Search

We introduce here a multifunctional material composed of alternating atomic sulfide sheets close to the composition of CuFeS2 and Mg-based hydroxide ones (valleriite), which are assembled due to their electric charges of opposite sign. Valleriite particles 50-200 nm in lateral size and 10-20 nm in thickness were synthesized via a simple hydrothermal pathway using various concentrations of precursors and dopants, and examined with XRD, TEM, EDS, X-ray photoelectron spectroscopy, reflection electron energy loss spectroscopy (REELS), Mössbauer, Raman and UV-vis-NIR spectroscopies, and magnetization, dynamic light scattering, and zeta potential measurements. The electronic, magnetic and optical characteristics are found to be critically dependent on the charge (electron density) at the narrow-gap sulfide layers containing Cu+ and Fe3+ cations, and can be tuned via the composition of the hydroxide part. Particularly, substitution of Mg2+ with Al3+ increases the negative charge of the hydroxide layers and reduces the content of Fe3+-OH centers (10-45% of total iron); the effects of Cr and Co dopants entering both layers are more complicated. Mössbauer doublets of paramagnetic Fe3+ detected at room temperature transform into several Zeeman sextets at 4.2 K; the hyperfine fields up to 500 kOe and complex magnetic behavior, but not pure paramagnetism or antiferromagnetism, were observed for valleriites with the higher positive charge of the sulfide sheets, probably due to the depopulation of the minority-spin 3d states of S-bonded Fe3+ ions. Aqueous colloids of valleriite show optical absorption at 500-750 nm, which, along with the peaks at the same energies in REELS, may arise due to quasi-static dielectric resonance involving the vacant Fe 3d band and being dependent on the composition of both layers too. These and other findings call attention to valleriites as a new rich family of 2D materials for a variety of potential applications. [ABSTRACT FROM AUTHOR]

We report here the application of the low-temperature X-ray photoelectron spectroscopy (cryo-XPS) of fast-frozen dispersions as a quasi in situ technique for a case study of metal sulfides reacted in acidic aqueous solutions under non-oxidizing and moderate oxidizing conditions. The sulfide surfaces are known to tend to be depleted in metals, producing essentially sulfur-enriched surfaces and extended underlayers on Fe- and Cu-bearing sulfides, which have previously been examined using depth-sensitive HAXPES and cryo-XPS. The current study is focused on zinc and lead sulfides (natural sphalerite and galena), for whom both the experiment and theoretical DFT simulations suggest a low stability of sulfur-excessive structures. Cryo-XPS revealed the complicated behavior of the minerals under non-oxidative etching conditions, in particular, a notable concentration of polysulfide for PbS in dilute perchloric acid and a very minor one in hydrochloric acid. Oxidative etching with Fe3+ cations produced polysulfide anions and then elemental sulfur, which both volatized in the ultra-high vacuum at room temperature; the species can, nonetheless, be distinguished by considering the binding energies, electrostatic charging and evaporation rates. The cryo-XPS also detected interfacial products, e.g., ferrous chloride. DFT found that S-excessive centers are unstable in the undersurface regions of both materials, but are less unfavorable for ZnS surfaces, in agreement with the experimental data. It was concluded that cryo-XPS allows us to greatly reduce distortions of the interface composition in comparison with conventional techniques. [ABSTRACT FROM AUTHOR]