The Hugoniot elastic limit and spall strength were measured for a heat-resistant metal-matrix composite Inconel 625–5%NiTi–TiB2 alloy additive manufactured (AM) by direct laser deposition. The strength characteristics of the alloy were obtained from the analysis of the complete wave profiles recorded with a VISAR laser Doppler velocimeter during shock-wave loading of the samples. The samples were loaded using a PP50 pneumatic gun or ad hoc explosive devices along and across the material deposition direction in order to determine the strength anisotropy of the AM alloy under study. The maximum shock compression pressure was ~7 GPa, and the strain rate under tension before spalling varied in the range of 105–106 s–1. Kinetic dependencies of elastic/plastic transition and critical fracture stresses vs. loading conditions were plotted. It was shown that the Hugoniot elastic limit of the alloy under study decreases as the shock wave travels into the sample, while the spall strength increases as the material’s strain rate increases at the moment of spall fracture. A comparison of the strength characteristics of the Inconel 625–NiTi–TiB2 composite alloy with the original Inconel 625 alloy has shown that an addition of 5% of powder based on NiTi-TiB2 leads to a decrease in its elastic limit and critical fracture stresses upon spalling by more than 10%. The alloy under study demonstrates anisotropy of strength properties relative to the material deposition direction.

The structure and mechanical properties of composites consisting of a metal matrix based on aluminum and its alloys of different compositions (AA-3003 and AA-5154) and graphene synthes sized in situ under a layer of molten salts were investigated depending on the chemical composition and grain size of the matrix. Aluminum matrix composites of three compositions were studied in as-cast coarse-grained, deformed fine-grained (grain size < 1 mm), and deformed sub microcrystalline (grain size < 1 μm) states in order to compare the structural characteristics of composites with different grain sizes. The composites were subjected to deformation with a split Hopkinson (Kolsky) bar and to dynamic-channel angular pressing. The hardness and dynamic mechanical properties of the composites were measured at strain rates ε˙ from 1.8 − 4.7 × 103 to 1.6 − 2.4 × 105 s−1. It was found that grain refinement induced a sharp increase in the hardness of composites with various compositions (by a factor of 1.6–2.6). A correlation of the elastic-plastic properties of the aluminum matrix composites with the grain sizes and chemical compositions of the matrices was established. A transition from coarse-grained to sub microcrystalline structure was shown to improve the elastic-plastic properties on average by a factor of 1.5. It was proved that the reinforcing effect of graphene increased with the decreasing grain size of the matrix. Mechanisms of reinforcement of the aluminum matrix composites using graphene were proposed.