Gas diffusion layers (GDLs) play a crucial role in heat transfer and water management of cathode catalyst layers in polymer electrolyte fuel cells (PEFCs). Thermal and water gradients can accelerate electrocatalyst degradation and therefore the selection of GDLs can have a major influence on PEFC durability. Currently, the role of GDLs in electrocatalyst degradation is poorly studied. In this study, electrocatalyst accelerated stress test studies are performed on membrane electrode assemblies (MEAs) prepared using three most commonly used GDLs. The effect of GDLs on electrocatalyst degradation is evaluated in both nitrogen (non-reactive) and air (reactive) gas environments at 100% relative humidity. In situ electrochemical characterization and extensive physical characterization is performed to understand the subtle differences in electrocatalyst degradation and correlated to the use of different GDLs. Overall, no difference is observed in the electrocatalyst degradation due to GDLs based on polarization curves at the end of life. But interestingly, MEA with a cracked microporous layer (MPL) in the GDL exhibited a higher electrocatalyst loading loss, which resulted in a lower and more heterogeneous increase in the average electrocatalyst nanoparticle size.

Batteries capable of extreme fast-charging (XFC) are a necessity for the deployment of electric vehicles. Material properties of electrodes and electrolytes along with cell parameters such as stack pressure and temperature have coupled, synergistic, and sometimes deleterious effects on fast-charging performance. We develop a new experimental testbed that allows precise and conformal application of electrode stack pressure. We focus on cell capacity degradation using single-layer pouch cells with graphite anodes, LiNi0.5Mn0.3Co0.2O2 (NMC532) cathodes, and carbonate-based electrolyte. In the tested range (10–125 psi), cells cycled at higher pressure show higher capacity and less capacity fading. Additionally, Li plating decreases with increasing pressure as observed with scanning electron microscopy (SEM) and optical imaging. While the loss of Li inventory from Li plating is the largest contributor to capacity fade, electrochemical and SEM examination of the NMC cathodes after XFC experiments show increased secondary particle damage at lower pressure. We infer that the better performance at higher pressure is due to more homogeneous reactions of active materials across the electrode and less polarization through the electrode thickness. Our study emphasizes the importance of electrode stack pressure in XFC batteries and highlights its subtle role in cell conditions. [ABSTRACT FROM AUTHOR]