Search

Porous materials have recently attracted significant attention in the aerospace and biomedical fields for addressing issues related to friction and wear. Porous materials are beneficial in applications where continuous lubrication is not feasible or for components that operate under extreme conditions, such as high speeds, elevated temperatures, and heavy loads. The pores can serve as reservoirs for liquid lubricants, which are gradually released during the operation of the components. The tribological properties of these materials depend on their porosity, the lubricants used, and any additional additives incorporated into the porous materials. This review article provides insight into common fabrication techniques for porous materials and examines their tribological performance for all three classes of materials—polymers, metals, and ceramics. Additionally, it discusses design criteria for porous self-lubricating materials by highlighting the critical properties of both the substrate and lubricants. [ABSTRACT FROM AUTHOR]

The present work reports the utilization of laser treatment for the structuring of a B2O3 coating on ceramic substrates. The two ceramic substrates, pure Al2O3, and Al2O3-20wt% B2O3, were prepared in-house using cold pressing and sintering route. The coatings were prepared by applying the ethanol-B2O3 slurry on the ceramic substrate using a dip coater followed by drying at 100 °C. The dried coatings were subjected to the continuous laser at 22, 29, and 36 W of laser power to achieve the final coating. Coating characterization by X-ray diffraction (XRD) revealed the importance of laser power on controlling the phases of B2O3, which are H3BO3, HBO2, and amorphous B2O3. The crystallinity index (CI) of the coatings calculated using XRD spectrum decreased with an increase in laser power. The coating processed at 36 W showed the lowest CI that reveals higher amorphous B2O3 content. Sliding tests conducted in a controlled humid environment at three sliding velocities suggested a direct relationship between tribological performance and CI value—coating with lower CI value provided consistent lower COF. Additionally, a strong influence of the substrate on tribological performance was also observed—the coatings on the Al2O3-20wt%B2O3 substrate performed superior compared to the coating on the pure Al2O3. The effect of substrates is discussed in terms of thermal conductivity to achieve higher amorphous B2O3 content and the initial surface roughness of the substrates. [ABSTRACT FROM AUTHOR]

The application of tribology is not just limited to mechanical components of engineering systems. As a matter of fact, the understanding of friction and wear can be applied to everyday life. One of the important fields is skin tribology, as human skin interacts with various surfaces of different materials. This paper focuses on the friction behavior of the skin when in contact with the fabric and other materials in relative motion. The excessive friction at the fabric-skin interface may lead to discomfort, blistering, chafing, and pressure ulcers especially in athletes who experience higher friction due to rapid movement for an extended period. Other than understanding the fabric properties, it is equally important to understand the structure and properties of the skin to evaluate its function and interaction with the different fabric materials. The identification of the contributing factors of skin friction can help to design suitable fabric materials. An overview of skin functions and the factors that affect the friction on the skin-textile material interface are presented in this review article.