Search

Abstract: An existing procedure based on the combined use of the Virtual Crack Closure Technique and of a fail release approach for the analysis of delamination growth phenomena in composite structures has been enhanced with a front-tracing algorithm and suitable expressions for the evaluation of the Strain Energy Release Rate when dealing with non-smoothed delamination fronts. The enhanced procedure has been implemented into a commercial finite element software by means of user subroutines and applied to the analysis of a composite stiffened panel with an embedded delamination under compressive load. The effectiveness and robustness of the enhanced procedure have been assessed by comparing literature experimental data and numerical results obtained by using different mesh densities in the damaged area (global/local approach). [Copyright &y& Elsevier]

Abstract: The compression after impact (CAI) strength of fully orthotropic composite laminates with up to 21 plies is presented, as analysed by an existing strip model. Candidate layups, which can be symmetric, anti-symmetric or non-symmetric, are preselected to exhibit no elastic coupling response, with manufacturing rules applied. These criteria, along with the use of a simple surrogate sublaminate buckling model, were chosen to allow analysis of all feasible laminates in the design space without excessive computation time. Results indicate that although the inclusion of non-symmetric layups in the design space does not give benefits with respect to maximum achievable damage tolerance, these laminates can exhibit damage tolerance close to that of an anti-symmetric design for some ply counts, and better than symmetric solutions in most cases. It is also noted that in some instances increasing the number of plies in a laminate can actually reduce the highest achievable threshold load for damage tolerance, as a result of the large influence Poisson’s ratio has on sublaminate buckling. Average errors in the surrogate model were low in all cases, with maximum non-conservative errors less than 1%. The surrogate buckling model reduced computational time by over 99% when compared to the fully exhaustive search. [Copyright &y& Elsevier]

Abstract: In this paper, the damage failure and behaviour of stitched composites under compression after impact (CAI) loading are experimentally investigated. This study focuses on the effect of stitch density and stitch thread thickness on the CAI strength and response of laminated composites reinforced by through-thickness stitching. Experimental findings show that stitched composites have higher CAI failure load and displacement, which corresponds to higher energy absorption during CAI damage, mainly attributed to greater energy consumption by stitch fibre rupture. The coupling relationships between CAI strength, impact energy, stitch density and stitch thread thickness are also revealed. It is understood that the effectiveness of stitching has high dependency on the applied impact energy. At low impact energy range, CAI strength is found to be solely dependent on stitch density, showing no influence of stitch thread thickness. It is however observed that stitch fibre bridging is rendered ineffective in moderately stitched laminates during compressive failure, as local buckling occurs between stitch threads, resulting in unstitched and moderately stitched laminates have similar CAI strength. The CAI strength of densely stitched laminates is much higher due to effective stitch fibre bridging and numerous stitch thread breakages. At high impact energy level, CAI strength is discovered to be intimately related to both stitch density and stitch thread thickness. Since CAI failure initiates from impact-induced delamination area, stitch fibre bridging is considerable for all specimens due to the relatively large delamination area present. Stitch threads effectively bridge the delaminated area, inhibit local buckling and suppress delamination propagation, thus leading to increased CAI strength for laminates stitched with higher stitch density and larger stitch thread thickness. Fracture mechanisms and crack bridging phenomenon, elucidated by X-ray radiography are also presented and discussed. This study reveals novel understanding on the effectiveness of stitch parameters for improving impact tolerance of stitched composites. [Copyright &y& Elsevier]

Abstract: This paper addresses the effect of a local quasi-static indentation or a low-velocity impact on the residual strength of foam core sandwich panels subjected to edgewise compression. The damage is characterized by a local zone of crushed core accompanied by a residual dent in the face sheet. Experimental studies show that such damage can significantly alter the compressive strength. Theoretical analysis of the face sheet local bending is performed for two typical damage modes (with or without a face–core debonding). The solutions allow estimation of the onset of (a) an unstable dent growth (local buckling) or (b) a compressive failure in the face sheet. The theoretical results are in agreement with the test data for two considered sandwich configurations. [Copyright &y& Elsevier]

Abstract: A fuselage representative carbon fibre-reinforced multi-stiffener panel is analysed under compressive loading. An intact and pre-damaged configuration is loaded into the postbuckling region and further on until collapse occurs. An analysis tool is applied that includes an approach for predicting interlaminar damage initiation and degradation models for capturing interlaminar damage growth as well as in-plane damage mechanisms. Analysis of the intact panel configuration predicts collapse due to fibre fracture in the stiffeners close to the panel clamps, which agrees well with the results from experimental testing. The pre-damaged configuration was proposed containing Teflon-coated layers to generate the initial debonds in the skin-stiffener interface. The outcome of the simulation of this configuration shows that crack growth is not predicted to occur, which agrees with the observations of the experiment. A parametric study is conducted to investigate the effect of the skin-stiffener debond parameters such as length, width and location on crack growth and the collapse behaviour of the panel. It is found that the sensitivity of the panel design to the damage parameters is highly dependent on the postbuckling mode shape or displacement pattern, and particularly the extent to which this influences the conditions at the crack front. More broadly, the analysis tool is shown to be capable of capturing the critical damage mechanisms leading to structural collapse of stiffened composite structures in the postbuckling region. [Copyright &y& Elsevier]

Abstract: The influence of nanoclay on the impact damage resistance of carbon fibre–epoxy composites has been investigated using the low-velocity impact and compression after impact (CAI) tests. The load–energy vs. time relations were analyzed to gain insight into the damage behaviours of the materials. The CFRPs containing organoclay brought about significant improvement in impact damage resistance and damage tolerance in the form of smaller damage area, higher residual strength and higher threshold energy level. The presence of nanoclay in the epoxy matrix induced the transition of failure mechanisms of CFRP laminates during the CAI test, from the brittle buckling mode to more ductile, multi-layer delamination mode. Addition of 3wt% clay was shown to be an optimal content for the highest damage resistance. [Copyright &y& Elsevier]