Search

A copper-iron mixed oxide was deposited by the washcoating procedure over cordierite honeycomb monoliths for its use as a heterogeneous catalyst in organic synthesis processes. In particular, the prepared catalyst, characterized by techniques such as X-ray fluorescence, X-ray diffraction, SEM-EDS, laser granulometry, adherence tests, Temperature-Programmed Oxidation and Temperature-Programmed Reduction, showed an excellent yield and stability in the selective production of the allylic ester derived from the Kharasch-Sosnovsky oxidation of cyclohexene with benzoic acid. The use of a structured catalyst here proposed opens up an interesting alternative to homogeneous catalysis in the field of synthetic chemistry.

A copper-iron-based catalyst has been prepared by a low-temperature co-precipitation and sonication method. The use of high-energy ultrasound reduces the time required for the preparation process from one workweek to one day with respect to the catalysts obtained by conventional coprecipitation and thermal treatment methods. The resulting material has been characterized at compositional, textural, structural, and chemical levels by ICP-AES, BET, SEM-EDS, XRD, TEM, and FTIR among other techniques. The material shows catalytic activity in the acyloxylation reaction of 1,4-dioxane and cyclohexene under microwave irradiation. In parallel with the optimized catalyst synthesis, the use of microwaves allowed for a substantial improvement in the outcome of the reaction in terms of cleanliness, yield, and time.

Exhausted TWCs subjected to chemical/thermal treatments were used as a support of MnOx catalysts for the total combustion of acetone. The so-prepared new devices were characterized by using adherence tests, elemental and thermal analyses, XRD, N2 physisorption, and SEM-EDS. Incorporation of only 2.6 wt.% of the active phase (Mn2O3 and Mn3O4) to the recycled honeycomb considerably improved the catalytic response, achieving at 250 °C a 60% increase in acetone conversion with respect to the spent autocatalyst. The following procedure is proposed as a simple way to provide the TWC devoid of noble metals a second life in the VOCs’ oxidation field.

Single-phase oxygen stoichiometric LaMnO3 and doped La0.8A0.2MnO3 (A = Ca, Sr, Ba) perovskites have been prepared by a simple one-step auto-combustion method. Cation-deficient LaMnO3+δ and La0.8A0.2MnO3+δ were obtained by calcination of the former samples in air at 750 °C. The samples were characterized by X-ray powder diffraction, X-ray photoelectron spectroscopy, temperature-programmed reduction, temperature-programmed oxygen desorption, and N2 physisorption in order to apply them as catalysts in the complete catalytic oxidation of acetone as a model volatile organic compound. The studied phases show the expected orthorhombic and rhombohedral perovskite crystal structures. Catalytic experiments performed with all the samples show measurable activity already at 100 °C. At 200 °C, doped La0.8A0.2MnO3 samples show higher activity than undoped LaMnO3, with increasing conversion with larger A-cation size. Calcined samples also show higher activity than as-prepared ones making La0.8Ba0.2MnO3+δ the best catalyst at this temperature. All doped samples show >95% acetone conversion at T ≥ 250 °C with a weak dependence on the sample processing or A cation doping. The collected evidence confirms that the most important factors for the catalytic activity of these oxides are the Mn4+/Mn3+ molar ratio on the surface of the samples and the cation-deficiency of the bulk perovskite structure. In addition, increasing the symmetry of the bulk crystal structure appears to have an additional favourable effect. Despite the observation of the presence of surface carbonates, we show that it is possible to use the as-prepared samples without further thermal treatment with good results in the oxidation of acetone.