Search

Rubber compounds based on acrylonitrile‐butadiene rubber were filled with biopolymer fillers, namely kraft lignin, and calcium lignosulfonate. For cross‐linking of rubber compounds, sulfur curing system, dicumyl peroxide, and combination of dicumyl peroxide with trimethylolpropane trimethacrylate were used. The main objective of the work was to investigate the influence of biopolymer fillers content and curing system composition on vulcanization process of rubber compounds, cross‐link density, morphology, and physical‐mechanical properties of vulcanizates. The results revealed that rubber compounds filled with calcium lignosulfonate can be efficiently cured with sulfur as well as peroxide curing systems. Modulus, hardness, and elongation at break were strongly dependent on cross‐link density. Vulcanizates filled with high content of lignosulfonate exhibited comparable values of tensile strength, regardless of the curing system applied. The application of kraft lignin into peroxide systems cured rubber compounds resulted in undesirable reactions between functional groups of the biopolymer and peroxide radicals. Depletion of peroxide radicals resulted in significant deceleration of curing process and decrease in cross‐link density of vulcanizates. This was reflected in typical change of physical‐mechanical characteristics, decrease in modulus and hardness, and increase in elongation at break. Very good adhesion and compatibility between the kraft lignin and the rubber matrix resulted in enhancement of tensile behavior of vulcanizates cured with sulfur system. [ABSTRACT FROM AUTHOR]

Rubber blends based on styrene–butadiene rubber, ethylene–propylene–diene monomer rubber and a combination of both rubbers were cured with different sulfur and peroxide curing systems. In sulfur curing systems, two type of accelerators, namely tetramethylthiuram disulfide, N-cyclohexyl-2-benzothiazole sulfenamide, and combinations of both accelerators were used. In peroxide curing systems, dicumyl peroxide, and a combination of dicumyl peroxide with zinc diacrylate or zinc dimethacrylate, respectively, were applied. The work was aimed at investigating the effect of curing systems composition as well as the type of rubber or rubber combinations on the curing process, cross-link density and physical–mechanical properties of vulcanizates. The dynamic mechanical properties of the selected vulcanizates were examined too. The results revealed a correlation between the cross-link density and physical–mechanical properties. Similarly, there was a certain correlation between the cross-linking degree and glass transition temperature. The tensile strength of vulcanizates based on rubber combinations was higher when compared to that based on pure rubbers, which points out the fact that in rubber combinations, not only are the features of both elastomers combined, but improvement in the tensile characteristics can also be achieved. When compared to vulcanizates cured with dicumyl peroxide, materials cured with a sulfur system exhibited higher tensile strength. With the application of co-agents in peroxide vulcanization, the tensile strength overcame the tensile behavior of sulfur-cured vulcanizates. [ABSTRACT FROM AUTHOR]

The sulfur curing system, peroxide curing system and their combinations were applied for the cross-linking of unfilled and carbon black-filled rubber formulations based on ethylene-propylenediene-monomer rubber. The results demonstrated that the type of curing system influenced the course and shape of curing isotherms. This resulted in the change of curing kinetics of rubber compounds. The cross-link density of materials cured with combined vulcanization systems was lower than that for vulcanizates cured with the peroxide or sulfur system. Good correlation between the cross-link density as well as the structure of the formed cross-links and physical–mechanical characteristics of the cured materials was established. Both filled and unfilled vulcanizates cured with combined vulcanization systems exhibited a higher tensile strength and elongation at break when compared to their equivalents vulcanized in the presence of the peroxide or sulfur curing system. It can be stated that by proper combination of vulcanization systems, it is possible to modify the tensile behavior of vulcanizates in a targeted manner. On the other side, dynamical–mechanical properties were found not be significantly influenced by the curing system composition. [ABSTRACT FROM AUTHOR]

In this work, dicumyl peroxide (DCP), di-tert-butyl peroxide (DTBP), di(tert-butylperoxyisopropyl)benzene (DTBPIB), and 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane (DDTBPH) were used for cross-linking of rubber matrix based on Ethylene-propylene-diene monomer rubber (EPDM). The aim was to investigate the influence of curing temperature and the type and content of peroxide on curing process of rubber compounds, cross-link density, and physical-mechanical properties of vulcanizates. The results revealed that higher curing temperatures promote faster decomposition of organic peroxides, leading to the faster reactions of peroxide radicals with rubber chains. The increase in temperature resulted also in the increase of cross-linking degree. Although, side reactions as chain scission take over the main cross-linking reactions at very high temperatures resulting in the decrease of cross-link density. The increasing content of peroxides resulted in the acceleration of curing reactions and to increase of cross-link density. The fastest curing kinetics exhibited rubber compounds cured with DCP. However, vulcanizates cured with DCP were found to have the lowest cross-link density. In generally, the dependences of modulus, hardness, and elongation at break of vulcanizates were in line with the dependences of the cross-link densities, while higher tensile strength were found to have vulcanizates cured at higher temperatures and lower peroxides content. [ABSTRACT FROM AUTHOR]

Calcium lignosulfonate in different loadings was applied to the rubber matrix based on EPDM. A sulfur curing system, organic peroxide, and a combination of organic peroxide with two coagent types were used for cross-linking of rubber compounds. The work was focused on the investigation of filler content and curing system composition in the curing process, cross-link density, morphology, and physical–mechanical properties of composites. The achieved results demonstrated that the curing parameters of rubber compounds cured with the sulfur system were significantly different from those cured with peroxide systems. There was also an observed different influence of curing systems composition on cross link density, though in all cases, the degree of cross-linking showed a decreasing trend with increasing content of lignosulfonate. The tensile strength of the composites cured with sulfur system and organic peroxide was comparable, regardless of lignosulfonate loading. This points to the application of both curing systems in cross-linking of rubber compounds with biopolymer filler. However, the introduction of coagents in peroxide vulcanization led to the improvement of adhesion and compatibility between the rubber and the filler on the filler–rubber interface. This subsequently resulted in the improvement of the tensile characteristics of composites. The introduction of organic peroxide in combination with coagent seems to be a very simple and efficient way for the preparation of biopolymer-filled composites with applicable physical–mechanical properties. [ABSTRACT FROM AUTHOR]

In the present work, barium ferrite in constant loading was dosed to the rubber matrices based on NR, SBR and NBR. Sulfur, peroxide and mixed sulfur and peroxide curing systems were applied for cross-linking of rubber magnetic composites. The application of sulfur or peroxide curing system leads to the formation of different types of linkages between rubber chain segments. As the structure of the formed cross-links plays a significant role in determining the final properties of rubber articles, the main aim of the work was to use the combination of curing systems in order to suppress the disadvantages of both systems and possibly to highlight their benefits. The results showed that composition of curing system has considerable influence on cross-link density of composites, which was subsequently reflected in typical change of physical-mechanical properties and glass transition temperature. The tensile strength was improved with increasing amount of peroxide curing system. The reason can be attributed to the presence of co-agent zinc methacrylate, which exhibits strong adhesion to magnetic filler and thus it contributes to the improvement of compatibility and homogeneity on the interphase filler–rubber. On the hand, there was observed no influence of curing system composition or type of rubber matrix on magnetic characteristics of composites. [ABSTRACT FROM AUTHOR]