Search

Healing of large bone defects requires implants or scaffolds that provide structural guidance for cell growth, differentiation, and vascularization. In the present work, an agarose-hydroxyapatite composite scaffold was developed that acts not only as a 3D matrix, but also as a release system. Hydroxyapatite (HA) was incorporated into the agarose gels in situ in various ratios by a simple procedure consisting of precipitation, cooling, washing, and drying. The resulting gels were characterized regarding composition, porosity, mechanical properties, and biocompatibility. A pure phase of carbonated HA was identified in the scaffolds, which had pore sizes of up to several hundred micrometers. Mechanical testing revealed elastic moduli of up to 2.8 MPa for lyophilized composites. MTT testing on Lw35human mesenchymal stem cells (hMSCs) and osteosarcoma MG-63 cells proved the biocompatibility of the scaffolds. Furthermore, scaffolds were loaded with model drug compounds for guided hMSC differentiation. Different release kinetic models were evaluated for adenosine 5′-triphosphate (ATP) and suramin, and data showed a sustained release behavior over four days.

This work presents a novel composite hydrogel consisting of silk fibroin (SF) and nanohydroxyapatite (nanoHA) prepared by a new and innovative method using ethanol as gelling agent capable of forming hydrogels in few minutes. The properties of the composite material, such as the microstructure as well as the chemical and physical properties were studied. Moreover in␣vitro studies of osteoblastic citocompatibility were performed. The microporosity and macroporosity obtained combined with interconnected porous structure and a uniform dispersion of nanoHA particles throughout the fibroin matrix makes composite hydrogel suitable for bone regeneration. The compression modulus of composite hydrogels was increased as the nanoHA concentration increased from 10 to 15 wt.% and the water uptake ability of these materials decreased with the incorporation of nanoHA. The metabolic and alkaline phosphatase activities of osteoblastic cells were improved with the incorporation of nanoHA in the SF matrix providing a more promising material for bone tissue engineering. [ABSTRACT FROM AUTHOR]

Abstract: Nanotechnology has enabled the engineering of nanostructured materials to meet current challenges in bone replacement therapies. Biocomposite nanofibrous scaffolds of poly(l-lactic acid)-co-poly(ɛ-caprolactone), gelatin and hydroxyapatite (HA) were fabricated by combining the electrospinning and electrospraying techniques in order to create a better osteophilic environment for the growth and mineralization of osteoblasts. Electrospraying of HA nanoparticles on electrospun nanofibers helped to attain rough surface morphology ideal for cell attachment and proliferation and also achieve improved mechanical properties than HA blended nanofibers. Nanofibrous scaffolds showed high pore size and porosity up to 90% with fiber diameter in the range of 200–700nm. Nanofibrous scaffolds were characterized for their functional groups and chemical structure by FTIR and XRD analysis. Studies on cell–scaffold interaction were carried out by culturing human fetal osteoblast cells (hFOB) on both HA blended and sprayed PLACL/Gel scaffolds and assessing their growth, proliferation, mineralization and enzyme activity. The results of MTS, ALP, SEM and ARS studies confirmed, not only did HA sprayed biocomposite scaffolds showed better cell proliferation but also enhanced mineralization and alkaline phosphatase activity (ALP) proving that electrospraying in combination with electrospinning produced superior and more suitable biocomposite nanofibrous scaffolds for bone tissue regeneration. [Copyright &y& Elsevier]

Different biomaterials have been used as scaffolds for bone tissue engineering. Here we characterize a biomaterial composed of sintered (1100°C) and powdered hydroxyapatite (HA) and type I collagen (Coll), both of bovine origin, designed for osteoconductive and osteoinductive scaffolds. Coll/HA proportions were 1/2.6 and 1/1 (wet weight), and particles sizes varied from 200 to 400 μm. Vv (volume density) and Sv (surface to volume density) for the HA particles in the composite ranged from 0.48±0.06 to 0.55±0.02 and 5.090±0.545 to 6.366±0.289 μm−1, respectively. Due to the relatively small changes in Vv and Sv, a macroporosity could be characterized for the biocomposite. X-ray diffraction and infrared spectroscopy showed that the sintered bone was composed essentially of HA with minimum additional groups such as surface calcium hydroxide, surface and crystal water, free carbon dioxide and possibly brushite. Mass spectrometry detected carbonates at A and B sites of HA, and weakly bound to the structure. Human osteoblasts adhered and spread on both the HA particle surface and the collagen fibers, which seemed to guide cells between adjacent particles. The biocomposite studied has several characteristics considered as ideal for its use as a scaffold for osteoconduction and osteoinduction. [Copyright &y& Elsevier]