Abstract In this paper, we present an experimental study of L10-FePt granular films with crystalline boron nitride (BN) grain boundary materials for heat assisted magnetic recording (HAMR). It is found that application of a RF substrate bias (V DC = -15 V) yields the formation of hexagonal boron nitride (h-BN) nanosheets in grain boundaries, facilitating the columnar growth of FePt grains during sputtering at high temperatures. The h-BN monolayers conform to the side surfaces of columnar FePt grains, completely encircling individual FePt grains. The resulting core–shell FePt-(h-BN) nanostructures appear to be highly promising for HAMR application. The high thermal stability of h-BN grain boundaries allows the deposition temperature to be as high as 650℃ such that high order parameters of FePt L10 phase have been obtained. For the fabricated FePt-(h-BN) thin film, excellent granular microstructure with FePt grains of 6.5 nm in diameter and 11.5 nm in height has been achieved along with good magnetic hysteresis properties.

A systematic investigation has been performed to optimize the microstructure of L10-FePt–SiOx granular thin films as recording media for heat-assisted magnetic recording. The FePt–boron nitride (BN) nucleation layer, which is stable even at 700 °C, is used to control the grain sizes and microstructure during the high-temperature processing. The study finds that films of high-aspect-ratio FePt grains with well-formed silicon oxide (SiOx) grain boundaries require the grading of the deposition temperature during film growth as well as the grading of the silicon oxide concentration. Well-isolated columnar grains of L10-FePt with an average height greater than 11 nm and diameters less than 7 nm have been achieved. Transmission electron microscopy analysis of the microstructures of samples produced under a variety of non-optimal conditions is presented to show how the microstructure of the films depends on each of the sputtering parameters.