Search

Abstract Recent studies have shown that under certain environmental conditions, plastic scintillators which are used in a variety of applications in outdoor environments develop defects called "fogging", resulting in a reduced useful lifetime and increased maintenance cost. Applications of plastic scintillators include scanning recycled steel going into a processing plant, personnel portals to scan employees, and scanning cargo and cars crossing borders of many countries. In this report, fogging was studied in conventional PVT and PS-based plastic scintillators, both field aged and freshly cast. A new fogging-resistant PVT-based formulation developed by scientists at Lawrence Livermore National Laboratory (LLNL) was tested as well. We used accelerated aging experiments via temperature and humidity cycling in controlled laboratory conditions to create observable temporary fogging defects in small samples (≤ 1 in3). Photoluminescence and optical transmission studies were used to evaluate the effect of the fogging. The time evolution of the induced temporary fogging formation and defogging (i.e. fading of defects in ambient conditions over time) were recorded using optical microscopy, time-lapse photography, and gravimetric analysis. [ABSTRACT FROM AUTHOR]

KCaI 3 :Eu crystals have been identified as very promising for use in spectroscopic detector applications related to nuclear nonproliferation and domestic security efforts. Initial studies have shown for small crystals a few mm 3 in size with 3% europium dopant concentration, a high light yield of >70,000 ph/MeV and energy resolution of ≈3% at 662 keV is attainable which is comparable with the highest performance scintillators discovered. In this work, single crystals of KCaI 3 with a range of Eu 2+ doping between 0 and 5 at% substituting for Ca 2+ were grown at 22 mm diameter and their performance for gamma-ray spectroscopy studied. Comparisons among crystals approximately Ø22 mm×22 mm (8.4 cm 3 or ≈0.5 in 3 ) provide a more accurate understanding of how scintillation performance changes with Eu doping and increased crystal size. KCaI 3 in the undoped form is shown to be a highly efficient intrinsic scintillator with a defect-related emission at 404 nm which coexists with the Eu 2+ 5d–4f emission in low dopant concentrations and is completely re-absorbed in more heavily doped crystals. For larger crystals, effects from self-absorption due to Eu activation become more evident by a near doubling of decay time for 0.5 in 3 crystals as the activator is increased from 0.5 to 5.0 at% Eu. Comparisons of pulse-height spectra obtained for Ø22 mm×22 mm cylinders with varying Eu concentration suggests best performance is achieved using lower Eu additions closer to 0.5–1.0 at%. Using a modified crystal packaging featuring an offset reflector geometry, 0.5 in 3 crystals of KCaI 3 :Eu can attain under 4% energy resolution at 662 keV. [ABSTRACT FROM AUTHOR]

The crystal growth of CsSrBr 3 : Eu with improved energy resolution for use in gamma-ray detection applications is reported. CsSrBr 3 boules doped with 5% Eu were grown by the vertical Bridgman method in quartz ampoules of 17 mm and 22 mm diameter. It was observed that the addition of an excess of CsBr in the melt improved the optical transparency and energy resolution of the scintillator crystals. The energy resolution of the gamma-ray spectra recorded with crystals measuring ø 22 mm×15 mm was 7.4% at 662 keV (for a crystal with non-optimized stoichiometry) and 6.2% at 662 keV (for a crystal with optimized stoichiometry i.e. excess CsBr in the melt), which is a significant improvement over previous reports. Temperature dependent powder XRD measurements were also carried out to study the solid–solid phase transition which occurs as the crystals are cooled after growth. [ABSTRACT FROM AUTHOR]

Abstract: The current work describes two new Eu2+-activated scintillator materials, CsCaI3:Eu and CsCaCl3:Eu. Single crystals of CsCaI3:Eu and CsCaCl3:Eu were grown from the melt via the vertical Bridgman method. Scintillation properties, including decay time, light output, X-ray excited luminescence and light output, as a function of excitation energy were measured, as were the photoluminescence emission and excitation spectra. In addition, moisture sensitivity was evaluated by measuring the moisture uptake rate and compared with those of NaI:Tl and Cs2LiYCl6:Ce reference scintillators. [Copyright &y& Elsevier]