Search

Mullite fiber felt is a promising material that may fulfill the demands of advanced flexible external thermal insulation blankets. However, research on the fabrication and performance of mullite fiber felt with high-temperature resistance and thermal stability is still lacking. In this work, mullite fibers were selected as raw materials for the fabrication of mullite fibrous porous materials with a three-dimensional net structure. Said materials' high-temperature resistance and thermal stability were investigated by assessing the effects of various heat treatment temperatures (1100 °C, 1300 °C, and 1500 °C) on the phase composition, microstructure, and performance of their products. When the heat treatment temperature was below 1300 °C, both the phase compositions and microstructures of products exhibited stability. The compressive rebound rate of the product before and after 1100 °C reached 92.9% and 84.5%, respectively. The backside temperature of the as-prepared products was 361.6 °C when tested at 1500 °C for 4000 s. The as-prepared mullite fibrous porous materials demonstrated excellent high-temperature resistance, thermal stability, thermal insulation performance, and compressive rebound capacity, thereby indicating the great potential of the as-prepared mullite fibrous porous materials in the form of mullite fiber felt within advanced flexible external thermal insulation blankets. [ABSTRACT FROM AUTHOR]

Fibers crystallize and become brittle at high temperatures for a long time, so the surface coating must maintain long-lasting emission performance, which requires superior antioxidant properties of the high-emissivity fillers. To improve the radiation performance of the coating and the tensile strength of the fiber fabric, a double-layer coating with high emissivity was prepared on the surface of flexible aluminum silicate fiber fabric (ASFF) using MoSi2 and SiC as emissive agents. The incorporation of borosilicate glass into the outer coating during high-temperature oxidation of ZrB2 results in superior encapsulation of emitter particles, effectively filling the pores of the coating and significantly reducing the oxidation rate of MoSi2 and SiC. Furthermore, the addition of an intermediate ZrO2 layer enhances the fiber bundle's toughness. The obtained double-coated ASFF exhibits an exceptionally high tensile strength of 57.6 MPa and a high bond strength of 156.2 kPa. After being subjected to a 3 h heating process, the emissivity exhibits a minimal decrease of only 0.032, while still maintaining a high value above 0.9. The thermal insulation composites, consisting of a flexible ASFF matrix and a ZrB2-modified double-layer coating, exhibit significant potential for broad applications in the field of thermal protection. [ABSTRACT FROM AUTHOR]

Fibrous porous materials are one of the most commonly used high-temperature insulation materials because of their high porosity and low thermal conductivity. Due to their wide applications in the aerospace and energy industries, the investigation of high-elastic thermally insulating porous materials has attracted increasing attention. In order to improve the elasticity of fibrous porous materials, quartz fibers with high aspect ratio were used as matrix, sodium hexametaphosphate (SHMP) was selected as dispersant. We innovatively reported that a unique three-dimensional skeleton structure was constructed by adjusting the dispersion of fibers in the slurry, and the lightweight, thermal insulating and elastic SiO2 fibrous porous material was then prepared by the compression molding method. The characterization results of zeta potential and absorbance showed that the addition of SHMP was an effective method to enhance the dispersibility of quartz fibers in the slurry. SiO2 fibrous porous materials with 0.4 wt% SHMP content exhibited an ideal three-dimensional skeleton structure, which endowed the porous material with high porosity (89.39%), low density (0.04751 g/cm3), and low thermal conductivity (0.0356 W·m−1·K−1). The three-dimensional skeleton structure formed by overlapping fibers with high aspect ratios endowed the porous material with excellent elasticity. SiO2 fibrous porous materials with 0.4 wt% SHMP content could undergo large strains of 30% and achieved a resilience ratio of 81.69% under the 30th compression cycle. Moreover, after heat treatment at 800 °C, SiO2 fibrous porous materials also maintained good elasticity with a resilience ratio of more than 80%. [ABSTRACT FROM AUTHOR]

Recently, many of the world's major river deltas have been sinking, making them increasingly vulnerable to floods and storm surges, salinization and permanent inundation. For the Yellow River delta, annual subsidence rates of several to dozens of centimeters have been reported in the past few years. The extraction of a considerable amount of groundwater due to continuous pumping is suggested as the main driver of the groundwater depression cone. Despite its scale and severity, methods to quantify subsidence are scarce. We introduce a soil mechanics approach to quantify subsidence due to the compaction of soft soil. The largest reduction in soft soil thickness, which is more than 2.6 m, occurred in the salt field area to the north of the Yellow River. Furthermore, by estimating the primary consolidation of soft soil, the subsidence caused by groundwater exploitation is quantified. In the coastal area of the delta, due to excessive exploitation of shallow underground brine resources, the maximum accumulated subsidence is as high as 2 m. Since the natural consolidation of these deltaic sediments has ended, if the current groundwater exploitation intensity is maintained, major subsidence disasters, such as subsidence depressions and ground fissures, will occur. [ABSTRACT FROM AUTHOR]

To prepare a coating with a high emissivity and low solar absorption ratio on the surface of aluminum silicate fiber cloth, the sol-gel method was used with silica sol as a binder. In this study, the effects of two white fillers, titanium oxide and zirconia, on the substrate and radiation properties of coatings were compared after heat treatment at 800–1200 °C. The ZrO 2 -based coating had good stability after heat treatment at 800–1200 °C, and maintained its white color, exhibiting solar absorption ratio of approximately 0.14 and emissivity of 0.84. ZrO 2 -based coatings prevented harmful cracking, as observed for the TiO 2 -based coatings after heat treatment, because of the ZrO 2 phase transformation. The ZrO 2 -based coating did not have strong bonding with the substrate, and the substrate strength was improved by maintaining a weak bonding interface. Compared with the TiO 2 -based coatings, which exhibit reduced substrate strength above 1000 °C, the ZrO 2 -based coating was more suitable for the surface of flexible fiber cloths as a temperature-resistant coating with good development prospects. [ABSTRACT FROM AUTHOR]

It is important to determine the relationship between the concentration of chlorophyll a (Chla) and the inherent optical properties (IOPs) of ocean water to develop optical models and algorithms that characterize the biogeochemical properties and estimate biological pumping and carbon flux in this environment. However, previous studies reported relatively large variations in the particulate backscattering coefficient (b bp (λ)) and Chla from more eutrophic high-latitude waters to clear oligotrophic waters, especially in oligotrophic oceanic areas where these two variables have little covariation. In this study, we examined the variability of b bp (λ) and Chla in the euphotic layer in oligotrophic areas of the tropical Western Pacific Ocean and determined the sources of these variations by reassessment of in-situ measurements and the biogeochemical-argo (BGC-Argo) database. Our findings identified covariation of b bp (λ) and Chla in the water column below the deep Chla maximum (DCM) layer, and indicated that there was no significant correlation relationship between b bp (λ) and Chla in the upper layer of the DCM. Particles smaller than 3.2 µm that were in the water column above the DCM layer had a large effect on the b bp (λ) in the vertical profile, but particles larger than 3.2 µm and smaller than 10 µm had the largest effect on the b bp (λ) in the water column below the DCM layer. The contribution of non-algal particles (NAPs) to backscattering is up to 50%, which occurs in the water depth of 50 m and not consistent with the distribution of Chla. Phytoplankton and NAPs were modeled as coated spheres and homogeneous spherical particles to simulate the b bp (λ) of the vertical profile by Aden-Kerker method and Mie theory, and the results also indicated that the backscattering caused by particles less than 20 µm were closer to the measured data when they were below and above the DCM layer, respectively. This relationship also reflects the b bp (λ) of particles in the upper water was significantly affected particle size, but b bp (λ) in the lower water was significantly affected by Chla concentration. This effect may have relationship with phytoplankton photoacclimation and the relationship of a phytoplankton biomass maximum with particle size distribution in the water column according to the previous relevant studies. These characteristics also had spatial and seasonal variations due to changes of Chla concentration at the surface and at different depths. There was mostly a linear relationship between Chla and b bp (700) during winter. During other seasons, the relationship between these two variables was better characterized by a power function (or a logarithmic function) in the lower layer of the DCM. The spatial and vertical relationships between the b bp (λ) and Chla and the corresponding variations in the types of particles described in this study provide parameters that can be used for accurate estimation of regional geochemical processes.