Abstract: Single-crystalline nanorods of β-MnO2, α-Mn2O3 and Mn3O4 were successfully synthesized via the heat-treatment of γ-MnOOH nanorods, which were prepared through a hydrothermal method in advance. The calcination process of γ-MnOOH nanorods was studied with the help of Thermogravimetric analysis and X-ray powder diffraction. When the calcinations were conducted in air from 250 to 1050°C, the precursor γ-MnOOH was first changed to β-MnO2, then to α-Mn2O3 and finally to Mn3O4. When calcined in N2 atmosphere, γ-MnOOH was directly converted into Mn3O4 at as low as 500°C. Transmission electron microscopy (TEM) and high-resolution TEM were also used to characterize the products. The obtained manganese oxides maintain the one-dimensional morphology similar to the precursor γ-MnOOH nanorods. Further experiments show that the as-prepared manganese oxide nanorods have catalytic effect on the oxidation and decomposition of the methylene blue (MB) dye with H2O2. [Copyright &y& Elsevier]

Nanocrystalline silicon carbide has been prepared via reacting magnesium silicide (Mg2Si) with carbon tetrachloride (CCl4) in an autoclave at 450–600°C. X-ray diffraction patterns of the products can be indexed as the cubic cell of SiC with the lattice constant, a=4.352 Å, in good agreement with a=4.349 Å (JCPDS card No. 75-0254). The transmission electron microscopy images show that the sample mainly consists of nanoparticles with an average size from 30 to 80 nm co-existing with a small fraction of nanorods and nanowires. Typically the nanorods range from 20 to 40 nm in diameter and the nanowires have diameters of 20 nm and lengths up to 10 μm. The Raman spectrum shows a characteristic sharp peak at 790 cm-1. X-ray photoelectron spectra (XPS) gives an atomic ratio of Si to C as 1.08:1.00 from the quantification of the peak intensities. Photoluminescence spectrum reveals that the SiC sample emits ultraviolet light of 328 nm. A possible mechanism and the influence of temperature on the formation of crystalline SiC are proposed. [Copyright &y& Elsevier]