Search

Barium zirconate (BaZrO3, BZO), which exhibits superior mechanical, thermal, and chemical stability, has been widely used in many applications. In dentistry, BZO is used as a radiopacifier in mineral trioxide aggregates (MTAs) for endodontic filling applications. In the present study, BZO was prepared using the sol–gel process, followed by calcination at 700–1000 °C. The calcined BZO powders were investigated using X-ray diffraction and scanning electron microscopy. Thereafter, MTA-like cements with the addition of calcined BZO powder were evaluated to determine the optimal composition based on radiopacity, diametral tensile strength (DTS), and setting times. The experimental results showed that calcined BZO exhibited a majority BZO phase with minor zirconia crystals. The crystallinity, the percentage, and the average crystalline size of BZO increased with the increasing calcination temperature. The optimal MTA-like cement was obtained by adding 20% of the 700 °C-calcined BZO powder. The initial and final setting times were 25 and 32 min, respectively. They were significantly shorter than those (70 and 56 min, respectively) prepared with commercial BZO powder. It exhibited a radiopacity of 3.60 ± 0.22 mmAl and a DTS of 3.02 ± 0.18 MPa. After 28 days of simulated oral environment storage, the radiopacity and DTS decreased to 3.36 ± 0.53 mmAl and 2.84 ± 0.27 MPa, respectively. This suggests that 700 °C-calcined BZO powder has potential as a novel radiopacifier for MTAs. [ABSTRACT FROM AUTHOR]

Barium titanate (BaTiO3, BTO), conventionally used for dielectric and ferroelectric applications, has been assessed for biomedical applications, such as its utilization as a radiopacifier in mineral trioxide aggregates (MTA) for endodontic treatment. In the present study, BTO powders were prepared using the sol-gel process, followed by calcination at 400–1100 °C. The X-ray diffraction technique was then used to examine the as-prepared powders to elucidate the effect of calcination on the phase composition and crystalline size of BTO. Calcined BTO powders were then used as radiopacifiers for MTA. MTA-like cements were investigated to determine the optimal calcination temperature based on the radiopacity and diametral tensile strength (DTS). The experimental results showed that the formation of BTO phase was observed after calcination at temperatures of 600 °C and above. The calcined powders were a mixture of BaTiO3 phase with residual BaCO3 and/or Ba2TiO4 phases. The performance of MTA-like cements with BTO addition increased with increasing calcination temperature up to 1000 °C. The radiopacity, however, decreased after 7 days of simulated oral environmental storage, whereas an increase in DTS was observed. Optimal MTA-like cement was obtained by adding 40 wt.% 1000 °C-calcined BTO powder, with its resulting radiopacity and DTS at 4.83 ± 0.61 mmAl and 2.86 ± 0.33 MPa, respectively. After 7 days, the radiopacity decreased slightly to 4.69 ± 0.51 mmAl, accompanied by an increase in DTS to 3.13 ± 0.70 MPa. The optimal cement was biocompatible and verified using MG 63 and L929 cell lines, which exhibited cell viability higher than 95%. [ABSTRACT FROM AUTHOR]

Purpose: This study aimed to investigate the retentive force and deformation of double Akers' polyetherketoneketone (PEKK) clasps on removable partial dentures (RPDs) with varying designs and undercut depths., Methods: Thirty double Akers' PEKK clasps with two different widths and heights (Groups I and II) were fabricated using computer-aided design and computer-aided manufacturing (CAD/CAM). Each design was further subdivided (n = 5) into three undercut depths (0.25, 0.50, and 0.75 mm). The retentive force of the clasps was measured after 10 years of clinical use (15,000 insertion/removal cycles), and the deformation of the clasp tips was analyzed before and after cycling., Results: Clasps with 0.50-mm and 0.75-mm undercut depths exhibited greater initial retentive forces (3.15-3.51 N) compared to those in the 0.25-mm undercut group (2.40-2.80 N). Group I maintained consistent retentive forces over the cycles (P = 0.345), whereas Group II showed declining forces after the initial use (P < 0.003). In both groups, the 0.50-mm undercut exhibited a greater retentive force than the 0.25-mm (P < 0.001 and P < 0.004, respectively), with no significant differences between the 0.50-mm and 0.75-mm undercut depths. Despite a lower initial retentive force, the 0.25-mm undercut showed less deformation and clasp tip wear., Conclusions: The PEKK clasps did not exhibit significantly reduced retentive forces or permanent deformations after 15,000 fatigue cycles. These results suggest that the PEKK polymer displays superior mechanical properties as an esthetic clasp material, and clasps with 0.50-mm and 0.75-mm undercut depths are recommended for long-term clinical use.