This study investigated the convective heat transfer coefficient and friction coefficient in a copper helical double pipe heat exchanger utilizing biosynthetic aqua-based silver (Ag) nanofluids prepared with Histiopteris incisa leaf extract. The nanofluids were characterized using UV–Vis spectroscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and high-resolution transmission electron microscopy. The experimental approach involved the constant heat flux method under laminar flow conditions with flow rates ranging from 100 to 160 litres per hour (LPH). Biosynthesized aqua-based silver nanofluids were synthesized using a one-step biosynthesis method, resulting in volume concentrations ranging from 0.3 to 0.9%. Our findings demonstrated that the biosynthesized aqua-based silver nanofluids exhibited enhanced convective heat transfer compared to pure water. Additionally, the heat transfer coefficient showed an increasing trend with higher volume concentrations of biosynthesized aqua-based silver nanofluids. Notably, the most significant improvement in convective heat transfer, reaching 40%, was achieved with a 0.9% volume concentration of biosynthesized aqua-based silver nanofluids, a flow rate of 140 LPH, and a Dean number of 1400. Moreover, the friction coefficients observed for biosynthesized aqua-based silver nanofluids were 35% higher than those of water in the Dean number range of 1400–2400. [ABSTRACT FROM AUTHOR]

In this present work, characterize the chemical, physical, thermal and Morphological behaviour of raw and alkali-treated (NaOH 5 %,10 % & 15 %) new natural cellulose Habara plant stem fiber (HF). From the chemical analysis, the 10 % alkali-treated HF obtained cellulose (67.9 %), hemicellulose (12.7 %), lignin (11.8 %) wax (0.18 %), moisture (2.44 %) and Ash (1.21 %). Fourier Transform Infrared Spectroscopy Analysis, alkali treatment effectively eliminates hemicellulose and lignin from the surfaces of natural fiber, as seen changes in the FTIR peaks at 1730, 1480, and 1140 cm−1.The X-ray analysis results indicate that, there is crystalline cellulose present, with a crystallinity level of 43.87 %, and that the other components are amorphous. In addition, the thermal stability of lignocellulosic fiber up to 230 °C was observed, and the degradation steps of each major component could be identified. The 10 % alkali-treated HF provides tensile strength of 790.9 MPa, with an elongation at break of about 3.41 %. The Scanning Electron Microscope analysis showcased the morphological changes on the fiber fractured surface, diameter variation, and impurities, etc. The Atomic Force Microscopy was used to determine the surface roughness characteristics of the HF , which confirmed the possible reinforcement in the structure of the polymer matrix composite structure. [ABSTRACT FROM AUTHOR]