Search

Extruded plates of 6005A aluminum alloy with 0.07 wt% Sc (referred to as M6005A alloy) was metal-inert-gas-welded (MIG-welded) with ER5087 filler wire. The microstructure, mechanical properties, and fatigue behavior of the joints were studied. Compared with the base material (BM), recrystallization occurred and the formation of the coarse β' phase was evident in the heat-affected zone close to the weld zone (HAZ 2), which resulted in a significant decrease in the mechanical properties of HAZ 2. However, trace Sc inhibited the growth of the recrystallized grains in the HAZ 2, strengthening the α-AlFeSi and β'′ phases in the BM, which drastically improved the mechanical properties of the BM. In the weld zone (WZ), grains were significantly refined since the presence of Al 3 (Sc, Zr) particles promoted the nucleation of such grains in the WZ, and the particles also promoted the non-uniform nucleation of the α-AlFeSi phase, which significantly improved the mechanical and fatigue properties of the WZ. The hardness distribution of the MIG-welded joint shows a double-W shape. The lowest hardness is 55 HV, observed in the HAZ 2. The ultimate tensile strength (UTS) and conditional fatigue strength (107 cycles) of the MIG-welded joint of M6005A-T6 are 238.5 MPa and 108.2 MPa, respectively, 38 MPa and 13 MPa higher than the those of the MIG-welded joint of 6005A-T6 alloy, respectively. • The 6005A alloy profile, with optimum content of Sc, was welded by MIG welding. • Study on microstructure and properties of welding joint of 6005A alloy containing Sc(referred to as M6005A-T6 alloy). • The mechanism of the effect of Sc on the structure and properties of 6005A welded joint was studied. • M6005A alloy is about to replace 6005A alloy as an important material for high-speed iron‑aluminum. [ABSTRACT FROM AUTHOR]

Mechanical property and corrosion resistance are essential performances in ultra-high strength Al-Zn-Mg-Cu alloys for the aerospace and weapon industries. In this study, the pre-strain and aging treatments were used to enhance such performances of the spray formed ultra-high strength Al-Zn-Mg-Cu alloy. After 2% pre-strain with peak aging (PA) and retrogression and re-aging (RRA) treatments, the ultimate tensile strength, yield strength, and elongation can reach to 774 MPa, 735 MPa, 10.7% and 774 MPa, 747 MPa, 9.4%, respectively. The coarser precipitates of the samples with 4% pre-strain can lead to the slight lower strength compared with the samples with 2% pre-strain. The proper combination of pre-strain and aging treatments can also effectively enhance the stress corrosion resistance of the studied alloy by the following reasons. First, the higher strain concentration degree and dislocation density introduced by pre-strain treatments have high internal energy and provide more stored energy for the growth of the passive film. Second, the spacing of grain boundary precipitates under double aging (DA) and RRA states is larger than that under PA state. The width of uniform precipitation free zone (PFZ) with 2% pre-strain is larger than that with 4% pre-strain. Third, after pre-strain treatments, the cracks perpendicular to the deformation direction can be produced in Al 7 Cu 2 Fe phase, which further breaks up such particles. According to the results of Kelvin probe microscopy, the Al 7 Cu 2 Fe phase with smaller dimension can obtain the lower difference of potential to Al matrix. • The strength and corrosion resistance of the alloy were enhanced by pre-strain. • The pre-strain produced cracks in Al 7 Cu 2 Fe particles and further broke up them. • The pre-strain improved the strain concentration degree and dislocation density. • The effect of precipitation free zone and precipitate is better under 2% strain. • The improvement mechanism of pre-strain treatment was revealed. [ABSTRACT FROM AUTHOR]

The precipitation behaviour, mechanical properties and corrosion performance of an Al-Zn-Mg-Sc-Zr alloy under one-stage aging (T6), two-stage aging (T74) and retrogression and re-aging (RRA) treatment were mainly investigated. For the RRA treatment, with increasing temperature and duration of retrogression, the grain interior precipitates (GIPs) gradually grew and changed from GP zones + η′ phases to η′ phases + η phases. In addition, the discontinuity of coarsened grain boundary precipitates (GBPs) significantly increased, and the width of precipitate free zones (PFZs) became broader. Consequently, progressive decrease in strength and hardness, and improved corrosion resistance of the alloy can be observed. Compared to conventional T6 and T74 treatments, a good balance of mechanical properties (168.5 HV for hardness, 547 MPa for ultimate tensile strength) and corrosion resistance can be obtained with retrogression treatment at 160 °C for 30 min. Moreover, research on the localized corrosion of the Al-Zn-Mg-Sc-Zr alloy showed that, at the initial stage of pitting corrosion, the Al matrix around the cathodic α-Al(Fe,Mn)Si particles was uniformly dissolved, leading to the detachment of the α-Al(Fe,Mn)Si particles from the matrix and the formation of pitting pits. • The strengthening and corrosion mechanisms of Al-Zn-Mg-Sc-Zr alloy under different aging conditions were studied. • A model for the process of pitting corrosion development is established. • The optimized RRA treatment for Al-Zn-Mg-Sc-Zr is obtained. [ABSTRACT FROM AUTHOR]

• The effects of Sc, Y and Zr on the performances and microstructure evolution of Al-0.7Mg-0.6Si-0.2Ce alloys were studied. • An excellent combination of strength, elongation and electrical conductivity was achieved with the addition of Sc and Y. • The strengthening and electrical resistance mechanism of the studied alloys were revealed by statistical calculation. [Display omitted] In order to achieve the compatibility between excellent mechanical properties and good electrical conductivity of Al-Mg-Si alloys, detailed investigation was carried out to understand the microstructure evolution and their influences on performances of different Al-0.7Mg-0.6Si-0.2Ce-X (X Sc, Y and Zr) alloys prepared by casting, homogenization, hot extrusion, solution and aging treatments. Under aging state, Ce can form a large number of micron-sized AlCeSi and a few AlCeFeSi phase. The strength increased to 334 MPa as a result of decreased grain size and improved precipitation effect and the electrical conductivity increased up to 53.53%IACS because of lower solute Si atoms. The β" precipitates were coarsened and consequently the volume fracture was largely reduced due to the presence of Sc element, leading to the decreased strength of 311 MPa. The more solute Mg, Si and Sc atoms increased the degree of free electron scattering and the electrical conductivity decreased to 51.86%IACS. It is also found that Sc significantly enhanced the elongation of the alloy from 11.8% to 18.0%, which might be attributed to the formation of Al 3 Sc and (Al, Si) 3 Sc phases. The addition of Y raised the electrical conductivity of Al-Mg-Si-Ce alloy to 55.79%IACS by ameliorating the volume fraction and distribution of β" precipitates and decreasing the solute Si atoms. The co-addition of Sc and Y inherited the advantages of such two alloys. The ultimate tensile strength, elongation, electrical conductivity of Al-0.7Mg-0.6Si-0.2Ce-0.2Sc-0.1Y alloy processed by aging treatments is 336 MPa, 19.4% and 53.11%IACS, respectively. [ABSTRACT FROM AUTHOR]