Search

With the development of automotive technology, long life, high power, and low fuel consumption performance are expected from the internal combustion engine. This study investigated the effects of commercial oil additives on friction under different experimental conditions. In order to examine the friction effect, the samples prepared from the piston ring and cylinder were tested with the Reciprocating Test Rig at different speeds and loads. Using additives in the commercial oil lubricant showed a little reduction under the lower load. When the applied load increased commercial oil showed better friction coefficient performance in the experimental study. As for the expected results, the friction coefficient reduced with increasing sliding speeds under all conditions. In general, it was found that the commercial oil supplement did not have much effect on reducing the coefficient of friction when all the results were evaluated under these experimental conditions

This work investigated the tribological performance of (Ta/ZrN)n multilayer coatings against ultrahigh molecular weight polyethylene (UHMWPE) material. Three multilayer coatings with different designs were deposited on Ti-6Al-4 V substrate and subjected to wear testing under lubrication of diluted bovine calf serum. The results revealed an improvement in wear resistance of (Ta/ZrN)n multilayer coatings and low coefficient of friction under an applied load of 1 N. High hardness, excellent biotribological properties, and low residual stresses were obtained in the multilayer coating with the thinnest ZrN as the topmost layer of 100 nm. This work demonstrates that Ta/ZrN multilayers can be promising coatings for prosthesis applications.

Multilayer thin coatings (~3 µm in thickness) were deposited using reactive radio frequency magnetron sputtering on Ti-6Al-4 V substrate for biomaterial applications. Films are a combination of hard zirconium nitride with pure tantalum, used to manage interfacial stress and to avoid crack growth. Alternating hard/ductile material is a biomimetic design inspired by nature (nacre-inspired materials). Tribocorrosion tests were performed in Hank’s solution at 37 ◦◦C, under open circuit potential by using a ball-on-disk reciprocating tribometer. A tendency to high resistance against corrosion was found for all the samples. Coatings with a top 100 nm thick ZrN layer showed more noble potential as well as a reduction of both the friction coefficient and the wear rate during the sliding phase. The principal wear mechanism is related to a tribocorrosion layer formation.

Over the past few decades, polyetheretherketone (PEEK) artificial bone joint materials faced problems of poor wear resistance and easy infection, which are not suitable for the growing demand of bone joints. The tribological behavior and wear mechanism of polyetheretherketone (PEEK)/polytetrafluoroethylene (PTFE) with black phosphorus (BP) nanosheets have been investigated under dry sliding friction. Compared with pure PEEK, the COF of PEEK/10 wt% PTFE/0.5 wt% BP was reduced by about 73% (from 0.369 to 0.097) and the wear rate decreased by approximately 95% (from 1.0 × 10−4 mm3/(N m) to 5.1 × 10−6 mm3/(N m)) owing to the lubrication of the BP transfer film. Moreover, BP can endow the PEEK composites with excellent biological wettability and antibacterial properties. The antibacterial rate of PEEK/PTFE/BP was assessed to be over 99.9%, which might help to solve the problem of PEEK implant inflammation. After comprehensive evaluation in this research, 0.5 wt% BP nanosheet-filled PEEK/PTFE material displayed the optimum lubrication and antibacterial properties, and thus could be considered as a potential candidate for its application in biomedical materials.