Ga 3 O 12 :Ce, Mg shows lower afterglow and TSL intensity. • Gd 3 Al 2 Ga 3 O 12 :Ce, Li exhibits high light yield and good energy resolution. [ABSTRACT FROM AUTHOR]

Mg2+-codoped Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce (YGAGG:Ce,Mg) single crystal was grown by the Czochralski method and its luminescence and scintillation properties were investigated. Temperature dependence of radioluminescence (RL) yield and photoluminescence (PL) decay time was measured, and activation energy of thermal ionization process was determined from temperature-dependent PL decay time measurement. YGAGG:Ce,Mg exhibited high X-ray excited RL yield almost 5 times higher than BGO reference scintillator. Its light yield of 41,500 ph/MeV and scintillation decay times of 12 ns (2%) + 52 ns (65%) + 207 ns (33%) were measured under excitation with 662 keV γ rays from 137Cs source. Afterglow and thermally stimulated luminescence characteristics are also investigated. • Luminescence and scintillation properties of Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg crystal are investigated. • Temperature dependence of photo-and radioluminescence are presented. • Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg shows high light yield of 41,500 photons/MeV. • Luminescence quenching above RT can be caused by thermal ionization. • Afterglow and thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]