Abstract Thickness-controlled transparent conducting films (TCFs) were fabricated by transfer printing a 100 nm thick Cu micromesh structure onto poly(vinyl alcohol) (PVA) substrates of different thicknesses (~ 50, ~ 80, and ~ 120 μm) to develop a lightweight transparent wearable heater with short response time. The Cu mesh-based TCF fabricated on a ~ 50 µm thick PVA substrate exhibited excellent optical and electrical properties with a light transmittance of 86.7% at 550 nm, sheet resistance of ~ 10.8 Ω/sq, and figure-of-merit of approximately 236, which are comparable to commercial indium tin oxide film-based transparent conductors. The remarkable flexibility of the Cu mesh-based TCF was demonstrated through cyclic mechanical bending tests. In addition, the Cu mesh-based TCF with ~ 50 μm thick PVA substrate demonstrated a fast Joule heating performance with a thermal response time of ~ 18.0 s and a ramping rate of ~ 3.0 ℃/s under a driving voltage of 2.5 V. Lastly, the reliable response and recovery characteristics of the Cu mesh/PVA film-based transparent heater were confirmed through the cyclic power test. We believe that the results of this study is useful in the development of flexible transparent heaters, including lightweight deicing/defogging films, wearable sensors/actuators, and medical thermotherapy pads.

We used capacitance–voltage (C–V), conductance–voltage (G–V), and noise measurements to examine the carrier trap mechanisms at the surface/core of an AlGaN/GaN nanowire wrap-gate transistor (WGT). When the frequency is increased, the predicted surface trap density promptly drops, with values ranging from 9.1 × 1013 eV−1∙cm−2 at 1 kHz to 1.2 × 1011 eV−1∙cm−2 at 1 MHz. The power spectral density exhibits 1/f-noise behavior in the barrier accumulation area and rises with gate bias, according to the 1/f-noise features. At lower frequencies, the device exhibits 1/f-noise behavior, while beyond 1 kHz, it exhibits 1/f2-noise behavior. Additionally, when the fabricated device governs in the deep-subthreshold regime, the cutoff frequency for the 1/f2-noise features moves to the subordinated frequency (~102 Hz) side.

Graphene oxide (GO) is one of the interesting ink materials owing to its fascinating properties, such as high dissolubility in water and high controllable electric properties. For versatile printing application, the viscosity of GO colloids should be controlled in order to meet the specific process requirements. Here, we report on the relatively rapid fabrication of viscosity-increased GO (VIGO) colloids mixed with electrophoretically deposited GO sheets (EPD-GO). As the GO colloid concentration, applied voltage, and deposition time increase, the viscosity of the GO colloids becomes high. The reason for the improved viscosity of GO colloids is because EPD-GO has parallel stacked GO sheets. The GO and VIGO colloids are compared and characterized using various chemical and structural analyzers. Consequently, our simple and fast method for the fabrication of GO colloids with enhanced viscosity can be used for producing inks for flexible and printed electronics.