Cellulose swelling using different protic, aprotic and alkaline solvents, which are capable of penetrating crystalline parts of cellulose is one of the important methods to enhance the accessibility and, as a result, the reactivity of cellulose in modification reactions. Here we discuss changes in the structure of cellulose II in never-dried Lyocell fibers upon swelling with different solvents and aqueous solutions using FTIR as well as solid-state 13C NMR spectroscopies and DSC thermal analysis. Changes in the water retention behavior and accessibility of fibers were correlated with solvent-related changes in the fiber structure and were in accordance with the results obtained by FTIR and 13C NMR spectroscopies.

Catalytic upgrading of fast pyrolysis bio-oil from two different types of lignocellulosic biomass was conducted using an H-ZSM-5 catalyst at different temperatures. A fixed-bed pyrolysis reactor has been used to perform in situ catalytic pyrolysis experiments at temperatures of 673, 773, and 873 K, where the catalyst (H-ZSM-5) has been mixed with wood chips or lignin, and the pyrolysis and upgrading processes have been performed simultaneously. The fractionation method has been employed to determine the chemical composition of bio-oil samples after catalytic pyrolysis experiments by gas chromatography with mass spectroscopy (GCMS). Other characterization techniques, e.g., water content, viscosity, elemental analysis, pH, and bomb calorimetry have been used, and the obtained results have been compared with the non-catalytic pyrolysis method. The highest bio-oil yield has been reported for bio-oil obtained from softwood at 873 K for both non-catalytic and catalytic bio-oil samples. The results indicate that the main effect of H-ZSM-5 has been observed on the amount of water and oxygen for all bio-oil samples at three different temperatures, where a significant reduction has been achieved compared to non-catalytic bio-oil samples. In addition, a significant viscosity reduction has been reported compared to non-catalytic bio-oil samples, and less viscous bio-oil samples have been produced by catalytic pyrolysis. Furthermore, the obtained results show that the heating values have been increased for upgraded bio-oil samples compared to non-catalytic bio-oil samples. The GCMS analysis of the catalytic bio-oil samples (H-ZSM-5) indicates that toluene and methanol have shown very similar behavior in extracting bio-oil samples in contrast to non-catalytic experiments. However, methanol performed better for extracting chemicals at a higher temperature.