Search

Activation of metal oxides by light is a robust yet facile approach to manipulating their surface chemistry for favorable reactions with target molecules in heterogeneous catalysis and gas sensors. However, a limited understanding of interface chemistry and the involved mechanism impedes the development of a rational design of oxide interfaces for light‐activated gas sensing. Herein, the TiOx‐assisted photosensitization of In2O3 toward NO2 sensing is investigated as a case study to elucidate the detailed mechanism of light‐activated surface chemistry at the metal/gas interface. The resultant heterogeneous oxides exhibit outstanding NO2 sensing performance under light irradiation thanks to abundant photoexcited electrons and holes that serve as adsorption and desorption sites, respectively, to accelerate both surface reactions. Furthermore, the facile transfer of electrons and holes across the TiOx‐In2O3 interface contributes to improving the reversibility of sensing kinetics. Through this study, the mechanistic understanding is established of how the surface chemistry of metal oxide surfaces can be tuned by light activation providing an effective route to the design fabrication of high‐performance gas sensors. [ABSTRACT FROM AUTHOR]

Transition metal dichalcogenides (TMDs) have attracted significant interest as gas‐sensing materials due to their unique crystal structure and surface. However, there are still issues when it comes to expanding the types of sensing gases for the TMD gas sensors. To extend gas‐sensing selectivity for the TMD gas sensors in this study, a monolayer (ML) 2D metal–organic framework (MOF) is introduced on top of the PtSe2 gas sensor, thereby tuning the major sensing analyte of PtSe2 from NO2 to H2S. Density functional theory calculations elucidate that the metal species of ML MOFs are attributed to the tuned selectivity of the analytes, based on the difference in binding energies. It is also demonstrated that ML MOF maintained the high responsivity of the pristine PtSe2 even at a low concentration of gas (200 ppb). This is further confirmed through the molecular dynamics simulations, which reveal that the ML feature of the ML MOF is highly essential to preserve the intrinsic ultra‐low limit detection properties of pristine PtSe2. [ABSTRACT FROM AUTHOR]

Graphene oxide (GO) doping and reduction allow for physicochemical property modification to suit practical application needs. Herein, the challenge of simultaneous low‐thermal‐budget heteroatom doping of GO and its reduction in ambient air is addressed through the synthesis of B‐doped reduced GO (B@rGO) by flash irradiation of boric acid loaded onto a GO support with intense pulsed light (IPL). The effects of light power and number of shots on the in‐depth sequential doping and reduction mechanisms are investigated by ex situ X‐ray photoelectron spectroscopy and direct millisecond‐scale temperature measurements (temperature >1600 °C, < 10‐millisecond duration, ramping rate of 5.3 × 105 °C s−1). Single‐flash IPL allows the large‐scale synthesis of substantially doped B@rGO (≈3.60 at% B) to be realized with a thermal budget 106‐fold lower than that of conventional thermal methods, and the prepared material with abundant B active sites is employed for highly sensitive and selective room‐temperature NO2 sensing. Thus, this work showcases the great potential of optical annealing for millisecond‐scale ultrafast reduction and heteroatom doping of GO in ambient air, which allows the tuning of multiple physicochemical GO properties. [ABSTRACT FROM AUTHOR]

Abstract: Edges of 2D transition metal dichalcogenides (TMDs) are well known as highly reactive sites, thus researchers have attempted to maximize the edge site density of 2D TMDs. In this work, metal‐organic framework (MOF) templates are introduced to synthesize few‐layered WS2 nanoplates (a lateral dimension of ≈10 nm) confined in Co, N‐doped hollow carbon nanocages (WS2_Co‐N‐HCNCs), for highly sensitive NO2 gas sensors. WS2 precursors are assembled in the surface cavity of Co‐based zeolite imidazole framework (ZIF‐67) and subsequent pyrolysis produced WS2_Co‐N‐HCNCs. During the pyrolysis, the carbonized ZIF‐67 are doped by Co and N elements, and the growth of WS2 is effectively suppressed, creating few‐layered WS2 nanoplates functionalized Co‐N‐HCNCs. The WS2_Co‐N‐HCNCs exhibit outstanding NO2 sensing characteristics at room temperature, in terms of response (48.2% to 5 ppm), selectivity, response and recovery speed, and detection limit (100 ppb). These results are attributed to the enhanced adsorption and desorption kinetics of NO2 on abundant WS2 edges, confined in the gas permeable HCNCs. This work opens up an efficient way for the facile synthesis of edge abundant few‐layered TMDs combined with porous carbon matrix via MOF templating route, for applications relying on highly active sites. [ABSTRACT FROM AUTHOR]

2D Oxide Sensors: Heterogeneous, Porous 2D Oxide Sheets via Rapid Galvanic Replacement: Toward Superior HCHO Sensing Application (Adv. Funct. In article number 1903012, Hee Jung Park, Il-Doo Kim, and co-workers develop porous and heterogeneous SnO SB 2 sb /CoO SB I x i sb nanosheets by combining exfoliation with galvanic replacement reaction. Due to the high porosity, thin-thickness (<10 nm), and numerous heterogeneous junctions, the heterogeneous SnO SB 2 sb /CoO SB I x i sb nanosheets show super-sensitive HCHO sensing characteristics with a rapid response (<10 sec). [Extracted from the article]

2D heterogeneous oxide nanosheets (NSs) have attracted much attention in various scientific fields owing to their exceptional physicochemical properties. However, the fabrication of 2D oxide NSs with abundant p–n interfaces and large amounts of mesopores is extremely challenging. Here, a facile synthesis of highly porous 2D heterogeneous oxide NSs (e.g., SnO2/CoOx) is suggested through a 2D oxide exfoliation approach combined with a fast galvanic replacement reaction (GRR). The ultrathin (<5 nm) layered CoOx NSs are simply prepared by ion‐exchange exfoliation and a subsequent GRR process that induces a rapid phase transition from p‐type CoOx to n‐type SnO2 metal oxides (<10 min). The controlled GRR process enables the creation of heterogeneous SnO2/CoOx NSs consisting of small SnO2 grain sizes (<10 nm), high porosity, numerous heterojunctions, and sub‐10 nm thickness, which are highly advantageous characteristics for chemiresistive sensors. Due to the advantage of these features, the porous SnO2/CoOx NSs exhibit an unparalleled HCHO‐sensing performance (Rair/Rgas > 35 @ 5 ppm with a response speed of 9.34 s) with exceptional selectivity compared to that of the state‐of‐the‐art metal oxide‐based HCHO gas sensors. [ABSTRACT FROM AUTHOR]