Search

The possible beneficial impact of self-healing on chloride transport through cracks has been assessed for two bacteria-based self-healing mortar mixtures in comparison with Ordinary Portland cement mortar. Intact self-healing specimens featured lower chloride transport coefficients thanks to a denser microstructure and to the formation of a layer of calcium carbonate on their surface. However, self-healing of cracks of cracked mortar specimens did not significantly reduce chloride penetration during 28 days of chloride exposure compared to cracked and non-healed specimens. On the other hand, this study demonstrated that self-healing of 150–200 µm wide cracks reduced chloride ingress during shorter term (14 days) chloride exposure in comparison to cracked but non-healed specimens. The results of this study suggest that self-healing of cracks through calcium carbonate formation results in water blockage (sealing) of cracks but that the limited amount of limestone formed creates an imperfect barrier against diffusion of chloride ions through the apparent porous limestone. The short-term positive effect of self-healing with respect to reduced chloride ingress could be beneficial in applications where chloride exposure is limited or non-permanent such as concrete structures irregularly exposed to deicing salts or located in the splash zone in marine environments., Materials and Environment

In this study, the applicability of two bacteria-based healing agents (e.g., poly-lactic acid and polyhydroxyalkanoate) in blast furnace slag cement (BFSC) mortar has been assessed. An experimental campaign on the functional properties, self-healing capacity, freezing–thawing and carbonation resistance has been conducted in comparison with plain mortar (Ctrl). Due to the relatively low alkalinity of the mixture, the addition of poly-lactic acid healing agents (PLA) caused coarsening of the micro-structure, decrease of strength and did not improve the self-healing capacity of the material. Among other consequences, the mass loss due to the freezing–thawing of PLA specimens was about 5% higher than that of the Ctrl specimens. On the contrary, no detrimental effect of the mortar functional properties was measured when polyhydroxyalkanoate healing agents (AKD) were added. The self-healing capacity of AKD specimens was higher than that of the Ctrl specimens, reaching a maximum healed crack width of 559 µm after 168 days of self-healing, while it was 439 µm for the Ctrl specimens and 385 µm for PLA specimens. The air void content of the AKD mixture was 0.9% higher than that of the Ctrl, increasing its resistance against freezing–thawing cycles. This study aims to confirm the potential applicability of AKD particles as self-healing agents in low-alkaline cementitious mixtures., Materials and Environment

Self-healing concrete has attracted increasing attention of researchers and industry over the last decades. Given the brittle nature and the relatively low tensile strength of concrete, the occurrence of cracks is an almost unavoidable phenomenon affecting (reinforced) concrete structures. Cracks allow harmful agents present in the environment to penetrate more easily in structures, accelerating the material degradation and compromising their service life. Repair and maintenance interventions are often needed in practice to maintain the serviceability of structures and to avoid any premature collapse. However, the costs of these interventions are socially and economically impactful. The aim of both academia and industry is (and it has been) therefore to limit the need of these interventions through different technologies such as, among others, self-healing concrete. Several technologies (or healing agents) have been proposed and investigated to improve the self-healing capacity of concrete, such as mineral and crystalline admixtures, superabsorbent polymers, micro- or macro-encapsulated polymers, and bio-concrete. Any technology has its own working principle, and the beneficial effects that the healing agents have on concrete properties are continuously under investigation. Despite the relatively high amount of available healing agents, this research focuses on the potential of innovatively using waste-derived polyhydroxyalkanoates (PHAs) as bacterial substrate for self-healing bio-concrete applications. Differently from other healing agents, PHAs are biodegradable and they can be extracted from biomass. The application of PHAs as substrate for bacterial healing agents in concrete does not ideally need high material requirements (e.g., purity) as other applications may do, hence opening the possibility to obtain efficient and relatively low costs healing agents, of which production would significantly contribute to the principles of circular economy. The, Materials and Environment

In this study, the applicability of two bacteria-based healing agents (e.g., poly-lactic acid and polyhydroxyalkanoate) in blast furnace slag cement (BFSC) mortar has been assessed. An experimental campaign on the functional properties, self-healing capacity, freezing–thawing and carbonation resistance has been conducted in comparison with plain mortar (Ctrl). Due to the relatively low alkalinity of the mixture, the addition of poly-lactic acid healing agents (PLA) caused coarsening of the micro-structure, decrease of strength and did not improve the self-healing capacity of the material. Among other consequences, the mass loss due to the freezing–thawing of PLA specimens was about 5% higher than that of the Ctrl specimens. On the contrary, no detrimental effect of the mortar functional properties was measured when polyhydroxyalkanoate healing agents (AKD) were added. The self-healing capacity of AKD specimens was higher than that of the Ctrl specimens, reaching a maximum healed crack width of 559 µm after 168 days of self-healing, while it was 439 µm for the Ctrl specimens and 385 µm for PLA specimens. The air void content of the AKD mixture was 0.9% higher than that of the Ctrl, increasing its resistance against freezing–thawing cycles. This study aims to confirm the potential applicability of AKD particles as self-healing agents in low-alkaline cementitious mixtures., Materials and Environment

The possible beneficial impact of self-healing on chloride transport through cracks has been assessed for two bacteria-based self-healing mortar mixtures in comparison with Ordinary Portland cement mortar. Intact self-healing specimens featured lower chloride transport coefficients thanks to a denser microstructure and to the formation of a layer of calcium carbonate on their surface. However, self-healing of cracks of cracked mortar specimens did not significantly reduce chloride penetration during 28 days of chloride exposure compared to cracked and non-healed specimens. On the other hand, this study demonstrated that self-healing of 150–200 µm wide cracks reduced chloride ingress during shorter term (14 days) chloride exposure in comparison to cracked but non-healed specimens. The results of this study suggest that self-healing of cracks through calcium carbonate formation results in water blockage (sealing) of cracks but that the limited amount of limestone formed creates an imperfect barrier against diffusion of chloride ions through the apparent porous limestone. The short-term positive effect of self-healing with respect to reduced chloride ingress could be beneficial in applications where chloride exposure is limited or non-permanent such as concrete structures irregularly exposed to deicing salts or located in the splash zone in marine environments., Materials and Environment