The ternary metal sulfide CdIn2S4 (CIS) has great application potential in solar-to-hydrogen conversion due to its suitable band gap, good stability and low cost. However, the photocatalytic hydrogen (H2) evolution performance of CIS is severely limited by the rapid electron–hole recombination originating from the slow photogenerated hole transfer kinetics. Herein, by simply depositing cobalt phosphate (CoHxPOy, noted as Co-Pi), a non-precious co-catalyst, an efficient pathway for accelerating the hole transfer process and subsequently promoting the H2 evolution reaction (HER) activity of CIS nanosheets is developed. X-ray photoelectron spectroscopy (XPS) reveals that the Co atoms of Co-Pi preferentially combine with the unsaturated S atoms of CIS to form Co-S bonds, which act as channels for fast hole extraction from CIS to Co-Pi. Electron paramagnetic resonance (EPR) and time-resolved photoluminescence (TRPL) showed that the introduction of Co-Pi on ultrathin CIS surface not only increases the probability of photogenerated holes arriving the catalyst surface, but also prolongs the charge carrier's lifetime by reducing the recombination of electrons and holes. Therefore, Co-Pi/CIS exhibits a satisfactory photocatalytic H2 evolution rate of 7.28 mmol g−1 h−1 under visible light, which is superior to the pristine CIS (2.62 mmol g−1 h−1) and Pt modified CIS (3.73 mmol g−1 h−1). [ABSTRACT FROM AUTHOR]

AgBiSe2 is a promising thermoelectric (TE) candidate because of its intrinsically low thermal conductivity (κ = 0.4–0.5 W K−1 m−1 at ∼770 K) and optimal n-type carrier concentration (5.85 × 1018 cm−3 at 300 K). However, its TE figure of merit (ZT) is still low (0.3 at ∼770 K). Therefore, it is necessary to further improve its ZT. In this work, the solid solutions (AgBiSe2)1−x(Ag2Te)x (x = 0–0.125) have been designed through simple alloying Ag2Te inspired by the entropy engineering concept, and the TE performance has been further regulated. The analyses show that the exothermic effects related to α/β and β/γ phase transitions weaken, and the transition temperature of β/γ decreases as the Ag2Te content increases, which indicates the stabilization of the cubic γ-phase at high temperatures. Aside from that, the power factor (PF) enhances from 2.91 μW/cm K2 (x = 0) to 3.49 μW/cm K2 (x = 0.075), and at the same time, the lattice thermal conductivity reduces from 0.3 W K−1 m−1 to 0.1 W K−1 m−1 at ∼760 K. This directly improves the TE performance with the highest ZT value of 1.0, which is almost double that of the pristine AgBiSe2. The result suggests that the entropy engineering is a very effective screening method in thermoelectrics. [ABSTRACT FROM AUTHOR]