Purpose Macro synthetic steel fibers were incorporated into the concrete material as a toughening agent to improve the corrosion and cracking resistances of concrete in a sulfate-containing service environment.Design/methodology/approach To study the basic mechanical properties of this system, an accelerated concrete degradation test was designed to evaluate the influence of the sulfate ions on the concrete. A three-point bending test was carried out in the laboratory to evaluate the fracture toughness. The thickness of the damaged concrete layer and changes of microstructure of the degraded concrete were monitored by using ultrasound, scanning electron microscopy and X-ray diffraction detection methods.Findings The results showed that compared to the performance of ordinary concrete, in an exposure environment containing sulfate ions, the structure compactness of macro synthetic steel fiber concrete was improved, degradation resistance to the sulfate solution was enhanced and the fracture resistance performance was improved significantly.Originality/value The thickness of the degradation layer on the macro synthetic steel fiber concrete was less than a half of that of ordinary concrete in the sulfate environment, and was generally unchanged with increase in the sulfate concentration. Through micro-structural analysis, it was confirmed that macro synthetic steel fiber improved the compactness of the concrete structure, inhibiting access of sulfate ions to the interior of the concrete and thereby reducing the degree of sulfate degradation to the concrete. [ABSTRACT FROM AUTHOR]

Purpose – The purpose of this study was to reuse cement kiln dust (CKD) in cement products and report the results of determining the long-term compression and flexural tensile strengths of mortars containing CKD as a partial replacement of sulfate-resistant cement (SRC). During the manufacturing of Portland cement, voluminous quantities of the byproduct dust are produced, which is commonly known as CKD. In the past decade, according to environmental requirements, many researchers have attempted to reuse CKD in cement products. Design/methodology/approach – The long-term compression and flexural tensile strengths of mortars containing CKD as a partial replacement of SRC were tested. The replacement ratios in this study were 0, 5, 10, 15 and 20 per cent. The specimens were exposed to a highly saline environment after normal curing in water for a 28-day period. Findings – The results indicated a slight increase in the strength of CKD–SRC mortar containing 10 per cent CKD and moderate sulfate resistance when the CKD ratio reached 20 per cent, as compared to the reference mortar. In addition, CKD did not adversely affect the properties of SRC mortar subjected to sulfate exposure, even after one year. Originality/value – The tests were inducted for the first time on SRC, and the new results can be used to produce an environmental-friendly concrete. [ABSTRACT FROM AUTHOR]