This paper examines the impact of silicon in the AlCrFeMnNi high-entropy alloy system, focusing on both its microstructural and mechanical properties. Alloys with varying silicon content (x = 0, 0.3, 0.6, 0.9 atomic ratio) were synthesized using vacuum arc melting. The phase formation of these high-entropy alloys was analyzed using x-ray diffraction to comprehend the alloying process behaviour. The findings revealed that the solidification of the AlCrFeMnNi alloy occurred in dendritically, with dendrite cores containing Cr, Fe, and Ni, while interdendritic regions were enriched in Al and Ni after adding Silicon. Increasing the silicon content from 0 to 0.9 led to significant improvements in microhardness and wear resistance. This improvement is attributed to the reinforcement of grain boundaries provided by silicon. The formation of an Al and Ni rich B2 phase is crucial in resisting dislocation motion and preventing further deformation. Additionally, the addition of silicon led to improved corrosion resistance, as demonstrated by potentiodynamic polarization measurements. However, a trade-off was observed between compressive strength and ductility: compressive strength increased with higher silicon concentrations, but at the expense of ductility.

A multi-component category of an alloy containing very specific properties revolutionized the area of material science and the present engineering era. Laser cladding, a technique for surface coating, enhances surface quality and modifies properties using advanced coating technologies. In current trends, Laser cladding is mainly used in equipment and machine parts for enhancing surface properties, repairing damaged parts and surface coating caused by its advantages such as small heat-affected zone, low substrate damage, low dilution rate and exceptional metallurgical material bonding among coating and used substrate. Laser cladding improves substrates’ mechanical and various functional-specific properties, ensuring a high-quality balance between mechanical and surface attributes. The research society was able to investigate laser-cladding HEAs coatings because of the superior attributes of HEAs compared to ordinary alloys. This paper reviews current developments in laser-cladding HEAs coatings and the application of laser-cladding technology to HEAs materials. The laser cladding high-entropy alloy coatings have potential applications in corrosion, wear, and oxidation resistance, as well as their respective substrates. Cladded coatings composed of HEAs materials are measured to have shown potential applications in recent technology, opening exciting possibilities for the future. The study also discusses current trends and future prospects.