The large size (4 cm × 4 cm × 1 cm) Ce3+-doped high gadolinium oxyfluoride glass with density of 5.83 g/cm³ was prepared by the melt quench method at 1220 °C. The glass is colorless and transparent over the visible range. The prolonged decay time under 275 nm UV light demonstrates the energy transfer from Gd3+ ions to Ce3+ ions. The X-ray excited luminescence spectra (XEL) show the emission peak corresponds to the 5d→4f transitions of Ce3+ ion. The integral emission intensity of glass was compared with that of bismuth germanate oxide (BGO) crystals. The scintillation property of glass was studied under the γ -ray from 137Cs source and a clear energy peak was observed with light yield (LY) over 1100 ph/MeV. The scintillation decay time comprises fast and slow components. All results presented in this work indicate the appropriate potential to be high-energy rays detecting material for CEPC. [ABSTRACT FROM AUTHOR]

Different B 2 O 3 content was added to Ce3+–doped Gd 2 O 3 –Al 2 O 3 –SiO 2 (xBGAS:1.1Ce3+, x = 0, 5, 10, 15) glasses to improve the photoluminescence (PL) and scintillation properties. The transmittance of 15BGAS:1.1Ce3+ glass is over 80%. The X–ray absorption near edge spectroscopy (XANES) spectra imply that Ce4+ can be effectively reduced to Ce3+ in the glasses by adding Si 3 N 4. The excitation and emission spectra show a blue shift with increase of B 2 O 3 content. The photoluminescence quantum yield (PL QY) increases with the increase of B 2 O 3 content, reached the maximum of 59.55% when x = 15. The PL decay time of the glasses exhibits typical values (44–50 ns) due to 5d→4f transition of Ce3+ ions. The PL thermal activation energy become larger, indicating that xBGAS:1.1Ce3+ glasses have better luminescent thermal stability. The integral X–ray excited luminescence (XEL) intensity of the 15BGAS:1.1Ce3+ glass is 37.38% of Bi 4 Ge 3 O 12 (BGO) crystal, and the light yield is 1267 ph/MeV with an energy resolution of 23.22% at 662 keV when exposed to γ–rays. With the increase of B 2 O 3 content, the fast component of scintillation decay time gradually becomes shorter and the slow component becomes longer. The thermally stimulated luminescence (TSL) curves were measured to investigate the trap depth and density of defects in xBGAS:1.1Ce3+ glasses. [ABSTRACT FROM AUTHOR]