Search

Abstract We developed an attractive combustion approach for synthesizing uniformly shaped AlN dendritic crystals by combustion of Al + 0.1AlF 3 + k Al 2 O 3 powder mixtures in a nitrogen atmosphere. The combustion temperature measured for various k values was between 1650 and 1750 °C and the micro-droplets of Al formed in the beginning stages of the process were enveloped by the solid layers of Al 2 O 3 , and the subsequent multipoint nucleation and crystallization produced morphologically and size uniform dendritic crystals. We proposed a theoretical model for calculating the thickness and the number of Al 2 O 3 layers around of Al microdroplets at known concentration of Al 2 O 3. Depending on the concentration of Al 2 O 3 , these structures were simple stars with six points and stellar dendrites with multiple petals. [ABSTRACT FROM AUTHOR]

In this study, a single-step combustion process for the synthesis 1-D, 2-D, and 3-D micro and nanostructures of AlN was developed. The structures were grown by combustion of Al+ k AlF 3 (or ZnF 2 )+ m NH 4 Cl reaction mixture under 4.0 MPa nitrogen atmosphere. Based on experimental data, the growth conditions, morphology, and composition, optical, and thermal properties of AlN micro and nanostructures were determined. The formation of structures was associated with the combustion temperature, liquid and gas-phase reactions, and the type of additives used in the experiments. The new insight, we gleaned from this study may help in the selective growth of AlN micro and nanostructures of different morphology, enhancing their functionality. [ABSTRACT FROM AUTHOR]

The synthesis of AlN nanoparticles in non-isothermal high-temperature conditions was developed. The process involved Al 2 O 3 –Mg–NH 4 Cl mixtures preparation and combustion in nitrogen atmosphere. Temperature profiles in the combustion waves were recorded by thermocouples, and the values of combustion temperature and wave velocity were determined from the recorded profiles. The existence of two independed combustion regimes with maximum temperatures of about 850 °C and 1400–1600 °C were revealed based on concentrations of NH 4 Cl. AlN nanocrystals were obtained and investigated by X-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy, and Brunauer–Emmett–Teller surface area. AlN nanocrystals prepared under non-isothermal combustion process were comprised well distributed multi-faceted particles with an average size of 50–200 nm. The chemical reactions in the combustion wave were discussed and a possible thermochemical pathway for the synthesis of AlN nanoparticles was proposed. [ABSTRACT FROM AUTHOR]

Abstract: Quasi-aligned, high-aspect-ratio AlN micro- and nanostructures were synthesized under high nitrogen pressure by the exothermic reaction of an Al+0.015mol (C2F4) n mixture. Structurally uniform AlN micro- and nanofibers with hexagonal and cylindrical morphologies were obtained when the system temperature was maintained within the range of 1600–1700°C. The fibers had aspect ratios as high as 2000, diameters in the range of ∼0.05–20μm, and were ∼100–1000μm in length. High-resolution transmission electron microscopic and selected area diffraction analyses indicated that the as-synthesized AlN micro- and nanostructures are perfectly single crystalline with preferential growth along the [001] direction. Branching was also observed in some of the micro-fibers, giving rise to randomized, two-dimensional comb textures. Based on the results obtained in the present study, a mechanism for the formation of AlN micro- and nanostructures under combustion conditions was proposed. [Copyright &y& Elsevier]