Search

The material selected for this investigation was low alloy weld metal deposit after TIG welding with various amount of oxygen in weld metal deposit (WMD). After TIG process it is difficult to get proper amount of oxygen in WMD on the level much lower than 350 ppm. The highest impact toughness of low alloy WMD corresponds with the amount of oxygen in WMD above 350 ppm. In the paper focuses on low alloy steel after innovate welding method with micro-jet cooling that could be treated as a chance on rising amount of oxygen in weld. Weld metal deposit (WMD) was carried out for TIG welding with micro-jet cooling with various amount of oxygen in WMD. In that paper various gas mixtures (gas mixtures Ar-O2 and Ar-CO2) were tested for micro-jet cooling after TIG welding. An important role in the interpretation of the results can give methods of artificial intelligence.

The paper focuses on low alloy steel after innovate welding method with micro-jet cooling. Weld metal deposit (WMD) was carried out for welding and for MIG and MAG welding with micro-jet cooling. This method is very promising mainly due to the high amount of AF (acicular ferrite) and low amount of MAC (self-tempered martensite, retained austenite, carbide) phases in WMD. That structure corresponds with very good mechanical properties, ie. high impact toughness of welds at low temperature. Micro-jet cooling after welding can find serious application in automotive industry very soon. Until that moment only argon, helium and nitrogen were tested as micro-jet gases. In that paper first time various gas mixtures (gas mixtures Ar-CO2) were tested for micro-jet cooling after welding.

This paper presents results of experimental research concerning the impact of an innovative method of micro-jet cooling on the padding weld performed with MIG welding. Micro-jet cooling is a novel method patented in 2011. It enables to steer the parameters of weld cooling in a precise manner. In addition, various elements which may e.g. enhance hardness or alter tribological properties can be entered into its top surface, depending on the applied cooling gas. The material under study was steel 20MnCr5, which was subject to the welding process with micro-jet cooling and without cooling. Nitrogen was used as a cooling gas. The main parameter of weld assessment was wear intensity. The tests were conducted in a tribological pin-on-disc type position. The following results exhibit growth at approximately 5% in wear resistance of padding welds with micro-jet cooling.

The material selected for this investigation was low alloy steel weld metal deposit (WMD) after MIG welding with micro-jet cooling. The present investigation was aimed as the following tasks: obtained WMD with various amount of acicular ferrite and further analyze impact toughness of WMD in terms of acicular ferrite amount in it. Weld metal deposit (WMD) was first time carried out for MIG welding with micro-jet cooling of compressed air and gas mixture of argon and air. Until that moment only argon, helium and nitrogen were tested as micro-jet gases for MIG/MAG processes. An important role in the interpretation of the results can give methods of artificial intelligence.

The material selected for this investigation was low alloy steel weld metal deposit (WMD) after MAG welding with micro-jet cooling. The present investigation was aimed as the following tasks: analyze impact toughness of WMD in terms of micro-jet cooling parameters. Weld metal deposit (WMD) was first time carried out for MAG welding with micro-jet cooling of compressed air and gas mixture of argon and air. Until that moment only argon, helium and nitrogen and its gas mixture were tested for micro-jet cooling.

The paper offers mathematical equations of the influence of micro-jet cooling on structure and impact toughness properties of metal weld deposit. Weld metal deposit (WMD) was carried out for standard MIG welding and for MIG welding with micro-jet cooling. This new method is very promising mainly due to the high amount of AF (acicular ferrite) and low amount of MAC (selftempered martensite, retained austenite, carbide) phases in WMD. That structure corresponds with very good mechanical properties ie. good impact toughness of welds at low temperature. Micro-jet cooling after welding can find serious application in automotive industry very soon. Until that moment only argon, helium, nitrogen and gas mixtures of argon were tested for micro-jet cooling after welding. The best results of mechanical properties of WMD in presented welding method correspond with micro-jet argon cooling. [ABSTRACT FROM AUTHOR]